Epoxy asphalt concrete for roads and bridges and preparation method thereof

A technology of epoxy asphalt and concrete, applied in the field of asphalt concrete, can solve the problems of unfavorable control process, insufficient structural stability, unsatisfactory use effect, etc., to improve the uniformity of texture, improve the effect of pavement pavement, and improve the anti-aging deformation effect of ability

Inactive Publication Date: 2020-02-14
张海龙
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the performance of the existing asphalt concrete is poor, it is easy to be deformed, the structural stability is insufficient, the use effect is not ideal, and it is not conducive to the control process, so it needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] As preferably, the preparation method of described curing agent comprises the steps:

[0037] P1. Add acrylate dropwise to the polyamine, stir at room temperature until the temperature of the system rises to 75°C to 85°C, and last for 25 minutes to 30 minutes to obtain a mixed reaction liquid;

[0038] P2, removing excess polyamine in the mixed reaction liquid to obtain a reaction liquid;

[0039] P3. Add alkyl glycidyl ether to the reaction solution, heat to 70-75 degrees Celsius for 20-30 minutes to obtain the curing agent.

[0040] Preferably, the modified asphalt is anti-aging modified asphalt, including 70%-90% of base asphalt, 3%-6% of asbestos fiber, 1%-5% of nonylphenol polyoxyethylene ether, and 2% of alumina -5% and polyurethane resin 8%-15%.

[0041] As preferably, the preparation method of described antiaging modified asphalt comprises the steps:

[0042] Q1. Heat the base asphalt to 170-180 degrees Celsius, transfer it to the production tank, keep the te...

Embodiment 1

[0048] An epoxy asphalt concrete for road bridges and a preparation method thereof, the epoxy asphalt concrete for road bridges and the preparation method thereof are made of the following raw materials: 15% epoxy resin, 3% curing agent, 25% aggregate, 25% filler %, coupling agent 5%, modified asphalt 12%, glass fiber 10% and water 5%.

[0049] As preferably, described comprises the steps:

[0050] S1. Mix the epoxy resin and the modified asphalt, and stir evenly for 15 minutes to 25 minutes to obtain the first mixture;

[0051] S2. Mix the aggregate and the filler, stir evenly for 30 minutes to 45 minutes, and then add water for wetting to obtain the second mixture,

[0052] S3, adding the first mixture and the second mixture into a large mixer, heating to 15 degrees Celsius to 160 degrees Celsius, then adding a coupling agent, and stirring uniformly for 10 minutes to 12 minutes to obtain a third mixture;

[0053] S4. Cool the third mixture to 110°C to 120°C, add glass fibe...

Embodiment 2

[0068] An epoxy asphalt concrete for road bridges and a preparation method thereof, the epoxy asphalt concrete for road bridges and the preparation method thereof are made of the following raw materials: 10% epoxy resin, 3% curing agent, 20% aggregate, 30% filler %, coupling agent 2%, modified asphalt 15%, glass fiber 15% and water 5%.

[0069] As preferably, described comprises the steps:

[0070] S1. Mix the epoxy resin and the modified asphalt, and stir evenly for 15 minutes to 25 minutes to obtain the first mixture;

[0071] S2. Mix the aggregate and the filler, stir evenly for 30 minutes to 45 minutes, and then add water for wetting to obtain the second mixture,

[0072] S3, adding the first mixture and the second mixture into a large mixer, heating to 15 degrees Celsius to 160 degrees Celsius, then adding a coupling agent, and stirring uniformly for 10 minutes to 12 minutes to obtain a third mixture;

[0073] S4. Cool the third mixture to 110°C to 120°C, add glass fibe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses epoxy asphalt concrete for roads and bridges and a preparation method thereof. The epoxy asphalt concrete for roads and bridges is prepared from the following raw materials byweight: 10%-20% of epoxy resin, 3%-6% of a curing agent, 20%-35% of aggregate, 25%-35% of a filler, 1%-5% of a coupling agent, 10%-20% of modified asphalt, 5%-10% of glass fibers and 5%-8% of water. According to the epoxy asphalt concrete for roads and bridges and the preparation method, through adding the epoxy resin and utilizing modified filtration, and by combining the filler components with different ratios and using the batch mixing process, the control is easily achieved, the mixing processing is conveniently performed, the texture uniformity is easily improved, the structural performance of the asphalt concrete can be effectively improved, aging deformation resistance is improved, the pavement laying effect is easily improved, and stability is easily improved, facilitating promotion and the use.

Description

technical field [0001] The invention relates to the technical field of asphalt concrete, in particular to epoxy asphalt concrete for roads and bridges and a preparation method thereof. Background technique [0002] In today's social life, the use of asphalt concrete is very common, which can pave the road surface and improve the quality, but for different road surface environments, the required asphalt concrete is also different. [0003] However, the performance of the existing asphalt concrete is poor, it is easy to be deformed, the structural stability is insufficient, the use effect is not ideal, and it is not conducive to the control of the process flow, so it needs to be improved. Contents of the invention [0004] The purpose of the present invention is in order to solve the shortcoming that exists in the prior art, and proposes a kind of epoxy asphalt concrete for road and bridge and preparation method thereof. [0005] In order to achieve the above object, the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/0075C04B24/281C04B14/02C04B14/42C04B14/04C04B24/121C04B24/045C04B24/023C04B24/42
Inventor 张海龙赵溪张兰党翠艳徐冰李小可王祎楠
Owner 张海龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap