A kind of anti-smoke oil degeneration material and its preparation method and application, atomization device

An atomizing device, oil deterioration technology, applied in applications, glass manufacturing equipment, tobacco, etc., can solve the problem of easy deterioration of e-liquid, and achieve the effect of wide wavelength range, variable wavelength range, and good effect.

Active Publication Date: 2022-04-29
SHENZHEN JIYOU TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a material for preventing the deterioration of e-liquid and its preparation method, so as to overcome the defect that the e-liquid in the oil cup is easy to deteriorate when exposed to sunlight for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-smoke oil degeneration material and its preparation method and application, atomization device
  • A kind of anti-smoke oil degeneration material and its preparation method and application, atomization device
  • A kind of anti-smoke oil degeneration material and its preparation method and application, atomization device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A material for preventing smoke oil deterioration, characterized in that it comprises the following raw materials in parts by weight: 80 parts of silicon dioxide, 6 parts of soda ash, 2 parts of alumina, 8 parts of limestone, 2 parts of boric acid, 1 part of sodium antimonate, and 15 parts of titanium dioxide , 7 parts of zinc oxide.

[0036] This embodiment provides the preparation method of the anti-smoke oil deterioration material, the specific process is as follows figure 1 described, including the following steps:

[0037] (1) Ingredients: The raw material powder is pulverized and mixed by ball milling to obtain a mixture, the ball milling speed is 400r / min, and the ball milling time is 12h;

[0038] (2) Heating and melting: the mixture in step (1) is heated and melted, the heating rate is 4°C / min, the temperature is 1200°C, the holding time is 2h, clarification, homogenization, and discharge of bubbles to obtain glass liquid;

[0039] (3) Molding: Pour the molte...

Embodiment 2

[0045] A material for preventing smoke oil deterioration, characterized in that it comprises the following raw materials in parts by weight: 80 parts of silicon dioxide, 6 parts of soda ash, 2 parts of alumina, 8 parts of limestone, 2 parts of boric acid, 1 part of sodium antimonate, and 15 parts of titanium dioxide , 7 parts of zinc oxide.

[0046] Titanium dioxide is modified titanium dioxide, and the preparation method of modified titanium dioxide comprises the following steps:

[0047] ① Add cerium nitrate, deionized water, absolute ethanol and acetic acid into the reaction vessel in turn, and stir and mix; for every 0.001mol of cerium nitrate, the required volume of deionized water is 40ml, the required volume of ethanol is 160ml, and the required volume of acetic acid is 36ml;

[0048] ② Mix butyl titanate and ethanol according to the volume ratio of 10:28 to obtain a mixed solution, and the molar ratio of butyl titanate to cerium nitrate in step ① is 1:0.005;

[0049] ...

Embodiment 3

[0058] A material for preventing smoke oil deterioration, characterized in that it includes the following raw materials in parts by weight: 70 parts of silicon dioxide, 5 parts of soda ash, 3 parts of alumina, 9 parts of limestone, 1 part of boric acid, 0.5 parts of sodium antimonate, and 12 parts of titanium dioxide , 8 parts of zinc oxide.

[0059] Titanium dioxide is modified titanium dioxide, and the preparation method of modified titanium dioxide comprises the following steps:

[0060] ① Add cerium nitrate, deionized water, absolute ethanol and acetic acid into the reaction vessel in turn, stir and mix; for every 0.001mol of cerium nitrate, the required volume of deionized water is 50ml, the required volume of ethanol is 140ml, and the required volume of acetic acid is 40ml;

[0061] ② Mix butyl titanate and ethanol according to the volume ratio of 10:30 to obtain a mixed solution, and the molar ratio of butyl titanate to cerium nitrate in step ① is 1:0.015;

[0062] ③ A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of electronic cigarette products, and specifically discloses a material for preventing the deterioration of smoke oil, which includes the following raw materials in parts by weight: 65-80 parts of silicon dioxide, 5-8 parts of soda ash, 2-4 parts of aluminum oxide, and 8-8 parts of limestone. 10 parts, boric acid 1~3 parts, sodium antimonate 0.5~2 parts, titanium dioxide 8~15 parts, zinc oxide 5~8 parts. The invention provides a preparation method of an anti-smoke oil deterioration material. Also provided is an atomizing device, which includes an oil cup made of an anti-smoke oil deterioration material. The anti-smoke oil deterioration material of the present invention has good anti-ultraviolet performance, and the smoke oil is completely wrapped in the oil cup made of the anti-smoke oil deterioration material. If sunlight needs to irradiate the smoke oil, it must pass through the oil cup, the oil cup It will absorb and reflect the ultraviolet rays in the sun that can damage the e-liquid, and prevent the e-liquid from deteriorating.

Description

technical field [0001] The invention belongs to the technical field of electronic cigarette products, and in particular relates to an anti-smoke oil deterioration material, a preparation method and application thereof, and an atomizing device. Background technique [0002] Electronic cigarettes, also known as virtual cigarettes, are a substitute for cigarettes. They are more and more popular among smokers because of their low harm to the human body, no second-hand smoke, no open flames, and no fire hazards. The atomizing device is a part used to heat and atomize the liquid e-liquid in the electronic cigarette. The oil cup of the atomizing device is the container for the e-liquid. The oil cup of the atomizing device on the market is generally made of transparent ordinary glass or plastic. , Transparent ordinary glass or plastic materials cannot protect the e-liquid in the atomizer. When the atomizer is exposed to sunlight for a long time, the e-liquid is easily deteriorated, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/04C03C1/02C03B19/02C03B32/00C03B15/14C03B23/049A24F40/10A24B15/167
CPCC03C1/00C03C1/02C03B19/02C03B32/00C03B15/14C03B23/049A24B15/167
Inventor 肖卫军赵贯云
Owner SHENZHEN JIYOU TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com