Non-magnetic hard alloy for instrument shaft and preparation method thereof

A cemented carbide, non-magnetic technology, applied in the field of non-magnetic cemented carbide for instrument shafts and its preparation, can solve the problems of limited use range, interference of measurement accuracy, not durable, etc., and achieve a wide range of use and stable work. The effect of good sex and long working hours

Active Publication Date: 2020-07-10
江西中孚硬质合金股份有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The instrument transmission shaft is mainly made of steel, and its main defect is low hardness, not durable and because it is a magnetic material, its measurement accuracy is disturbed and affected in the widespread electromagnetic environment, and the scope of use is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-magnetic hard alloy for instrument shaft and preparation method thereof
  • Non-magnetic hard alloy for instrument shaft and preparation method thereof
  • Non-magnetic hard alloy for instrument shaft and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment takes the total weight of 100kg as an example for illustration:

[0039] Step 1, weighing raw materials:

[0040]

[0041] WC powder requirements: Fsss particle size: 2-4u, carbon content: 5.91-5.95%;

[0042] W powder requirements: Fsss particle size: 2-4u;

[0043] Ni powder requirements: Fsss particle size: 1.5-2.5u, Ni powder is preferably Canadian nickel powder;

[0044] Cr 3 C 2 Powder requirements: Fsss particle size: 1-2u;

[0045] Mo powder requirements: Fsss particle size: 1-2u;

[0046] Step 2, mixing the above raw materials, and then adding a wet grinding agent for wet grinding (such as alcohol);

[0047] Step 3, sieving;

[0048] Step 4, after drying, sieve again;

[0049] Step 5, adding a molding agent for mixing;

[0050] Step 6, extrusion molding;

[0051] Step 7, get rid of forming agent;

[0052] Step 8, sintering;

[0053] Step 9, physical testing; check whether the magnetic force, void, density, strength, and hardness o...

Embodiment 2

[0062] This embodiment is basically the same as Embodiment 1, except that MoC powder is used instead of Mo powder.

Embodiment 3

[0064] The present embodiment is basically the same as embodiment 1, and the difference is that the raw materials taken are:

[0065]

[0066]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a non-magnetic hard alloy for instrument shaft and a preparation method thereof. The hard alloy is prepared from the raw materials in percentage by weight: 86.5 % of WC powder,1.6 % of W powder, 11 % of Ni powder, 0.4 % to 0.6 % of Cr3C2 powder and 0.3 % to 0.5 % of Mo powder or MoC powder. The preparation method comprises the steps of raw material weighing, wet grinding,sieving, screening after drying, mixing with a molding agent, extrusion molding, molding agent removing, sintering, physical detecting, shape inspection to obtain products and processing to obtain theinstrument shaft. According to the non-magnetic hard alloy, the requirements of hardness of the instrument shaft can be met, magnetism is further avoided, thus an instrument can resist electromagnetic interference, the working stability is good, and working can also be conducted normally without being affected in the presence environment of surrounding large electric magnetic field.

Description

technical field [0001] The invention relates to a hard alloy material, in particular to a nonmagnetic hard alloy for an instrument shaft and a preparation method thereof. Background technique [0002] The instrument transmission shaft is mainly made of steel, and its main defect is low hardness, not durable and because it is a magnetic material, its measurement accuracy is disturbed and affected in the widespread electromagnetic environment, and the scope of use is limited. . [0003] Cemented carbide material is an alloy material made of hard compound of refractory metal and bonding metal through powder metallurgy process. Cemented carbide has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance and corrosion resistance, especially its high hardness and wear resistance, which basically remain unchanged even at a temperature of 500°C , It still has high hardness at 1000 °C. Therefore, cemented carbide materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/08C22C1/05C22C1/10B22F9/04B22F3/20B22F3/10
CPCB22F3/1021B22F3/20B22F9/04B22F2009/042C22C1/051C22C29/067C22C29/08C22C2202/02
Inventor 李云卿
Owner 江西中孚硬质合金股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com