Firing technology of crystal wine set and water set surface patterns

A surface pattern and wineware technology, which is applied in crafts, decorative arts, coatings and other directions for producing decorative surface effects, can solve problems such as the sales of wineware and waterware products without crystals, achieve bright color, meet environmental requirements, The effect of not polluting the environment

Pending Publication Date: 2020-11-03
张展
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no pattern firing technology with crystal materials as the carrier in China, and there are no crystal wine and water utensils made by this process on the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Firing technology of crystal wine set and water set surface patterns

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Step 1: Take a blank crystal wine set as a carrier and put it into an ultrasonic cleaner;

[0025] Step 2: Heat the water temperature of the ultrasonic cleaner to 50°C, add cleaning agent, and clean for 5-10 minutes;

[0026] Step 3: Print the pattern designed on the computer into a pattern sticker through the machine;

[0027] Step 4: Soak the pattern sticker in 30-47°C water for 10-15 minutes;

[0028] Step 5: After the pattern sticker is fully soaked, separate the entire pattern protected by the cover glue from the backing paper;

[0029] Step 6: Paste the separated pattern on the surface of the cleaned crystal wine set;

[0030] Step 7: Send the patterned crystal wine set and water set into a dust-free air-drying box to dry, and the process lasts for about 1-8 hours;

[0031] Step 8: Put the dried crystal wine and water utensils into the kiln for firing. The temperature in the kiln is heated evenly and slowly, from room temperature to 100-120°C in 0-10 minutes, a...

Embodiment 2

[0039] Step 1: Take a blank crystal water tool as a carrier and put it into an ultrasonic cleaner;

[0040] Step 2: Heat the water temperature of the ultrasonic cleaner to 50°C, add cleaning agent, and clean for 5-10 minutes;

[0041] Step 3: Print the pattern designed on the computer into a pattern sticker through the machine;

[0042] Step 4: Soak the pattern sticker in 30-47°C water for 10-15 minutes;

[0043] Step 5: After the pattern sticker is fully soaked, separate the entire pattern protected by the cover glue from the backing paper;

[0044] Step 6: Paste the separated pattern on the surface of the cleaned crystal wine set;

[0045] Step 7: Send the patterned crystal wine set and water set into a dust-free air-drying box to dry, and the process lasts for about 1-8 hours;

[0046] Step 8: Put the dried crystal wine and water utensils into the kiln for firing. The temperature in the kiln is heated evenly and slowly, from room temperature to 100-120°C in 0-10 minutes,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a firing technology of crystal wine set and water set surface patterns. The firing technology comprises the following steps that blank crystal wine sets and water sets are taken and put into an ultrasonic cleaning machine; water temperature inside the ultrasonic cleaning machine is increased for cleaning; patterns are designed on a computer and printed into stickers through a machine; the stickers are soaked in water; after the whole stickers are completely soaked, the whole patterns protected by cover adhesives are separated from backing paper; the separated patternsare pasted to the surfaces of the cleaned crystal wine sets and water sets; the crystal wine sets and water sets with the patterns pasted are sent into an air-drying box for air-drying; the air-driedcrystal wine sets and water sets are put into a kiln for heating and firing, the temperature in the kiln is uniformly and slowly increased, and heating is stopped after the rated temperature is reached; and an air vent of the kiln is opened, and waiting for cooling to the room temperature is carried out until the products are formed. By means of the manner, the exquisite floral patterns are addedto the surfaces of the wine sets and water sets, the original high chemical stability of a crystal material is kept, and the environment requirement for using the wine sets and water sets is met.

Description

technical field [0001] The invention relates to a technology for firing crystal surface patterns, in particular to a technology for firing surface patterns of wine and water utensils. Background technique [0002] Artificial lead-free crystal has the advantages of high permeability, heavy weight, good refraction, and strong impact resistance. However, there is no pattern firing technology with crystal material as the carrier in China, and there is no commercial sale of crystal wine and water utensils made by this process on the market. The present invention utilizes the advantages of the above material itself, and then fires at high temperature in a kiln, so that the aesthetics of the product itself is increased, and it is easier to attract consumers to buy. The present invention is a method for producing crystal wine and water utensils by firing patterns at high temperature. Its biggest advantage is that it can be mass-produced, the process is simple, and it is elegant in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C1/00C03C17/22
CPCB44C1/00C03C17/008C03C2217/29C03C2217/72C03C2218/32
Inventor 张展
Owner 张展