Superhydrophobic phenolic resin laminate and preparation method thereof

A technology of phenolic resin and laminate, which is applied in lamination, lamination equipment, lamination auxiliary operation, etc., can solve the problems of unsatisfactory, complicated preparation process, and failure to improve the hydrophobicity and wear resistance of phenolic resin laminates. Achieve the effect of convenient operation and simple preparation process

Active Publication Date: 2021-11-09
HUBEI POLYTECHNIC UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantage of this method is that it does not improve the hydrophobicity and wear resistance of the phenolic resin laminate, and cannot meet the needs of practical applications.
However, the disadvantage of this method is that the preparation process is complicated, and the impact resistance and wear resistance of the laminate have not been improved, so it is difficult to carry out large-scale popularization and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Superhydrophobic phenolic resin laminate and preparation method thereof
  • Superhydrophobic phenolic resin laminate and preparation method thereof
  • Superhydrophobic phenolic resin laminate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The invention provides a kind of preparation method of superhydrophobic phenolic resin laminate, comprises the steps:

[0040] S1. Preparation of phenolic resin laminate: Prepare a mixed solution of phenolic resin / organic solvent with a predetermined concentration, then use the mixed solution to infiltrate the paper-based material, and dry it at 110-130°C for 20-40 minutes to obtain a prepreg ; Then, the prepreg is stacked and thermocompressed to obtain a phenolic resin laminate;

[0041] S2. Prepare super-hydrophobic coating: prepare a polyvinyl chloride / tetrahydrofuran mixed solution, then add the organic solvent into the mixed solution, and stir to obtain a super-hydrophobic coating;

[0042] S3. Preparation of a superhydrophobic phenolic resin laminate: using the superhydrophobic coating described in step S2 to spray-coat and dry the surface of the phenolic resin laminate described in step S1 to obtain a superhydrophobic phenolic resin laminate.

[0043] Further, i...

Embodiment 1

[0057] see Figure 1-3 Shown, the preparation method of superhydrophobic phenolic resin laminate:

[0058] S1, preparation of phenolic resin laminate:

[0059] Bake the kraft paper for 1 hour at a temperature of 110°C. After drying, put it in a sealed bag and store it in a dry environment; Evenly apply a layer of the above-mentioned phenolic resin mixed solution on both sides of the kraft paper, and let it stand until the phenolic resin completely infiltrates the kraft paper; bake the soaked kraft paper at 110°C for a certain period of time for 30 minutes, take it out after drying, and cool it at room temperature.

[0060] Cut off the edges of the dried and cooled prepregs and cut them to the same size; turn on the flat vulcanizer, set the temperature to 120°C, and adjust the pressure to 2MPa; stack the cut 6 prepregs on the iron On the prepreg, press three iron plates on the prepreg, use ten sheets of paper to separate the prepreg and the iron plate, and separate the prepre...

Embodiment 2

[0071] The difference with embodiment 1 is: as Figure 4 As shown, the phenolic resin-coated laminate prepared in step S1 is subjected to surface grinding pretreatment, and other steps are the same as in Example 1, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
densityaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention provides a superhydrophobic phenolic resin laminate and a preparation method thereof. First, prepare a predetermined concentration of phenolic resin / organic solvent mixed solution to infiltrate the paper-based material, and then dry it to obtain a prepreg; then perform stacking thermocompression molding and pretreatment on the prepreg to obtain a phenolic resin laminate; then , prepare a polyvinyl chloride / tetrahydrofuran mixed solution and then add an organic solvent to obtain a superhydrophobic coating; finally, use a superhydrophobic coating to spray-dry the surface of the phenolic resin laminate to obtain a superhydrophobic phenolic resin laminate. The impact strength of the superhydrophobic phenolic resin laminate provided by the invention reaches 11.978kJ / m 2 , with a density of 1.41g / cm 3 , the elastic modulus and bending strength reached 23.8GPa and 642.7Mpa respectively, and its contact angle reached more than 160°, while the contact angle of the laminate with kraft paper attached to the substrate can be maintained above 155°, which has excellent hydrophobic properties.

Description

technical field [0001] The invention relates to the field of laminate material preparation, in particular to a superhydrophobic phenolic resin laminate and a preparation method thereof. Background technique [0002] As one of the three general-purpose resins, phenolic resin has good adhesion. The cured phenolic resin has high heat resistance, good dielectric properties, excellent ablation resistance and good mechanical properties. Blended with other polymers to achieve high performance and widely used in various fields of national economy such as aerospace, automobile, electronics, machinery, transportation and so on. However, after curing, the phenolic resin has the defects of high brittleness, poor impact resistance and non-abrasion resistance. Moreover, because phenol, one of the raw materials for phenolic resin synthesis, contains a large amount of hydrophilic group phenolic hydroxyl groups, and phenolic hydroxyl groups do not participate in the reaction during the synt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/30D21H17/48D21H17/06D21H21/18C09D127/06B32B29/00B32B29/06B32B37/06B32B37/10B32B38/08B32B33/00
CPCB32B29/005B32B29/06B32B33/00B32B37/06B32B37/10B32B38/08B32B2250/26B32B2255/26B32B2255/28B32B2260/028B32B2260/046B32B2307/554B32B2307/558B32B2307/73C09D127/06D21H17/06D21H17/48D21H21/18D21H27/30
Inventor 阮敏范士林李凡奇常忠维刑雅艺吕召春王德华
Owner HUBEI POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com