A kind of coating powder composition and the method for preparing coating

A technology of composition and powder, which is applied in coating, metal processing equipment, transportation and packaging, etc., can solve the problems affecting the safety and reliability of fasteners, damage, and the decrease of fastener pre-tightening force, etc., and achieve good The effect of antioxidant protection

Active Publication Date: 2022-02-22
NINGXIA ORIENT TANTALUM IND
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When this coating is applied to the surface of the fastener, it will lead to a decrease in the mechanical properties of the fastener at room temperature, and the phenomenon of slippage will occur during assembly or use, resulting in a decrease in the pre-tightening force of the fastener or complete damage, seriously affecting the fastening Software security and reliability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coating powder composition and the method for preparing coating
  • A kind of coating powder composition and the method for preparing coating
  • A kind of coating powder composition and the method for preparing coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] 1) formulate the coating powder composition shown in table 1, then put into container;

[0078] 2) adding anhydrous ethanol which is 1 times the volume of the above powder composition into the container as a carrier;

[0079] 3) Add 1.2wt% polyethylene glycol of the mass of the above-mentioned powder composition into the container as a binding agent;

[0080] 4) The above materials are made into slurry after high-speed ball milling, the ball milling speed is 150r / min, and the ball milling time is 10h;

[0081] 5) The fastener (blank sample) made of the NbW5-1 alloy of Comparative Example 1 was completely immersed in the slurry for 5 seconds, then taken out, and dried in a ventilated environment for 10 minutes;

[0082] 6) Place the fasteners coated with slurry on the surface in a vacuum resistance furnace for sintering at high temperature and in a vacuum environment (1550°C, below 0.1Pa). After sintering, a high temperature resistant and oxidation resistant coating is ...

Embodiment 2

[0085] 1) formulate the coating powder composition shown in table 1, then put into container;

[0086] 2) adding anhydrous ethanol which is 1 times the volume of the above powder composition into the container as a carrier;

[0087] 3) Add polyethylene glycol (molecular weight 6000) of 5wt% of the mass of the above-mentioned powder composition into the container as a binding agent;

[0088] 4) The above materials are made into slurry after high-speed ball milling, the ball milling speed is 450r / min, and the ball milling time is 3.5h;

[0089] 5) The fastener (blank sample) made of the NbW5-1 alloy of Comparative Example 1 was completely immersed in the slurry for 10 seconds, then taken out, and dried in a ventilated environment for 45 minutes;

[0090] 6) Place the fasteners coated with slurry on the surface in a vacuum resistance furnace for sintering at high temperature and in a vacuum environment (1550°C, below 0.1Pa). After sintering, a high temperature resistant and oxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a coating powder composition, which includes: Mo powder, W powder, Y 2 o 3 powder, Cr powder, V powder, Ta powder, B powder, ZrB 2 powder, KF powder, Ir powder, carbide powder, MoSi 2 Powder, Si powder, wherein, the carbide is selected from one or more of SiC and NbC; wherein, the coating powder composition does not contain Ti element and Hf element.

Description

technical field [0001] The invention belongs to the field of surface treatment, and in particular relates to a coating powder composition and a coating preparation method. Background technique [0002] Aerospace, aerospace vehicle engines, structural parts, and control functional components need to be used in high-temperature oxidizing environments, and fasteners that can simultaneously have high melting points, high room temperature mechanical properties, strong oxidation resistance, and low density requirements are required to adapt to aerospace, aviation, etc. Special requirements for light weight and high strength. In addition, steel, chemical, metallurgical and other industries have many high-temperature operating procedures, and similar fasteners with high temperature resistance, high room temperature mechanical properties, and oxidation resistance are also required. [0003] At present, titanium, iron, cobalt, and nickel-based alloys are mostly used as fastener mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/12B22F9/04C09D1/00
CPCB22F1/0003B22F9/04B22F2009/041B22F1/103B22F1/10
Inventor 赵刚周小军刘尖梁斌王立斐任广宁
Owner NINGXIA ORIENT TANTALUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com