Preparation method of anti-reflection PET film for liquid crystal writing board

A technology for writing boards and films, which is applied in the field of preparation of anti-reflection PET films for liquid crystal writing boards. It can solve the problems of shortening the service life of PET films, poor light transmission effect of PET films, and affecting the quality of liquid crystal writing boards, so as to improve the writing feel. , to achieve anti-slip effect, to achieve the effect of wear-resistant effect

Inactive Publication Date: 2021-04-20
TIANJIN BAOXINGWEI TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PET film is an essential part of liquid crystal writing board. The quality of PET film directly affects the quality of liquid crystal writing board. The existing PET film has low surface hardness and is easy to be scratched and worn, which shortens the service life of PET film.
In addition, the existing PET film has poor light transmission effect, which affects people's use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] A kind of preparation method of anti-reflection PET film for liquid crystal writing board, it is characterized in that, comprises steps as follows:

[0019] a. Configure anti-reflection coating solution: carry out emulsion polymerization of methyl methacrylate, styrene and cadmium acrylate to obtain random copolymer latex particles of methyl methacrylate, styrene and acrylic acid;

[0020] b. Coating anti-reflection coating solution: dilute the random copolymer latex particles obtained in step a, and spin-coat on the surface of PET film, dry to obtain anti-reflection PET film;

[0021] c. Configure anti-slip and wear-resistant coating liquid: mix 97% acrylic monomer, 2% ultraviolet absorber, and 1% ultraviolet trigger curing agent according to the weight ratio to obtain the coating liquid;

[0022] d. Coating anti-slip and wear-resistant coating solution: apply the coating solution evenly on the upper surface of the anti-reflection PET film to obtain a coating layer;

...

Embodiment 1

[0031] A kind of preparation method of anti-reflection PET film for liquid crystal writing board, it is characterized in that, comprises steps as follows:

[0032] a. Configure anti-reflection coating solution: carry out emulsion polymerization of methyl methacrylate, styrene and cadmium acrylate to obtain random copolymer latex particles of methyl methacrylate, styrene and acrylic acid;

[0033] b. Coating anti-reflection coating solution: dilute the random copolymer latex particles obtained in step a, and spin-coat on the surface of PET film, dry to obtain anti-reflection PET film;

[0034] c. Configure anti-slip and wear-resistant coating liquid: mix 97% acrylic monomer, 2% ultraviolet absorber, and 1% ultraviolet trigger curing agent according to the weight ratio to obtain the coating liquid;

[0035] d. Coating anti-slip and wear-resistant coating solution: apply the coating solution evenly on the upper surface of the anti-reflection PET film to obtain a coating layer;

...

Embodiment 2

[0044] A kind of preparation method of anti-reflection PET film for liquid crystal writing board, it is characterized in that, comprises steps as follows:

[0045] a. Configure anti-reflection coating solution: carry out emulsion polymerization of methyl methacrylate, styrene and cadmium acrylate to obtain random copolymer latex particles of methyl methacrylate, styrene and acrylic acid;

[0046] b. Coating anti-reflection coating solution: dilute the random copolymer latex particles obtained in step a, and spin-coat on the surface of PET film, dry to obtain anti-reflection PET film;

[0047] c. Configure anti-slip and wear-resistant coating liquid: mix 97% acrylic monomer, 2% ultraviolet absorber, and 1% ultraviolet trigger curing agent according to the weight ratio to obtain the coating liquid;

[0048] d. Coating anti-slip and wear-resistant coating solution: apply the coating solution evenly on the upper surface of the anti-reflection PET film to obtain a coating layer;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an anti-reflection PET film for a liquid crystal writing board. The preparation method comprises the following steps: a, preparing an anti-reflection coating solution; b, coating an anti-reflection coating solution; c, preparing antiskid wear-resistant coating liquid; d, coating anti-skid wear-resistant coating liquid; e, pressing anti-dazzle textures; and f photocuring. The coating layer is a polymer layer mainly composed of acrylic monomers, so that the PET film has high hardness and can be prevented from being scratched, and the service life is prolonged; and the anti-dazzle textures can avoid light reflection, the anti-skid effect and the wear-resisting effect can be achieved, and the writing hand feeling is improved. Besides, the random copolymer latex particles are uniformly distributed on the PET film, micropores among the particles can be generated due to the arrangement of the latex particles, the refractive index of the surface of the PET film is reduced, and the light transmittance of the PET film is improved.

Description

technical field [0001] The invention relates to the technical field of liquid crystal writing board production, in particular to a method for preparing an anti-reflection PET film for liquid crystal writing boards. Background technique [0002] Liquid crystal electronic writing board is an electronic device that adopts high-tech flexible liquid crystal technology, relies on pressure sensing to display text, patterns and graphics, and can complete writing with a single stroke and a light touch. PET film is an essential part of the liquid crystal writing board. The quality of the PET film directly affects the quality of the liquid crystal writing board. The existing PET film has a low surface hardness and is easy to be scratched and worn, thereby shortening the service life of the PET film. In addition, the existing PET film has poor light transmission effect, which affects people's use. Contents of the invention [0003] The invention aims to solve the deficiencies of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C08J7/046C09D133/12C09D4/02C08F212/08C08F220/06C08F220/14G02B1/111G02B1/118C08L67/02
Inventor 司荣美潘中海鲍彦广
Owner TIANJIN BAOXINGWEI TECH
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com