Dark yellow grey glass composition

A glass composition, gray technology, applied in the field of float glass composition, can solve the problems of low transmission color shift, can not meet privacy protection and other problems, achieve low UV penetration, avoid damage to accessories and personnel, good energy saving and environmental protection Effect

Active Publication Date: 2020-01-03
FUYAO GLASS IND GROUP CO LTD
View PDF15 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent CN200480007732.8 discloses a neutral gray glass composition with low transmittance color shift characteristics for automotive vision panels, the main colorant is 0.30-0.75% (by weight) of Fe2O3 (total iron), 0- With 15ppm of CoO and 1-15ppm of Se, the glass composition basically does not contain nickel. Based on the glass thickness of 3.9 mm, its visible light transmittance (Lta) is at least 65%, which obviously cannot meet the needs of privacy protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dark yellow grey glass composition
  • Dark yellow grey glass composition
  • Dark yellow grey glass composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0040] The present invention uses silica sand, soda ash, sodium nitrate, Glauber's salt, dolomite, limestone, iron powder, carbon powder, titanium dioxide, chromite, cerium powder, cobalt and selenium, etc. as raw materials to prepare the glass compositions of Examples 1-9 . The glass compositions of Examples 1-9 have approximately the same basic components (by weight percentage) as shown in Table 1.

[0041] Table 1: Basic components of the glass compositions of Examples 1-9

[0042]

[0043]

[0044] As shown in Table 2, the functional coloring components (by weight percentage) of the glass compositions of Examples 1 to 9 are respectively described in the following Table 2.

[0045] Table 2: Functional coloring components of the glass compositions of Examples 1-9

[0046] Total iron (%) redox ratio CeO 2 (%)

TiO 2 (%)

Cr 2 o 3 (PPM)

CoO(PPM) Se(PPM) Example 1 1.66 0.276 1.4510 1.34 300 200 20 Example 2 1.54 0.25...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a float glass composition, particular to a grey glass composition, and specifically provides a dark yellow grey glass composition. The dark yellow grey glass composition comprises the following functional coloring components: total iron (Fe2O3), cerium dioxide (CeO2), titanium dioxide (TiO2), chromium sesquioxide (Cr2O3), cobalt oxide (CoO) and selenium (Se). The dark yellow gray glass composition adopted by the invention has solar transmittance of 20% or below, infrared transmittance of 25% or below, visible light transmittance of 20% or below and ultraviolet transmittance of 1% or below on the basis of a glass thickness of 3.2 mm; so the dark yellow grey glass composition can meet the demand for privacy protection, has ultra-strong ultraviolet penetration blocking performance and low solar transmittance, can well prevent ultraviolet rays from damaging ornaments and people in a vehicle or in a room, and has good energy-saving and environment-friendly effects.

Description

Technical field: [0001] The invention relates to a float glass composition, especially a gray glass composition, and specifically provides a dark yellow-gray glass composition with an ultraviolet transmittance (Tuv) less than or equal to 1%. Background technique: [0002] Gray glass is a kind of body tinted glass, which has the advantages of heat insulation, UV protection and privacy protection. It is often used as automotive glass, architectural glass and even aviation glass. When using gray glass, in addition to considering its optical properties, such as visible light transmittance, infrared transmittance and ultraviolet transmittance, etc., it is also necessary to consider its color tone and appearance, the composition of the glass itself, the selection of colorants and their proportions, etc. All aspects will affect the optical properties of the glass and the tint of the glass. [0003] Japanese patent JP3669019B2 discloses a kind of dark gray glass, the coloring compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/095C03C3/087C03C3/078C03C4/02C03C4/08
CPCC03C3/078C03C3/087C03C3/095C03C4/02C03C4/082C03C4/085
Inventor 何世猛关建光陈国树叶苏铨徐如斌林开福罗祥智
Owner FUYAO GLASS IND GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products