A composite film for liquid medicine packaging and its dry composite process

A technology of dry lamination and dry lamination machine, which is applied in the field of liquid pharmaceutical packaging lamination film and its dry lamination process, which can solve the problems of affecting the bonding force of the lamination film, incomplete removal of solvent, and increase of solvent residue, etc., to achieve production efficiency Improve and reduce the effect of solvent surface skinning and increase solvent volatilization speed

Active Publication Date: 2021-04-06
SICHUAN HUILI IND
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The technical problem to be solved by the present invention is: in the existing dry compounding process, due to incomplete solvent removal or moisture entering during the solvent removal process, it is easy to cause foaming of the composite film, affect the bonding force between the composite films and increase the solvent residue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite film for liquid medicine packaging and its dry composite process
  • A composite film for liquid medicine packaging and its dry composite process
  • A composite film for liquid medicine packaging and its dry composite process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] Adopt the technology of the present invention to prepare PET-AL-CPP, and the technological process is as follows figure 1 shown, including the following specific steps:

[0070] 1. Printing:

[0071] Turn on the printing machine, place the corona-treated PET substrate on the inner layer in the unwinding section of the gravure printing machine, control the unwinding tension to 100N, and then enter the printing section, control the speed of the printing machine to 130m / min, and control the drying temperature at 60℃, control the printing roller pressure to 0.2Mpa and the printing blade pressure to 0.2Mpa, and print the outer layer of the PET substrate. Before printing, use ethyl acetate to adjust the ink viscosity to 13S. After printing, control the winding tension to 60N for winding. .

[0072] 2. Aluminum foil composite:

[0073] Transfer the PET base material printed on the outer layer to the unwinding part of the dry laminating machine, control the unwinding tension...

Embodiment 2

[0079] Example 2

[0080] It is investigated that the temperature of the drying tunnel and the compounding speed are both at the upper limit, that is, the temperature of the first drying tunnel 1 is 72-75 °C; the temperature of the second drying tunnel 2 is 78-80 °C, and the temperature of the third drying tunnel 3 is 88-90 ℃, when the compounding speed is also at the upper limit, that is, the compounding speed of PET and AL is adjusted to 150m / min, and the compounding speed of PET-AL and CPP is adjusted to 200m / min, the performance of the compound film.

Embodiment 3

[0082] Compared with Example 2, the third gear 7 is removed, so that the power drive of the flow aid guide roller 11 to the flow aid 4 is released, that is, the flow aid stops working, and the PET-AL-CPP composite film is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a liquid medicine packaging composite film and its dry composite process, which solves the problem that in the existing dry composite process, due to incomplete solvent removal or moisture entering during the solvent removal process, the composite film is easily caused to foam and affect The binding force between the composite films and the problem of increasing solvent residues, the present invention includes: (1) open the dry composite machine and the induced draft fan, the movement of the guide roller drives the operation of the flow aid in the drying tunnel, and preheats the drying tunnel to make it reach Preset temperature; (2) Glue coating of the outer layer film; (3) After the glue coating is completed, the outer layer film enters the drying tunnel for solvent volatilization; (4) The outer layer film and the barrier layer film are combined to obtain the outer layer-barrier film intermediate product (5) heat-sealing layer film gluing; (6) after the gluing is completed, enter the drying tunnel for solvent volatilization; (7) compound the outer layer-barrier film intermediate product and the heat-sealing layer film to obtain a liquid drug packaging composite film . The invention has the advantages of fast solvent volatilization, good water removal in the drying tunnel and the like.

Description

technical field [0001] The invention relates to the technical field of liquid medicine packaging composite films, in particular to a liquid medicine packaging composite film and a dry compounding process thereof. Background technique [0002] Due to the higher requirements on barrier properties of liquid medicines, the main packaging currently used is still thicker glass bottles, plastic bottles or plastic tubes made of composite hard sheets with better barrier properties. [0003] For the composite film, due to the thin film layer, to meet the use of liquid medicine packaging, the requirements for the composite process are higher. [0004] First, for the structure of the composite film, it is required that the outer layer has good weather resistance, the middle layer has good barrier properties, and the inner layer has good heat sealing performance, and the bonding force between the film layer and the film layer is large. [0005] In the compounding process, in order to ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/085B32B15/09B32B15/20B32B27/32B32B27/36B32B37/12B32B38/00B32B7/12
CPCB32B7/12B32B15/085B32B15/09B32B15/20B32B27/32B32B27/36B32B37/1284B32B38/164B32B2038/168B32B2439/80
Inventor 张辉柏金枝张华江黄蛟
Owner SICHUAN HUILI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com