Non-oriented electrical steel plate with extremely-low iron loss and continuous annealing process of non-oriented electrical steel plate

A technology of oriented electrical steel sheet and annealing process, applied in the field of non-oriented electrical steel sheet and its continuous annealing, can solve the problems of production management and quality management, prolong the production time and delivery cycle of finished steel sheet, and increase the manufacturing cost of finished steel sheet.

Inactive Publication Date: 2020-12-29
BAOSHAN IRON & STEEL CO LTD
View PDF25 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these process steps, especially the normalization or intermediate annealing in the bell furnace, will not only greatly increase the manufacturing cost of the finished stee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-oriented electrical steel plate with extremely-low iron loss and continuous annealing process of non-oriented electrical steel plate
  • Non-oriented electrical steel plate with extremely-low iron loss and continuous annealing process of non-oriented electrical steel plate
  • Non-oriented electrical steel plate with extremely-low iron loss and continuous annealing process of non-oriented electrical steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0067] In the following, the ultra-low iron loss non-oriented electrical steel sheet and its continuous annealing process described in the present invention will be further explained and described in conjunction with the accompanying drawings and specific examples. However, the explanation and description do not constitute the technical solution of the present invention. Improperly qualified.

[0068] The conventional electrical steel sheets of each comparative example and the non-oriented electrical steel sheets of the embodiments were prepared by the following steps:

[0069] (1) Use molten iron and steel scrap to match the chemical composition shown in Table 1. After smelting in the converter, RH refining is carried out for decarburization and deoxidation alloying. The molten steel is treated with calcium, nickel, and rare earth by using the input method or the wire feeding method. Treatment, that is, adding one or more of Ca, Mg, and RE to purify the steel and improve the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a non-oriented electrical steel plate with the extremely-low iron loss. The non-oriented electrical steel plate is prepared from the chemical elements including, by mass, morethan 0 and less than or equal to 0.005% of C, 1.0%-3.45% of Si, 0.1%-1.2% of Mn, 0.001%-2.0% of Al, 0-0.2% of Cu, 0-0.0015% of Ti, one or both of Sb and Sn with the total content ranging from 0.005% to 0.2%, one or more of Ca, Mg and RE with the total content ranging from 0.0005% to 0.01% and the balance Fe and other inevitable impurities. Besides, the invention discloses a continuous annealing process of the non-oriented electrical steel plate with the extremely-low iron loss. In addition, the invention discloses a manufacturing method of the non-oriented electrical steel plate with the extremely-low iron loss. The method includes the following steps that smelting is performed; casting is performed; hot rolling is performed; normalizing is performed; cold rolling is performed; the continuous annealing process is carried out; and the plate is coated with an insulating coating, so that the non-oriented electrical steel plate with the extremely-low iron loss is obtained.

Description

technical field [0001] The invention relates to a steel plate and its manufacturing process, in particular to a non-oriented electrical steel plate and its continuous annealing method. Background technique [0002] In recent years, high-efficiency EI iron cores, motors, small transformers and other electrical equipment have become more and more popular, and the reason is that these electrical equipment meet the needs of environmental protection, energy saving and effective reduction of carbon dioxide emissions. At the same time, with the continuous improvement of the comprehensive performance of these electrical equipment, correspondingly, the requirements for the non-oriented electrical steel sheet as its raw material are also gradually increased. Specifically, it is expected that the non-oriented electrical steel sheet should have excellent magnetic properties while ensuring the cost advantage, that is to say, the non-oriented electrical steel sheet used to manufacture the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/14C22C38/16C22C38/60C21D8/12C21D1/74C21D1/26
CPCC21D1/26C21D1/74C21D8/1222C21D8/1233C22C38/002C22C38/005C22C38/008C22C38/02C22C38/04C22C38/06C22C38/14C22C38/16C22C38/60
Inventor 储双杰张峰王志成张文岳王波李国保
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap