Preparation method of waterborne epoxy floor paint

An epoxy floor paint, water-based technology, applied in epoxy resin coatings, chemical instruments and methods, fibrous fillers, etc., can solve the problem of not considering the interface between graphene and water-based epoxy floor paint, poor stability, inability It has been subjected to problems such as acid and alkali erosion for a long time to achieve the effect of prolonging the time of acid and alkali resistance, good performance stability and excellent comprehensive performance.

Inactive Publication Date: 2020-06-09
启东曦瑞新材料科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the water-based epoxy floor paint prepared by this method overcomes the agglomeration phenomenon of graphene, making the paint film withstand the erosion of a certain concentration of acid-base medium, but due to not considering the relationship between graphene and water-based epoxy floor paint Interface, in long-term use, its stability is poor, and it cannot withstand the erosion of acid and alkali for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of waterborne epoxy floor paint
  • Preparation method of waterborne epoxy floor paint

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A preparation method of water-based epoxy floor paint, characterized in that, comprising the following steps:

[0027] S1. Preparation of modified inorganic filler:

[0028] a. natural cellulose is placed in the reactor, then the temperature in the reactor is raised to 120~140 ℃, the pressure in the reactor is raised to 2~3MPa, and the relative humidity of the air in the control reactor is 88~98 %, after high temperature and high pressure treatment for 2 to 3 minutes, the pressure is quickly released to normal pressure, and the treated natural cellulose is taken out for use;

[0029] b. First, the natural cellulose and graphene powder treated in operation a are immersed in the treatment solution in a ratio of 80 to 90:1 by weight, and the temperature in the treatment solution is kept at 80 to 90 ° C, and the stirring treatment is performed for 30 to 40 minutes. Suction filtration, then put the solid mixture obtained by suction filtration into a cryogenic pulverizer, an...

Embodiment 1

[0044] A preparation method of water-based epoxy floor paint, characterized in that, comprising the following steps:

[0045] S1. Preparation of modified inorganic filler:

[0046] a. The natural cellulose is placed in the reactor, then the temperature in the reactor is raised to 120 ° C, the pressure in the reactor is raised to 2MPa, the relative humidity of the air in the control reactor is 88~98%, high temperature and high pressure After 2 minutes of treatment, the pressure was quickly released to normal pressure, and the treated natural cellulose was taken out for use;

[0047] b. First, the natural cellulose and graphene powder treated in operation a are immersed in the treatment solution according to the weight ratio of 80:1, keep the temperature in the treatment solution at 80°C, stir for 30min, suction filtration, and then pump The filtered solid mixture was put into a cryogenic pulverizer, and pulverized in a liquid nitrogen environment. The speed of the pulverizer w...

Embodiment 2

[0058] A preparation method of water-based epoxy floor paint, characterized in that, comprising the following steps:

[0059] S1. Preparation of modified inorganic filler:

[0060] a. The natural cellulose is placed in the reactor, then the temperature in the reactor is raised to 130 ° C, the pressure in the reactor is raised to 2.5MPa, the relative humidity of the air in the control reactor is 93%, and the high temperature and high pressure treatment After 2.5 minutes, the pressure was quickly released to normal pressure, and the treated natural cellulose was taken out for use;

[0061] b. First, the natural cellulose and graphene powder treated in operation a are immersed in the treatment solution according to the weight ratio of 85:1, keep the temperature in the treatment solution at 85 ° C, stir for 35 minutes, suction filtration, and then pump The filtered solid mixture was put into a cryogenic pulverizer, and pulverized in a liquid nitrogen environment. The speed of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of waterborne epoxy floor paint, and belongs to the technical field of floor paint processing and preparation, wherein the preparation method comprises thefollowing steps: S1, preparing a modified inorganic filler; S2, weighing raw materials; and S3, preparing a finished product. The invention provides the preparation method of the waterborne epoxy floor paint. The special modified inorganic filler is added in the preparation of the waterborne epoxy floor paint; the compatibility of the modified inorganic filler and the matrix component is excellent; the acid and alkali resistance, the oil resistance, the water resistance and the wear resistance of the finally prepared waterborne epoxy floor paint are effectively improved, so that a paint filmis corroded by an acid and alkali medium with a certain concentration, the acid and alkali resistance time is prolonged, the performance stability is good, the defect that the hardness of the paint film is too low is overcome, the hardness can reach 4H, and the comprehensive performance is excellent.

Description

technical field [0001] The invention belongs to the technical field of floor paint processing and preparation, and particularly relates to a preparation method of a water-based epoxy floor paint. Background technique [0002] Epoxy floor paint (or epoxy paint) coating is a ground and wall coating method that has risen rapidly with the advancement of industrial technology and the improvement of people's living standards. At present, epoxy floor paint has become the coating industry. One of the strongest developing lacquers in China. Epoxy floor paint is known for its many advantages, such as the coating surface is smooth and clean, and can be in a matte state of diffuse reflection; good integrity, less or complete, no gaps, so it is not easy to accumulate dust and bacteria , easy to clean; high surface hardness, with a certain degree of wear resistance and compressive strength; rich colors, bright, decorative; good waterproof and anti-permeability, which can avoid polluting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D7/62C09D7/63C09D7/65C09C1/46C09C3/04C09C3/10
CPCC08L2205/035C09C1/46C09C3/006C09C3/04C09C3/10C09D163/00C09D7/62C09D7/63C09D7/65C08L91/06C08L83/04C08L71/02C08K13/06C08K9/08C08K3/042C08K5/098C08K5/12C08K5/053C08K5/1345C08K5/42
Inventor 张华
Owner 启东曦瑞新材料科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com