Method for preparing magnetic 4a zeolite with kaolin and red mud as raw materials

A technology of kaolin and red mud, which is applied in the field of preparing magnetic 4A zeolite, can solve the problems of weak magnetic properties and many steps of magnetic zeolite, achieve the effect of reducing wastewater treatment process, facilitating large-scale industrial preparation, and realizing large-scale industrial preparation

Active Publication Date: 2021-06-22
HUAIYIN INSTITUTE OF TECHNOLOGY
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Among the above-mentioned magnetic zeolite preparation methods, the first two methods need to use iron salts to synthesize magnetic particles, and there are many steps, and a large amount of waste water will be generated when synthesizing magnetic materials; the third method introduces ferromagnetic materials (pyrite, red mud) to prepare Due to the limited magnetic properties of the magnetic zeolite, the magnetic properties of the obtained magnetic zeolite are weak and need to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing magnetic 4a zeolite with kaolin and red mud as raw materials
  • Method for preparing magnetic 4a zeolite with kaolin and red mud as raw materials
  • Method for preparing magnetic 4a zeolite with kaolin and red mud as raw materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0018] 2g of red mud and 20g of kaolin were mixed uniformly in a ball mill for 30min according to the mass ratio of 1:10; then they were calcined at 650°C for 1h under a nitrogen atmosphere, and then reduced by hydrogen for 1h; 2.2g of the reduced red mud and kaolin mixture, 0.36 Mix 1 g of sodium hydroxide and 20 g of water in a mass ratio of 6:1:50, stir evenly to form a gel-like mixture, then transfer it to a reaction kettle, heat and crystallize at 90°C, cool, wash with water, and dry to obtain the magnetic 4A zeolite.

[0019] The XRD spectrum, SEM photos and magnetic separation photos of the magnetic 4A zeolite prepared in this embodiment are as follows: figure 1 , 2 and 3. It can be seen that the obtained zeolite is A-type zeolite with high crystallinity, and its shape is the cubic shape of 4A zeolite. It has good magnetic properties and can realize rapid separation under an external magnetic field.

Embodiment approach 2

[0021] 2.5g of red mud and 20g of kaolin were mixed uniformly in a ball mill for 45 minutes according to the mass ratio of 1:8; then calcined at 600°C for 2 hours under a nitrogen atmosphere, and then reduced by hydrogen for 1.5 hours; 2.2g of the reduced red mud and kaolin mixture , 0.55g sodium hydroxide and 20g water were mixed according to the mass ratio of 6:1.5:50, stirred evenly to form a gel-like mixture, then transferred to a reaction kettle, heated to crystallize at 100°C, cooled, washed with water, and dried to obtain magnetic 4A Zeolite.

Embodiment approach 3

[0023] 5g of red mud and 20g of kaolin were mixed uniformly in a ball mill for 50 minutes according to the mass ratio of 1:4; then they were calcined at 700°C for 3 hours under a nitrogen atmosphere, and then reduced by hydrogen for 2 hours; 2.2g of the reduced red mud and kaolin mixture, 0.44 Mix g sodium hydroxide and 20 g water according to the mass ratio of 6:1.2:50, stir evenly to form a gel-like mixture, then transfer it to a reaction kettle, heat and crystallize at 80°C, cool, wash with water, and dry to obtain magnetic 4A zeolite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of zeolite preparation, and discloses a method for preparing magnetic 4A zeolite using kaolin and red mud as raw materials. ~60min to form a homogeneous mixture; S2: The mixture of kaolin and red mud was calcined at 600~700°C for 2~3h under a nitrogen atmosphere, and then reduced by hydrogen for 1~2h; S3: The mixture of red mud and kaolin obtained in S2, sodium hydroxide Mix with water according to the mass ratio of 6:1~1.5:50, and stir evenly to form a gel-like colloid; S4: Transfer the gel-like mixture to a reaction kettle, heat and crystallize at 80~100°C, cool, wash with water, and dry. A magnetic 4A zeolite is obtained. Compared with the prior art, the present invention uses kaolin and red mud as raw materials to prepare magnetic 4A zeolite through calcination, activation and reduction, hydrothermal treatment after adding lye, realizes low-cost and green preparation of magnetic 4A zeolite, and avoids the preparation of magnetic particles. The subsequent processing process is reduced, economical and environmentally friendly.

Description

technical field [0001] The invention relates to the technical field of zeolite preparation, in particular to a method for preparing magnetic 4A zeolite by using kaolin and red mud as raw materials. Background technique [0002] 4A zeolite is a zeolite molecular sieve with excellent adsorption properties, which is widely used in detergent aids, desiccants, adsorbents and other products. In order to reduce costs, many clay minerals are used to synthesize 4A zeolite. At present, commercial 4A zeolite is mostly prepared from bauxite or waste aluminum slag from aluminum factories. Kaolin is a non-metallic clay mineral containing silicon and aluminum. Its theoretical composition is similar to that of 4A zeolite. It is an ideal raw material for preparing 4A zeolite. After calcination and activation of kaolin, it can be obtained by hydrothermal crystallization by adding NaOH solution. [0003] The synthesized 4A zeolite has a small particle size, and there are still separation prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/18C01G49/08
CPCC01B39/18C01G49/08C01P2002/72C01P2004/03C01P2004/80C01P2006/42
Inventor 朱朝蒋文彬裘倩倩蔡韡郑恒刘木子蒋金龙吴妹谷亚昕
Owner HUAIYIN INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com