Adhesive used for metal powder injection molding and preparation method thereof

A technology of injection molding and metal powder, applied in metal processing equipment, transportation and packaging, etc., can solve problems such as poor mechanical properties of parts, and achieve the effect of improving fusion effect, low production cost, and improving mold filling.

Active Publication Date: 2020-02-04
中航迈特增材制造(徐州)有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem of poor mechanical properties of injection molded parts using water-soluble adhesives in the prior art, an adhesive for metal powder injection molding and its preparation method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] An adhesive for metal powder injection molding, its weight is 100kg, and it is composed of the following components in terms of weight percentage: polyethylene glycol 59wt%, plasticizer (polymethyl methacrylate) 34.8wt%, hard Fatty acid 6wt%, o-sulfonyl benzimide sodium 0.2wt%.

[0065] The preparation method of the adhesive for the above-mentioned metal powder injection molding, the method steps are as follows:

[0066] Step 1. Melt a certain amount of polyethylene glycol at a constant temperature of 170°C; choose an oil bath constant temperature stirring pot for constant temperature equipment.

[0067] Step 2. Add materials to the step 1 in three batches, stir evenly after feeding in each batch and let stand for a certain period of time; add a certain amount of plasticizer in the first batch, stir evenly, and let stand for 30 minutes, the second batch Add a certain amount of stearic acid for the first time, stir evenly, and let stand for 30 minutes; add a certain amo...

Embodiment 2

[0072] An adhesive for metal powder injection molding in this embodiment has a weight of 100kg and is composed of the following components in terms of weight percentage: polyethylene glycol 50wt%, plasticizer (polypropylene) 45wt%, hard 4.85wt% fatty acid, 0.15wt% sodium o-sulfonylbenzimide.

[0073] The preparation method of the adhesive for the above-mentioned metal powder injection molding, the method steps are as follows:

[0074] Step 1. Melt a certain amount of polyethylene glycol at a constant temperature of 170°C; choose an oil bath constant temperature stirring pot for constant temperature equipment.

[0075] Step 2: Add materials to the step 1 in three batches, stir evenly after feeding each batch and let it stand for a certain period of time; add a certain amount of plasticizer in the first batch, stir evenly, let stand for 20min, the second batch Add a certain amount of stearic acid for the first time, stir evenly, and let stand for 30 minutes; add a certain amoun...

Embodiment 3

[0080] A metal powder injection molding adhesive in this embodiment has a weight of 100kg, and is composed of the following components in terms of weight percentage: polyethylene glycol 52wt%, plasticizer (polypropylene and polymethacrylic acid Methyl ester, its mass ratio is 1:1) 43.8wt%, stearic acid 4wt%, o-sulfonyl benzimide sodium 0.2wt%.

[0081] The preparation method of the adhesive for the above-mentioned metal powder injection molding, the method steps are as follows:

[0082] Step 1. Melt a certain amount of polyethylene glycol at a constant temperature of 170°C; choose an oil bath constant temperature stirring pot for constant temperature equipment.

[0083] Step 2: Add materials to the step 1 in three batches, stir evenly after feeding each batch and let it stand for a certain period of time; add a certain amount of plasticizer in the first batch, stir evenly, let stand for 20min, the second batch Add a certain amount of stearic acid for the first time, stir even...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of metal powder injection molding, and discloses an adhesive used for metal powder injection molding. The adhesive used for metal powder injection moldingcomprises the following components of, in percentage by weight, polyethylene glycol 50wt% to 65wt%, plasticizer 30wt% to 45wt%, stearic acid 4wt% to 6wt%, and Saccharin soluble hydrate 0.1wt% to 0.2wt%. The invention also discloses a preparation method of the adhesive for metal powder injection molding, and the mechanical properties of injection molding parts can be improved.

Description

technical field [0001] The invention relates to the technical field of metal powder injection molding, in particular to an adhesive for metal powder injection molding and a preparation method thereof. Background technique [0002] In recent years, the technology of preparing metal powder has advanced by leaps and bounds, and the near-net shape technology has risen rapidly. Metal powder injection molding technology (Metal Powder Injection Molding Technology, referred to as MIM) has also developed accordingly. , sintering, post-processing and other processes to quickly manufacture structural parts with high density, high precision, and three-dimensional complex shapes, which can be mass-produced. Metallurgical products have the disadvantages of uneven material, low mechanical properties, thin walls and complex structures, and are especially suitable for mass production of small, complex and special metal parts. [0003] However, at present, only a small part of metal powder i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F3/22
CPCB22F3/225B22F1/103B22F1/107
Inventor 张志桐高正江王山秦亚洲殷雷陈鹏陈帅
Owner 中航迈特增材制造(徐州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More