Ceramic tile anti-cockroach agent and preparation method thereof, ceramic tile anti-cockroach method and anti-cockroach ceramic tile

A ceramic tile and antifouling agent technology, which is applied in botany equipment and methods, biocides, pest control, etc., can solve the problems of low safety in the production process, complicated preparation methods, and poor effect of repelling and killing cockroaches, so as to ensure The effect of uniformity, simple operation and low safety requirements

Active Publication Date: 2020-04-28
FOSHAN OCEANO CERAMICS
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The tile anti-cockroach agent in the prior art has the problems of poor repelling and killing cockroaches, low safety in the production process, and complicated preparation methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0060] The second aspect of the present invention provides the preparation method of the tile anti-cockroach agent described in the first aspect, comprising:

[0061] Step a) mixing the film-forming agent and water at a ratio of mass ratio (3-8): 20, and dispersing evenly to prepare liquid A;

[0062] Step b) Mix the emulsifier and water at a mass ratio of 1: (2-10), disperse evenly, then add cockroach repellent and antifouling agent in turn, emulsify, and prepare B liquid;

[0063] Step c) Mix liquid A and liquid B, add a slow-release filler, and then add the remaining amount of water, mix well, defoam, and obtain the tile anti-cockroach agent.

[0064] The preparation method provided by the invention has simple operation, low requirements on production equipment, high safety in the production process, and is beneficial to actual production and application.

[0065] In some embodiments of the present invention, the preparation method includes:

[0066] Step a) pre-mixing th...

Embodiment 1

[0078] The present embodiment provides a kind of anti-cockroach agent for tiles, which consists of 2.5 grams of cockroach repellent (methethrin), 5.0 grams of film-forming agent (hydroxypropyl cellulose), 5.0 grams of emulsifier (polyoxyethylene sorbitan fat Ester), 3.5 grams of slow-release filler (sepiolite, particle size is 300 mesh), 1.5 grams of antifouling agent (nano silicon dioxide), 82.5 grams of deionized water. The preparation method is as follows:

[0079] (1) Pre-mix the hydroxypropyl cellulose and 20.0 grams of deionized water, and stir with a mechanical stirrer at a speed of 300 rpm for 25 minutes until the dispersion is uniform, and A liquid is obtained;

[0080] (2) Add polyoxyethylene sorbitan fatty acid ester to 20.0 grams of deionized water, stir for 20 minutes, until the dispersion is uniform, then add mefethrin and nano silicon dioxide in turn, use mechanical stirring for 30 minutes, until The emulsification is complete, and B liquid is obtained;

[008...

Embodiment 2

[0083] The present embodiment provides a kind of anti-cockroach agent for tiles, which consists of 1.0 gram of cockroach repellent (transfluthrin), 3.0 gram of film-forming agent (hydroxyethyl cellulose), 4.0 gram of emulsifier (polyoxyethylene monolaurate) ), 2.5 grams of slow-release filler (diatomaceous earth, a particle size of 250 mesh), 1.5 grams of antifouling agent (nano silicon dioxide), and 88.0 grams of deionized water. The preparation method is as follows:

[0084] (1) Pre-mix hydroxyethyl cellulose and 20.0 grams of deionized water, stir with mechanical stirring at a speed of 300 rpm for 25 minutes, until the dispersion is uniform, and obtain liquid A;

[0085] (2) Add polyoxyethylene monolaurate to 20.0 grams of deionized water, stir for 20 minutes until uniformly dispersed, then add transfluthrin and nano-silica in turn, and use mechanical stirring for 30 minutes until emulsification is complete , to prepare liquid B;

[0086] (3) Mix liquid A and liquid B, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a ceramic tile anti-cockroach agent and a preparation method thereof, a ceramic tile anti-cockroach method and an anti-cockroach ceramic tile. The ceramic tile anti-cockroach agent comprises the following components in percentage by mass: 0.5%-5.0% of a cockroach repellent, 3.0%-12.0% of a film-forming agent, 1.0%-13.0% of an emulsifier, 0.1%-10.0% of a slow-release filler,0.1%-3.0% of an antifouling agent and 57.0%-95.3% of water. The ceramic tile anti-cockroach agent has long-acting anti-cockroach and cockroach-repelling effects, the preparation method is simple to operate, the requirement on production equipment is low, the safety in the production process is high, and the actual production and application are facilitated.

Description

technical field [0001] The invention relates to the field of pest repellents, in particular to a tile anti-cockroach agent and a preparation method thereof, a tile anti-cockroach method and an anti-cockroach tile. Background technique [0002] Cockroach is a common sanitary pest, widely distributed in tropical and subtropical regions, and has very strong ability to survive and reproduce. Cockroaches are omnivorous insects. In houses, warehouses, storage rooms, etc., they can eat cotton and wool products, leather products, paper, books, soap, etc. In places such as outdoor garbage dumps, gutters and toilets, they feed on decaying organic matter and even gnaw on dead animals. Because cockroaches like to crawl everywhere and eat everything, they are infected and swallowed a lot of pathogens. The findings suggest that cockroaches can be artificially infected with bacteria that cause Asian diseases such as cholera, pneumonia, diphtheria, melioid, anthrax and tuberculosis. In a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N53/06A01N53/10A01N65/28A01N65/44A01N25/08A01N25/18A01P17/00E04F13/14
CPCA01N25/08A01N25/18A01N53/00A01N65/00A01N65/28A01N65/44E04F13/142Y02A50/30
Inventor 孙飞野柯善军田维马超朱志超周营
Owner FOSHAN OCEANO CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap