Anticorrosive and waterproof coating for wooden furniture and preparation method thereof

A technology for waterproof coatings and wooden furniture, applied in anti-corrosion coatings, epoxy resin coatings, coatings and other directions, can solve problems such as unfavorable curing epoxy resin coatings, reducing the production efficiency of wooden furniture, and curing efficiency needs to be improved, etc. Production efficiency, good economic benefits, and the effect of easy construction and use

Pending Publication Date: 2020-11-24
周鹏
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after it is coated on wood, it generally requires a higher curing temperature and a longer curing time, which is not conducive to the curing and molding of epoxy resin coatings and wood, reducing the production efficiency of wooden furniture, and the curing efficiency needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Anticorrosion and waterproof paint for wooden furniture, comprising the following preparation steps:

[0033] (1) Preparation of UV-curable fluoroalcohol-modified epoxy resin: Mix toluene diisocyanate and heptafluorobutanol at a mass ratio of 1:1, then add dibutyltin dilaurate and solvent in sequence, and add bisphenol after the reaction is complete A-type epoxy resin is directional grafted, and then acrylic acid is added to obtain UV-curable fluoroalcohol-modified epoxy resin;

[0034] (2) Preparation of coating components: Mix 110 parts of UV-curable fluoroalcohol modified epoxy resin and 45 parts of acetone, then add 4 parts of benzil, 3 parts of BYK-220S wetting and dispersing agent, 2 parts of BYK -345 and 1 part of silicone defoamer, heat and disperse under stirring conditions. The dispersion conditions are: dispersion temperature 55°C, stirring speed 3800rpm, dispersion time 18min, and the coating component is obtained after aging;

[0035] (3) Preparation of th...

Embodiment 2

[0038] Anticorrosion and waterproof paint for wooden furniture, comprising the following preparation steps:

[0039] (1) Preparation of UV-curable fluoroalcohol-modified epoxy resin: Mix toluene diisocyanate and heptafluorobutanol at a mass ratio of 1:1, then add stannous octoate and solvent in sequence, and add bisphenol F type after the reaction is complete Epoxy resin is directional grafted, and then acrylic acid is added to obtain UV-curable fluoroalcohol-modified epoxy resin;

[0040] (2) Preparation of coating components: Mix 115 parts of UV-curable fluoroalcohol-modified epoxy resin and 35 parts of n-butanol, then add 7 parts of alkyl phenones, 5 parts of BYK-220S wetting and dispersing agent, 1 part of BYK-345 and 2 parts of silicone defoamer, heat and disperse under stirring conditions, the dispersion conditions are: dispersion temperature 60°C, stirring speed 3200rpm, dispersion time 23min, and the coating component is obtained after aging;

[0041] (3) Preparation of...

Embodiment 3

[0044] Anticorrosion and waterproof paint for wooden furniture, comprising the following preparation steps:

[0045] (1) Preparation of UV-curable fluoroalcohol-modified epoxy resin: Mix toluene diisocyanate and heptafluorobutanol at a mass ratio of 1:1, then add dibutyltin dilaurate and solvent in sequence, and add bisphenol after the reaction is complete S-type epoxy resin is directional grafted, and then acrylic acid is added to obtain UV-curable fluoroalcohol-modified epoxy resin;

[0046] (2) Preparation of coating components: Mix 100 parts of UV-curable fluoroalcohol modified epoxy resin and 50 parts of butyl acetate, then add 3 parts of benzophenones, 4 parts of BYK-220S wetting and dispersing agent, 1 part of BYK-345 and 2 parts of silicone defoamer, heat and disperse under stirring conditions, the dispersion conditions are: dispersion temperature 57°C, stirring speed 3500rpm, dispersion time 20min, and the coating component is obtained after aging;

[0047] (3) Prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anticorrosive and waterproof coating for wooden furniture and a preparation method thereof in the technical field of waterproof coatings. The anticorrosive and waterproof coating comprises a coating component and a curing component, wherein the mass ratio of the coating component to the curing component is 18-20: 1; the coating comprises the following raw material raw material in parts by weight: 100-120 parts of ultraviolet light cured fluoroalcohol modified epoxy resin, 30-50 parts of an organic solvent, 2-7 parts of a photoinitiator, 3-5 parts of a dispersant, 1-2parts of a leveling agent and 1-2 parts of a defoamer; the curing component comprises the following raw material in parts by weight: 100-110 parts of an amine curing agent, 2-5 parts of an epoxy accelerator and 15-30 parts of an organic solvent. The anticorrosive and waterproof coating for the wooden furniture has good anticorrosive and waterproof properties, and is higher in curing efficiency under the conditions of normal temperature and illumination, simple in preparation process, and convenient to construct and use; and the manufacturing efficiency of the wooden furniture is effectively improved, and good economic benefits can be brought.

Description

technical field [0001] The invention relates to the technical field of waterproof coatings, in particular to antiseptic and waterproof coatings for wooden furniture and a preparation method thereof. Background technique [0002] Furniture refers to the category of utensils and facilities necessary for human beings to maintain normal life, engage in production practice and carry out social activities. Furniture also follows the footsteps of the times and continues to develop and innovate. Up to now, there are many categories, different materials, complete varieties, and different uses. It is an important foundation for building a working and living space. [0003] Wooden furniture: except for decorative parts and accessories among the main components, the rest are made of wood materials such as wood and wood-based panels. Solid wood furniture: furniture made of solid wood sawn lumber or solid wood boards as the base material, with the surface treated; or furniture that is c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D5/08C08G59/17C08G59/14C08G59/50C08G59/44
CPCC08G59/1477C08G59/1494C08G59/44C08G59/5033C09D5/08C09D163/10
Inventor 周鹏
Owner 周鹏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap