Inorganic fireproof building decoration material and process thereof

A technology for fireproof building and decoration materials, applied in the field of building decoration materials, can solve the problems of small scope of application, poor fireproof performance and support performance, etc.

Inactive Publication Date: 2021-04-13
陕西威斯特高新技术投资有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an inorganic fireproof building decoration material and its technology, which has the advantages of good fireproof performance, and solves the problem that traditional building decoration materials are generally wooden panels, which have poor fireproof performance and support performance. problems that lead to its narrow scope of application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic fireproof building decoration material and process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: An inorganic fireproof building decoration material, comprising a core layer 1 , a filling layer 2 and an inorganic fireproof layer 3 .

[0026] The core layer 1 includes the following raw materials: steel skeleton, silicon dioxide powder, gypsum powder, reinforcing fiber and water.

[0027] Filling layer 2 includes the following raw materials: foaming agent, cement, fly ash, stone powder and water.

[0028] The inorganic fireproof layer 3 includes the following raw materials in proportions by weight: 40-60 parts of quartzite, 20-30 parts of waste silica bricks, 12-20 parts of mineralizer, 8-12 parts of binder and 10-20 parts of admixture .

[0029] SiO2 is the main component in quartzite, Al2O3, Fe2O3, CaO, MgO, K2O, Na20 and TiO2 are all impurities, and the mass fraction of Al2O3 is less than 0.5% of the total mass fraction of quartzite.

[0030] The mineralizer is one or more combinations of rolled iron scale (iron scale), open hearth slag, sulfuric a...

Embodiment 2

[0037] Embodiment 2: An inorganic fireproof building decoration material, comprising a core layer 1 , a filling layer 2 and an inorganic fireproof layer 3 .

[0038] The core layer 1 includes the following raw materials: steel skeleton, silicon dioxide powder, gypsum powder, reinforcing fiber and water.

[0039] Filling layer 2 includes the following raw materials: foaming agent, cement, fly ash, stone powder and water.

[0040] The inorganic fireproof layer 3 includes the following raw materials in proportions by weight: 40-60 parts of quartzite, 20-30 parts of waste silica bricks, 12-20 parts of mineralizer, 8-12 parts of binder and 10-20 parts of admixture .

[0041] SiO2 is the main component in quartzite, Al2O3, Fe2O3, CaO, MgO, K2O, Na20 and TiO2 are all impurities, and the mass fraction of Al2O3 is less than 0.5% of the total mass fraction of quartzite.

[0042] The mineralizer is one or more combinations of rolled iron scale (iron scale), open hearth slag, sulfuric a...

Embodiment 3

[0049] Embodiment 3: An inorganic fireproof building decoration material, comprising a core layer 1 , a filling layer 2 and an inorganic fireproof layer 3 .

[0050] The core layer 1 includes the following raw materials: steel skeleton, silicon dioxide powder, gypsum powder, reinforcing fiber and water.

[0051] Filling layer 2 includes the following raw materials: foaming agent, cement, fly ash, stone powder and water.

[0052] The inorganic fireproof layer 3 includes the following raw materials in proportions by weight: 40-60 parts of quartzite, 20-30 parts of waste silica bricks, 12-20 parts of mineralizer, 8-12 parts of binder and 10-20 parts of admixture .

[0053] SiO2 is the main component in quartzite, Al2O3, Fe2O3, CaO, MgO, K2O, Na20 and TiO2 are all impurities, and the mass fraction of Al2O3 is less than 0.5% of the total mass fraction of quartzite.

[0054] The mineralizer is one or more combinations of rolled iron scale (iron scale), open hearth slag, sulfuric a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building decoration materials, and discloses an inorganic fireproof building decoration material which comprises a core layer, a filling layer and an inorganic fireproof layer. According to the inorganic fireproof building decoration material and the process thereof, the filling layer and the foamed concrete layer are formed by mixing the foaming agent, the cement, the fly ash, the stone powder and the water, so that the novel building energy-saving material which is light in weight, high in strength, non-absorbent and non-combustible is prepared by recycling waste. The building decoration material can be used for roof heat preservation and heat insulation, floor heating, ground cushion layer, inner partition wall and outer wall heat preservation and the like, so that the application range of the building decoration material is widened, finally, quartzite, waste silicon bricks, a mineralizing agent, a binding agent and an additive are mixed to form an inorganic fireproof layer, and waste recycling is adopted as well. The production cost of the building decoration material is further reduced, meanwhile, the blank firing shrinkage is reduced, the firing rejection rate of the building decoration material is reduced, and the effects of energy conservation, environmental protection and waste recycling are achieved.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to an inorganic fireproof building decoration material and its technology. Background technique [0002] Decorative materials (building decoration materials) are mainly used to decorate the inner and outer walls of buildings, make inner walls, and realize part of the use functions on the basis of decoration, decorate various civil buildings to improve their use functions and aesthetics, and protect the main structure in the building. Stable and durable building materials and their products under various environmental factors, also known as decoration materials and facing materials, mainly include grass, wood, stone, sand, brick, tile, cement, gypsum, reinforced fiber, lime, Glass, mosaic, soft porcelain, ceramics, paint, paper, ecological wood, metal, plastic, fabric, etc., as well as various composite products, are divided into 3 categories according to their ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/94E04C2/288E04C2/30E04F13/072E04F13/075C04B28/14C04B28/00C04B28/10C04B28/04C04B111/28
CPCC04B28/00C04B28/04C04B28/10C04B28/14C04B2111/00612C04B2111/28E04B1/942E04C2/288E04C2/30E04F13/0875E04F2290/046C04B14/06C04B20/0048C04B32/02C04B2103/0068C04B18/08C04B18/12C04B18/16C04B18/14C04B18/141C04B18/0481C04B2103/12C04B7/02C04B22/0006Y02A30/244
Inventor 杜亚宁
Owner 陕西威斯特高新技术投资有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap