A martensitic stainless steel continuous annealing pickling line welding method

A technology of martensitic stainless steel and welding methods, applied in welding equipment, welding accessories, arc welding equipment, etc., can solve the problems of easy cracking of welds, avoid weld fractures, avoid cracking of annealing and pickling lines, and increase protection intensity effect

Active Publication Date: 2021-07-09
GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of this invention is to provide a martensitic stainless steel continuous annealing and pickling line welding method to solve the problem that the weld seam of martensitic stainless steel coils with a carbon content above 0.5% is easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A martensitic stainless steel continuous annealing pickling line welding method
  • A martensitic stainless steel continuous annealing pickling line welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The specific MIG welding parameters for 50Cr15MoV stainless steel are shown in Table 1.

[0023]

[0024] The annealing and pickling line requires two volumes of annealed 50Cr15MoV stainless steel with a thickness of 5.0mm before and after welding. First, the welding seam 1 of the steel coil is formed by welding with the corresponding parameters in Table 1 according to the thickness of the steel coil. The welding wire is 309Si and the specification is 1.2mm.

[0025] Rib plate 3 is prepared in advance, the material is 304 annealed, the welding rod material is 309L, and the specification is 2.5*350mm. Ribs 3 have the same size, the specific specification is 4.0 (thickness) * 100 * 300mm, and the surrounding is arc-shaped, the arc radius is 10mm, to avoid stress concentration cracking at the corner, the specific shape is as follows figure 1 shown.

[0026] Use a shearing device with a crescent-shaped incision to cut off the arc-starting and arc-ending sections of the...

Embodiment 2

[0033] The annealing and pickling line requires two volumes of annealed 50Cr15MoV stainless steel with a thickness of 3.0mm before and after welding. First, weld the weld seam 1 of the steel coil with the corresponding parameters in Table 1 according to the thickness of the steel coil. The welding wire is 309Si and the specification is 1.2mm.

[0034] Prepare the rib plate 3 in advance, the material is 304 annealed state, the size of the rib plate 3 is the same, the specific specification is 1.5 (thickness)*100*300mm, and the surrounding is arc-shaped, the radius of the arc is 5mm, to avoid stress concentration cracking at the corner , the specific form is as figure 1 shown.

[0035] Use a shearing device with a crescent-shaped incision to cut off the arc-starting and arc-ending sections of the weld 1 of the steel coil to avoid poor formation of these two places, which will cause cracks to occur first in the arc-starting and arc-ending sections during the operation of the str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a martensitic stainless steel continuous annealing and pickling line welding method, belongs to the field of stainless steel welding, and solves the problem that the weld seam of a martensitic stainless steel coil with a carbon content of more than 0.5% is easy to crack. The present invention comprises the following steps: use a MIG welding machine to weld between the stainless steel coils at the entrance of the annealing and pickling line; use a shearing device to cut off the arc-starting and arc-ending sections of the weld seam of the steel coils to avoid poor molding at these two places; During the operation of the strip steel, cracks first occur in the arc starting and arc closing sections, resulting in tearing of the weld seam; the ribs are welded at both sides of the weld seam of the steel coil at the same time, and then the rib plate is welded in the middle of the weld seam of the steel coil, requiring ribs The periphery of the plate is completely welded without leaving gaps to prevent residual acid in the gaps, which will pollute the surface when the residual acid flows out; the rib plate is air-cooled after welding to reduce the amount of martensite formation and the hardness of the heat-affected zone. The invention can effectively prevent the weld seam of the martensitic stainless steel coil with the carbon content above 0.5% from cracking in the annealing and pickling line.

Description

technical field [0001] The invention belongs to the field of stainless steel welding, in particular to a martensitic stainless steel continuous annealing pickling line welding method. Background technique [0002] With the development of the domestic knife and scissors market, 50Cr15MoV stainless steel, as a high-carbon martensitic stainless steel, has a hardness of 56-58 HRC after quenching. 50Cr15MoV stainless steel has good corrosion resistance, processability and grindability, and is widely used in the production of high-end knives. There are relatively few domestic steel mills that can produce this type of steel, mainly because its production is difficult, which is mainly reflected in smelting, hot rolling, cold rolling, welding and other processes. When the hot-rolled and cold-rolled coils of this steel type are produced on the annealing and pickling line, in order to ensure continuous production, the coils must be welded by welding machines. The current welding techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/173B23K9/32
CPCB23K9/173B23K9/32
Inventor 李照国李聚宝潘吉祥王军伟申德
Owner GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com