Method for preparing cerium-zirconium-aluminum composite oxide
A composite oxide, cerium zirconium aluminum technology, applied in chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, chemical/physical processes, etc., can solve the complex preparation process, high cost, structure and texture. structural instability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] A method for preparing cerium-zirconium-aluminum composite oxides, comprising the steps of: 35 parts of CeO 2 and 20 parts ZrO 2 Put it into a planetary high-energy ball mill, use a stainless steel tank and quenched steel balls, the ball-to-material ratio is 10:1, the speed is 250r / min, ball mill for 32 hours under the protection of argon, and then add 55 parts of Al 2 o 3 The powder is then ball-milled for 32 hours, and then the obtained powder is placed in a box-type resistance furnace, roasted at 890° C. for 3 hours, and cooled to obtain the product; all raw materials are parts by weight.
Embodiment 2
[0016] A method for preparing cerium-zirconium-aluminum composite oxides, comprising the steps of: 30 parts of CeO 2 and 15 parts of ZrO 2 Put it into a planetary high-energy ball mill, use a stainless steel tank and quenched steel balls, the ball-to-material ratio is 10:1, the speed is 250r / min, ball mill for 31 hours under the protection of argon, and then add 50 parts of Al 2 o 3 The powder is then ball-milled for 31 hours, and then the prepared powder is placed in a box-type resistance furnace, roasted at 885° C. for 2.5 hours, and cooled to obtain the product; all raw materials are parts by weight.
Embodiment 3
[0018] A method for preparing cerium-zirconium-aluminum composite oxides, comprising the steps of: 40 parts of CeO 2 and 25 parts ZrO 2 Put it into a planetary high-energy ball mill, use a stainless steel tank and quenched steel balls, the ball-to-material ratio is 10:1, the speed is 250r / min, ball mill for 33 hours under the protection of argon, and then add 60 parts of Al 2 o 3 The powder is then ball-milled for 33 hours, and then the prepared powder is placed in a box-type resistance furnace, roasted at 895° C. for 3.5 hours, and cooled to obtain the product; all raw materials are parts by weight.
[0019] The method is simple, fast and easy to operate, and can prepare a large amount of CeO 2 -ZrO 2 The composite powder of solid solution, the prepared cerium-zirconium-aluminum composite oxide has good stability, large specific surface area and excellent catalytic activity.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com