Babbitt metal wire and preparation technology thereof

A babbitt alloy and preparation process technology, which is applied in the field of babbitt alloy wire and babbitt alloy wire preparation technology, can solve the problems of poor flexibility and strength of babbitt alloy, difficult to process into wire, etc., so as to improve flexibility and the effect of strength

Active Publication Date: 2020-07-24
SHENZHEN XINGHONGTAI TIN
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a babbitt wire and its preparation process, to solve the problem that the babbitt wire made by the existing technology has poor flexibility and strength and is difficult to process into wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A Babbitt wire of the present invention, comprising the following raw material components in mass percentage: Sb: 8%; Cu: 4%; Au: 0.0001%; ​​Ni: 0.0001%; ​​balance: Sn and traces of Cr, Mo, W element.

[0020] The preparation technology of a kind of babbitt wire of the present invention comprises the following steps:

[0021] -First put the copper material into the intermediate frequency furnace for stirring and melting, then put the tin material into the intermediate frequency furnace for stirring and melting, after the copper and tin materials are melted, add the antimony material, raise the furnace temperature to 800°C-900°C, then stir and Adding hydrogen chloride to remove impurities, wherein the stirring step is carried out by electromagnetic stirring, and each stirring time is 5-15min;

[0022] -Raise the furnace temperature to 1400°C-1500°C, add gold material and nickel-based superalloy containing nickel, molybdenum, tungsten, and chromium and adjust the element...

Embodiment 2

[0026] A Babbitt wire of the present invention, comprising the following raw material components in mass percentage: Sb: 7%; Cu: 3%; Au: 0.002%; Ni: 0.005%; balance: Sn and traces of Cr, Mo, W element.

[0027] The preparation technology of a kind of babbitt wire of the present invention comprises the following steps:

[0028] -First put the copper material into the intermediate frequency furnace for stirring and melting, then put the tin material into the intermediate frequency furnace for stirring and melting, after the copper and tin materials are melted, add the antimony material, raise the furnace temperature to 800°C-900°C, then stir and Adding hydrogen chloride to remove impurities, wherein the stirring step is carried out by electromagnetic stirring, and each stirring time is 5-15min;

[0029] -Raise the furnace temperature to 1400°C-1500°C, add gold material and nickel-based superalloy containing nickel, molybdenum, tungsten, and chromium and adjust the element conte...

Embodiment 3

[0033] A Babbitt wire of the present invention, comprising the following raw material components in mass percentage: Sb: 9%; Cu: 5%; Au: 0.005%; Ni: 0.01%; balance: Sn and traces of Cr, Mo, W element.

[0034] The preparation technology of a kind of babbitt wire of the present invention comprises the following steps:

[0035] -First put the copper material into the intermediate frequency furnace for stirring and melting, then put the tin material into the intermediate frequency furnace for stirring and melting, after the copper and tin materials are melted, add the antimony material, raise the furnace temperature to 800°C-900°C, then stir and Adding hydrogen chloride to remove impurities, wherein the stirring step is carried out by electromagnetic stirring, and each stirring time is 5-15min;

[0036] -Raise the furnace temperature to 1400°C-1500°C, add gold material and nickel-based superalloy containing nickel, molybdenum, tungsten, and chromium and adjust the element conten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a Babbitt metal wire and a preparation technology thereof, and relates to the technical field of mechanical materials. The Babbitt metal wire comprises the following raw material ingredients in parts by weight: 7-18% of Sb, 3-8% of Cu, 0.0001-0.005% of Au, 0.0001-0.01% of Ni and the balance of Sn and trace elements including Cr, Mo and W. A raw material ingredient proportion of the Babbitt metal wire is regulated, the trace elements are added, the flexibility and the metallographic structure of the Babbitt metal which is finally smelted can be greatly improved, a situation that the Babbitt metal is free from a fracture phenomenon when the Babbitt metal is pulled to form wires can be guaranteed, and the flexibility and the strength of the Babbitt metal wire are improved.

Description

technical field [0001] The invention belongs to the technical field of mechanical materials, and in particular relates to a Babbitt wire and a preparation process of the Babbitt wire. Background technique [0002] Babbitt is the most widely known bearing material, a tin- and lead-based bearing alloy with antifriction properties. Babbitt alloys are mainly used in bearing pads, bearings, bushings and bushings of large mechanical spindles. However, the existing babbitt alloy has the characteristics of poor flexibility, so frequent fractures will occur during wire drawing, which makes it difficult to make babbitt alloy into wire shape. Therefore, in view of this technical problem, a Babbitt wire and its preparation process. Contents of the invention [0003] The object of the present invention is to provide a babbitt wire and its preparation process, so as to solve the problem that the babbitt alloy made by the existing technology has poor flexibility and strength and is dif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C13/02C22C1/02C22F1/16
CPCC22C1/02C22C13/02C22F1/16
Inventor 王寿银邢鸿伟邢璧凡邢璧元
Owner SHENZHEN XINGHONGTAI TIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More