Metallizable double-sided corona BOPP extinction heat sealing film and preparation method thereof

A metallized and heat-sealable film technology, which is applied in the direction of chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of poor heat-sealing performance and non-heat-sealable packaging, so as to maintain stability and prevent Excellent effect of film adhesion and performance index

Inactive Publication Date: 2020-03-27
ANHUI GUOFENG PLASTIC
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing BOPP matting film has poor heat sealing performance and cannot be heat sealed for packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metallizable double-sided corona BOPP extinction heat sealing film and preparation method thereof
  • Metallizable double-sided corona BOPP extinction heat sealing film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A metallizable double-sided corona BOPP matting heat-sealing film, which consists of an upper surface layer, an upper core layer, a lower core layer, and a lower surface layer from top to bottom, wherein the upper surface layer and the lower surface layer have been treated with corona, and the upper surface layer and the lower surface layer are corona-treated. The surface layer is a heat-sealing layer, the upper core layer is a polypropylene layer, and the lower core layer and lower surface layer are matting layers;

[0026] The heat-sealing layer is made of the following raw materials by weight percentage: 96% of ternary copolymerization heat-sealing masterbatch and 4% of anti-blocking masterbatch. The melt index of the ternary copolymerization heat-sealing masterbatch is 5g / 10min at 230°C / 2.16kg; the ternary copolymerization heat-sealing masterbatch is made of the following raw materials by weight percentage: terpolymerization polypropylene 85%, ethylene-butylene ethy...

Embodiment 2

[0036] A metallizable double-sided corona BOPP matting heat-sealing film, which consists of an upper surface layer, an upper core layer, a lower core layer, and a lower surface layer from top to bottom, wherein the upper surface layer and the lower surface layer have been treated with corona, and the upper surface layer and the lower surface layer are corona-treated. The surface layer is a heat-sealing layer, the upper core layer is a polypropylene layer, and the lower core layer and lower surface layer are matting layers;

[0037] The heat-sealing layer is made of the following raw materials by weight percentage: 97% of ternary copolymerization heat-sealing masterbatch and 3% of anti-blocking masterbatch. The melt index of the ternary copolymerization heat-sealing masterbatch is 6g / 10min under the condition of 230℃ / 2.16kg; the ternary copolymerization heat-sealing masterbatch is made of the following raw materials by weight percentage: terpolymerization polypropylene 80%, ethy...

Embodiment 3

[0047] A metallizable double-sided corona BOPP matting heat-sealing film, which consists of an upper surface layer, an upper core layer, a lower core layer, and a lower surface layer from top to bottom, wherein the upper surface layer and the lower surface layer have been treated with corona, and the upper surface layer and the lower surface layer are corona-treated. The surface layer is a heat-sealing layer, the upper core layer is a polypropylene layer, and the lower core layer and lower surface layer are matting layers;

[0048] The heat-sealing layer is made of the following raw materials by weight percentage: 98% of ternary copolymerization heat-sealing masterbatch and 2% of anti-blocking masterbatch. The melt index of the ternary copolymerization heat-sealing masterbatch is 6g / 10min under the condition of 230℃ / 2.16kg; the ternary copolymerization heat-sealing masterbatch is made of the following raw materials by weight percentage: terpolymerization polypropylene 82%, ethy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a metallizable double-sided corona BOPP extinction heat sealing film and a preparation method thereof. The metallizable double-sided corona BOPP extinction heat sealing film issequentially composed of an upper surface layer, an upper core layer, a lower core layer and a lower surface layer. The corona treatment is conducted on the upper surface layer and the lower surfacelayer, the upper surface layer is a heat sealing layer, the upper core layer is a polypropylene layer, and the lower core layer and the lower surface layer are extinction layers. The heat sealing layer is prepared from the following raw materials in percentage by weight: 96-98% of ternary polymerization heat sealing master batch and 2-4% of anti-blocking master batch. The BOPP film prepared by themethod has high elasticity modulus and low thermal shrinkage rate, and the performance indexes such as haze and glossiness of the extinction layerd are excellent.

Description

technical field [0001] The invention relates to the field of film technology, in particular to a metallizable double-sided corona BOPP matting heat-sealing film and a preparation method thereof. Background technique [0002] Heat-seal aluminized film is a functional film with good transparency, high stiffness, low static electricity, low heat-sealing temperature, haze less than 2%, and small friction coefficient, which is used for metallized substrates. The metallized base material greatly improves the barrier property, thereby prolonging the timeliness of the package, and is widely used in food packaging. After partial printing, it is used for independent packaging of small products, suitable for vertical or horizontal packaging; products are simply printed on the surface and then heat-welded and heat-sealed (lap joint type), packaging CDs, snow cakes, cakes, etc.; products and back-printed BOPP , BOPET film compounded and then self-connected heat-sealed, packaging various...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/32B32B33/00B32B27/08C08L23/14C08L23/08C08L23/12C08L23/06C08K7/18C08J5/18
CPCB32B27/08B32B27/32B32B33/00C08J5/18C08J2323/14C08J2423/06C08J2423/12C08J2423/14C08K7/18C08K2201/011
Inventor 谢城城
Owner ANHUI GUOFENG PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap