Polypropylene resin for melt-blown fabric production and preparation method thereof

A polypropylene resin and melt-blown cloth technology is applied in the field of melt-blown cloth production materials, which can solve the problems of waste of resources, inability to realize the repeated use of masks, and no inhibition of bacteria and virus growth, and achieve good color fastness to rubbing. Effect

Inactive Publication Date: 2021-04-16
广西德福莱医疗器械有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a polypropylene resin for the production of melt-blown cloth and a preparation method thereof. The polypropylene resin prepared by the method not only has the effect of inhibiting the growth of bacteria and viruses, but also has the corresponding effect of producing melt-blown cloth. The effect of inhibiting the growth of bacteria and viruses, thus solving the problem that the existing masks made of melt-blown cloth cannot be used repeatedly because they have no effect of inhibiting the growth of bacteria and viruses, resulting in waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Adopt the raw material of following parts by weight:

[0023] 100 parts of polypropylene resin, 1 part of silver ion aqueous solution, 1 part of water-based aziridine, 5 parts of water-based polyurethane, 2 parts of compatibilizer, 0.5 part of weather resistance agent, and 0.1 part of antioxidant;

[0024] Wherein, the concentration of the silver ion aqueous solution is 0.2%, and the pH value is 8;

[0025] Described compatibilizer is polyethylene graft maleic anhydride;

[0026] The weather resistance agent is prepared by compounding hindered amine and hindered benzoic acid ester in a mass ratio of 1:1;

[0027] The antioxidant is prepared by compounding a hindered phenol antioxidant and a phosphite antioxidant in a mass ratio of 3:1;

[0028] Its preparation method comprises the following steps:

[0029] A. take each raw material by weight ratio;

[0030] B. Put each raw material into a mixer and stir and mix to obtain a mixed material;

[0031] C. Put the mixed ...

Embodiment 2

[0034] Adopt the raw material of following parts by weight:

[0035] 100 parts of polypropylene resin, 3 parts of silver ion aqueous solution, 3 parts of water-based aziridine, 9 parts of water-based polyurethane, 3 parts of compatibilizer, 0.7 part of weather resistance agent, and 0.8 part of antioxidant;

[0036] Wherein, the concentration of the silver ion aqueous solution is 0.25%, and the pH value is 9;

[0037] Described compatibilizer is polyethylene graft maleic anhydride;

[0038] The weather resistance agent is prepared by compounding hindered amine and hindered benzoic acid ester in a mass ratio of 1:1;

[0039] The antioxidant is prepared by compounding a hindered phenol antioxidant and a phosphite antioxidant in a mass ratio of 3:1;

[0040] Its preparation method comprises the following steps:

[0041] A. take each raw material by weight ratio;

[0042] B. Put each raw material into a mixer and stir and mix to obtain a mixed material;

[0043] C. Put the mix...

Embodiment 3

[0046] Adopt the raw material of following parts by weight:

[0047] 100 parts of polypropylene resin, 5 parts of silver ion aqueous solution, 5 parts of water-based aziridine, 10 parts of water-based polyurethane, 4 parts of compatibilizer, 1 part of weather resistance agent, and 0.5 parts of antioxidant;

[0048] Wherein, the concentration of the silver ion aqueous solution is 3%, and the pH value is 10;

[0049] Described compatibilizer is polyethylene graft maleic anhydride;

[0050] The weather resistance agent is prepared by compounding hindered amine and hindered benzoic acid ester in a mass ratio of 1:1;

[0051] The antioxidant is prepared by compounding a hindered phenol antioxidant and a phosphite antioxidant in a mass ratio of 3:1;

[0052] Its preparation method comprises the following steps:

[0053] A. take each raw material by weight ratio;

[0054] B. Put each raw material into a mixer and stir and mix to obtain a mixed material;

[0055] C. Put the mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polypropylene resin for melt-blown fabric production and a preparation method thereof, and relates to the technical field of materials for melt-blown fabric production. The polypropylene resin is prepared from the following raw materials: polypropylene resin, a silver ion aqueous solution, waterborne aziridine, waterborne polyurethane, a compatilizer, a weather-proof agent and an antioxidant. The preparation method comprises the following steps: stirring and mixing raw materials in a stirrer to obtain a mixed material; putting the mixed material into a double-screw extruder for plasticizing extrusion, cooling to obtain a hardened material, granulating, sieving, cooling and drying. The melt-blown fabric has the effect of inhibiting the growth of bacteria and viruses, and solves the problem that the mask and other products made of the existing melt-blown fabric cannot be repeatedly used due to no effect of inhibiting the growth of bacteria and viruses, and therefore the resource waste is caused.

Description

technical field [0001] The invention relates to the technical field of materials for the production of melt-blown cloth, in particular to a production process of polypropylene resin for the production of melt-blown cloth. Background technique [0002] Meltblown cloth is the core material for mask production, and polypropylene is the main raw material for production. Because of its large voids, fluffy structure, and good wrinkle resistance, the ultrafine fibers with a unique capillary structure increase the number and surface area of ​​fibers per unit area, so that the melt blown cloth has good filterability, shielding, heat insulation and oil absorption. It is widely used in air and liquid filter materials, isolation materials, absorbent materials, medical and industrial mask materials, thermal insulation materials, oil-absorbing materials and wiping cloths. [0003] However, although the existing melt-blown cloth plays an irreplaceable role with its excellent filtration pe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L75/04C08L51/06C08K5/3412
Inventor 蓝国勇阮健
Owner 广西德福莱医疗器械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com