Flux-covered welding wire and preparation method thereof

A coating and welding wire technology, which is applied in welding equipment, welding media, manufacturing tools, etc., can solve the problems of high degree of automation and the inability to simultaneously melt the "tube" shape of the end of the welding wire, etc., to achieve a high degree of automation and enhance the overall Effect of position weldability and no fill rate restriction

Pending Publication Date: 2020-10-30
SHANGHAI DIANJI UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a coated welding wire and its preparation method in order to overcome the defects of the above-mentioned prior art, which can successfully combine the advantages of flux-cored welding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flux-covered welding wire and preparation method thereof
  • Flux-covered welding wire and preparation method thereof
  • Flux-covered welding wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example

[0032] A kind of coated welding wire, which consists of a coating and a welding core, and the coating is wrapped outside the welding core. The welding core is the metal core of the welding wire, and it mainly plays the role of conducting current and filling metal during welding. The metal core is a solid wire. Compared with the alloy composition of the coated wire, the metal core can be a solid wire with similar or the same alloy composition, or a solid wire with a different alloy composition. The medicine skin is a medicine skin that contains slag-forming and gas-forming substances. The coating is decomposed and melted in the welding process to form gas and slag, which play a role in protecting and improving process performance. The composition of the deposited metal alloy of the welding wire of the present invention is as follows:

[0033] Table 1 Alloy composition of welding wire deposited metal (mass percentage)

[0034]

[0035] Others are Fe and other unavo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a flux-covered welding wire and a preparation method thereof. The flux-covered welding wire consists of a solid welding wire and a flux cover, wherein the flux cover wraps thesolid welding wire. The preparation method specifically comprises the steps of (1) selecting the solid welding wire as a metal core of the flux-covered welding wire; (2) adjusting the components andthe proportion of the composite flux cover, meanwhile, improving the technological performance according to the actual welding requirement, and taking the treated flux cover as a flux cover blank; and(3) adjusting the thickness, the preheating temperature, the coating speed, the curing temperature and the curing time of the flux cover, and uniformly and firmly coating the outside of the metal core with the flux cover blank. Compared with the prior art, the flux-covered welding wire and the preparation method thereof have the advantages that the problem that all-position welding, high automation degree, zero filling rate limitation and welding wire tip pipe-shaped melting cannot be achieved simultaneously is solved.

Description

technical field [0001] The invention relates to the field of welding materials, in particular to a coated welding wire and a preparation method thereof. Background technique [0002] Welding wire mainly includes solid welding wire and flux cored welding wire. Solid cored wire is made by smelting, pouring, forging, rolling, annealing and drawing, and is protected by adding gas or flux during welding; The cross-sectional shape of the welding wire made by drawing can be protected by adding gas or flux during welding, and can also be self-protected by adding arc stabilizing agents, slagging agents and gas-generating agents to the flux core. Welding rod refers to pressing and coating a certain composition of coating on the welding core outside the special metal welding core, and drying it at a specific temperature to make a strip-shaped welding material. During welding, the coating decomposes and melts to form gas and slag. It plays the role of mechanical protection, metallurgi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/30B23K35/12B23K35/40
CPCB23K35/0266B23K35/3066B23K35/406
Inventor 杨淼森刘西洋方乃文郭彦兵张旺陆斌锋
Owner SHANGHAI DIANJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products