Concrete additive and preparation method thereof

An additive and concrete technology, applied in the field of building materials, can solve problems such as unfavorable ecological value and poor environmental performance

Inactive Publication Date: 2020-10-27
韩昌龙
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the component β-sulfonate sodium formaldehyde condensate is used in this invention, which leads to poor environmental performance and is not conducive to the realization of ecological value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] Preferably, the preparation method of the phosphate-based s-triazine-based hyperbranched macromolecular compound comprises the steps of: adding the s-triazine-based hyperbranched compound to an organic solvent, and then adding chloromethyl phosphoric acid thereto, and at 40 Stir and react at -60°C for 4-6 hours, then remove the solvent by rotary evaporation, wash the crude product with ether for 3-5 times, and then remove the ether by rotary evaporation to obtain a phosphate-s-triazine-based hyperbranched macromolecular compound.

[0031] Preferably, the mass ratio of the s-triazine-based hyperbranched compound, organic solvent, and chloromethyl phosphoric acid is (3-4):(10-15):1.

[0032] Preferably, the s-triazine-based hyperbranched compound is a second-generation s-triazine-based hyperbranched compound. For the preparation method, refer to Example 1 of the Chinese invention patent with application number 201910881075.8.

[0033] Preferably, the organic solvent is an...

Embodiment 1

[0049] Embodiment 1 provides a kind of concrete additive, it is characterized in that, comprises the following components by weight: Phosphate-s-triazine-based hyperbranched macromolecular compound 2 parts, sulfonic acid diethanolamine / 1,3-adamantane di 8 parts of acetic acid polycondensate, 1 part of attapulgite, and 1 part of graphene oxide fiber.

[0050] The preparation method of the phosphate-based s-triazine-based hyperbranched macromolecular compound comprises the following steps: adding the s-triazine-based hyperbranched compound to an organic solvent, and then adding chloromethyl phosphoric acid to it, stirring at 40°C After reacting for 4 hours, the solvent was removed by rotary evaporation, and the crude product was washed 3 times with ether, and then the ether was removed by rotary evaporation to obtain a phosphate-s-triazine-based hyperbranched macromolecular compound.

[0051] The mass ratio of the s-triazine-based hyperbranched compound, organic solvent, and chl...

Embodiment 2

[0061] Embodiment 2 provides a kind of concrete additive, it is characterized in that, comprises the following components by weight part: Phosphate-s-triazine-based hyperbranched macromolecular compound 3 parts, sulfonic acid diethanolamine / 1,3-adamantane two 9 parts of acetic acid polycondensate, 1.5 parts of attapulgite, and 2 parts of graphene oxide fiber.

[0062] The preparation method of the phosphate-based s-triazine-based hyperbranched macromolecular compound comprises the following steps: adding the s-triazine-based hyperbranched compound to an organic solvent, then adding chloromethyl phosphoric acid to it, and stirring at 45°C After reacting for 4.5 hours, the solvent was removed by rotary evaporation, and the crude product was washed 4 times with ether, and then the ether was removed by rotary evaporation to obtain a phosphate-s-triazine-based hyperbranched macromolecular compound.

[0063] The mass ratio of the s-triazine-based hyperbranched compound, organic solv...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a concrete additive, which is characterized by being prepared from the following components in parts by weight: 2 to 5 parts of phosphate s-triazinyl hyperbranched macromolecular compound, 8 to 12 parts of sulfonic diethanol amine / 1, 3-adamantane diacetic acid condensation polymer, 1 to 3 parts of attapulgite and 1 to 4 parts of graphene oxide fiber. The invention also discloses a preparation method of the concrete additive. The concrete additive disclosed by the invention is more excellent in water reducing effect, less in mixing amount, better in environmental protection property and plasticizing effect, diverse in function, more remarkable in effect of improving the strength, flowability, durability and impermeability of a concrete material, free of negative influence on the comprehensive performance of concrete, and relatively high in economic value, social value and ecological value.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a concrete additive and a preparation method thereof. Background technique [0002] In recent years, with the progress of society and the development of economy, various buildings and construction projects have sprung up. These buildings and construction projects are the crystallization of the development of the times and a symbol of a city. It records the history and Change is the hallmark of modern civilization. Behind these buildings and construction projects that represent modern cities, the use of construction engineering materials is inseparable. Construction engineering materials are a necessary condition to ensure the quality of construction projects and the safety of buildings. Concrete, as an indispensable construction material in the construction process of modern construction engineering, plays a vital role in ensuring the safety and quality of buildings. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/28C04B24/16C08G63/688C08G83/00C04B14/38C04B14/10
CPCC04B24/166C04B24/243C04B40/0039C08G63/6886C08G83/005C04B14/102C04B14/386
Inventor 韩昌龙
Owner 韩昌龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products