A kind of lock type self-healing polymer and its preparation method and application

A technology of self-healing and polymers, which is applied in the field of lock-type self-healing polymers and its preparation, can solve the problems of cumbersome synthesis methods, and achieve the effects of simple repair methods, high repair efficiency, and high yield

Active Publication Date: 2022-04-19
GUANGDONG UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the disadvantages and deficiencies of existing self-healing materials that other groups need to be introduced and the synthesis method is cumbersome, and provide a lock-type self-healing polymer. The lock-type self-healing polymer does not Need to introduce other groups to achieve self-healing, and the repairing efficiency is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lock type self-healing polymer and its preparation method and application
  • A kind of lock type self-healing polymer and its preparation method and application
  • A kind of lock type self-healing polymer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A lock-type self-healing polymer obtained by polymerization of methyl methacrylate (PMMA) and butyl acrylate (BA). The name of the polymer is PMMA-co-PBA.

[0039] The preparation method of PMMA-co-PBA comprises the following steps:

[0040] Dissolve 5.05g MMA, 4.30g BA (molar mass ratio is 6:4) and 0.0936g BPO in 5mL toluene and react in an oil bath at 120°C for 12h. After the reaction is completed, add a certain amount of 5mL toluene, and then add a large amount of The product was precipitated by isopropanol, then filtered with suction, washed with isopropanol, and dried in an oven at 60°C to obtain PMMA-co-PBA.

Embodiment 2

[0042] A lock-type self-healing polymer obtained by polymerization of methyl methacrylate (PMMA) and butyl acrylate (BA). The name of the polymer is PMMA-co-PBA.

[0043] The preparation method of PMMA-co-PBA comprises the following steps:

[0044] Dissolve 5.05g MMA, 4.30g BA (molar mass ratio is 6:4) and 0.0936g BPO in 5mL toluene and react in an oil bath at 100°C for 12h. After the reaction is completed, add a certain amount of 5mL toluene, and then add a large amount of The product was precipitated by isopropanol, then filtered with suction, washed with isopropanol, and dried in an oven at 60°C to obtain PMMA-co-PBA.

Embodiment 3

[0046] A lock-type self-healing polymer obtained by polymerization of methyl methacrylate (PMMA) and butyl acrylate (BA). The name of the polymer is PMMA-co-PBA.

[0047] The preparation method of PMMA-co-PBA comprises the following steps:

[0048] Dissolve 5.05g MMA, 4.30g BA (molar mass ratio is 6:4) and 0.0936g BPO in 5mL toluene and react in an oil bath at 120°C for 8h. After the reaction is completed, add a certain amount of 5mL toluene, and then add a large amount of The product was precipitated by isopropanol, then filtered with suction, washed with isopropanol, and dried in an oven at 60°C to obtain PMMA-co-PBA.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lock-type self-healing polymer and its preparation method and application. The lock-type self-healing polymer is obtained by polymerization of hard segment monomers and soft segment monomers. The hard segment monomers and soft segment monomers are The segment monomers are all acrylate monomers. The preparation method of the lock-type self-healing polymer comprises the following steps: dissolving the hard segment monomer, the soft segment monomer and the initiator in a solvent to undergo a polymerization reaction, adding a precipitating agent after the reaction to obtain precipitation, and the precipitation is the described Lock type self-healing polymer. The invention synthesizes a lock-type self-healing polymer through random copolymerization, which can effectively adjust the softness and interlocking mode of the chain segments by adjusting the ratio and type of monomers; the branched chain on the polymer molecular chain is inserted Interlocking to form a certain riveting force, self-repair can be realized without introducing other groups, and the mechanical strength of the material can be improved. The repair method is simple and the repair efficiency is high. The preparation method is simple, easy to purify and high in yield.

Description

technical field [0001] The invention relates to the technical field of self-healing materials, and more specifically, to a lock-type self-healing polymer and its preparation method and application. Background technique [0002] During the use of materials, due to the influence of environmental factors such as heat, force and light, it is difficult to avoid damage in the form of cracks and defects inside or on the surface of the material, which will reduce the performance of the material and shorten its service life. The traditional repair methods are usually resin injection, adhesive patching and other technologies, but such technologies are difficult to repair the internal damage of the material, and cannot meet the repair requirements of the material. [0003] In recent years, related research on self-healing materials has attracted the attention of society and scientific research circles. This type of material has the ability to repair the micro-cracks of the material, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/14C08F220/18
CPCC08F220/14
Inventor 洪浩群郭权南肖睿靖
Owner GUANGDONG UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com