Spray-coating method of aluminum alloy door and window

A technology of aluminum alloy doors and windows, aluminum alloy profiles, applied in the direction of coating, electrolytic coating, surface reaction electrolytic coating, etc., can solve the problems of uneven surface, unsatisfactory spraying effect, etc., achieve excellent adsorption performance, improve spraying quality and Efficiency, excellent wear and corrosion resistance effect

Inactive Publication Date: 2020-02-21
苏州嘉睦碧晟建筑装饰有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the existing aluminum alloy surface treatment before spraying is not in place, and there are still small pits or cracks on the aluminum alloy surface, which leads to uneven surface after passivation treatment of the aluminum alloy surface, and finally leads to unsatisfactory spraying effect. Now design A spraying method for aluminum alloy doors and windows to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: a kind of spraying method of aluminum alloy doors and windows, this method comprises the following steps:

[0021] S1. Pretreatment: Perform mechanical polishing on the surface of the aluminum alloy profile to remove defects such as air bubbles, roughening, pressing pits, and bending on the surface of the aluminum profile;

[0022] S2. Degreasing: put the pretreated aluminum profile into the degreasing solution for degreasing treatment, and rinse with water after degreasing;

[0023] S3. Degreasing: put the aluminum profile into the degreasing liquid for degreasing treatment, and rinse with water after degreasing;

[0024] S4, neutralization: put the washed aluminum profile into the neutralization solution for neutralization treatment, and rinse with clean water after neutralization;

[0025] S5. Electrochemical polishing: Electrochemical polishing is used to polish the aluminum profile again, and rinse with clean water after treatment;

[0026] S6. Anod...

Embodiment 2

[0033] Embodiment 2: a kind of spraying method of aluminum alloy doors and windows, this method comprises the following steps:

[0034] S1. Pretreatment: Perform mechanical polishing on the surface of the aluminum alloy profile to remove defects such as air bubbles, roughening, pressing pits, and bending on the surface of the aluminum profile;

[0035] S2. Degreasing: put the pretreated aluminum profile into the degreasing solution for degreasing treatment, and rinse with water after degreasing;

[0036] S3. Degreasing: put the aluminum profile into the degreasing liquid for degreasing treatment, and rinse with water after degreasing;

[0037] S4, neutralization: put the washed aluminum profile into the neutralization solution for neutralization treatment, and rinse with clean water after neutralization;

[0038] S5. Electrochemical polishing: Electrochemical polishing is used to polish the aluminum profile again, and rinse with clean water after treatment;

[0039] S6. Anod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of aluminum alloy door and window spray-coating, and particularly discloses a spray-coating method of an aluminum alloy door and window. The method includes the steps of preprocessing, degreasing, deoiling, neutralizing, electrochemical polishing, anodizing, spray-coating and curing. The completeness of the surface of a non-spray-coated aluminum alloy profile can be improved, the smoothness of the surface of a anodized aluminum profile is improved, and therefore the airtightness of a coating is improved, the decoration performance and corrosion resistance of the aluminum alloy profile are enhanced, the spray-coating quality is improved, and the machining quality of the aluminum alloy profile is improved.

Description

technical field [0001] The invention relates to the related fields of aluminum alloy doors and windows, in particular to a spraying method for aluminum alloy doors and windows. Background technique [0002] Aluminum alloy is an alloy composed of aluminum as a matrix element and one or more alloying elements. Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and has been widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. Especially with the hot expansion of the real estate industry, aluminum alloy profiles have become an important form of exterior wall and interior enclosure in current buildings, reflecting the new concept of modern architecture. [0003] Most of the existing aluminum alloy surface treatment before spraying is not in place, and there are still small pits or cracks on the aluminum alloy surface, which leads to uneven surface after passivation treatment of the alu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14B05D3/02B05D3/10C25D11/16C25F3/20
CPCB05D3/0254B05D3/102B05D7/14C25D11/16C25F3/20
Inventor 董大进
Owner 苏州嘉睦碧晟建筑装饰有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap