Lightweight gypsum mortar and preparation method thereof

A gypsum mortar and lightweight technology, applied in the field of building materials, can solve the problems of light gypsum mortar, such as dirty and unsafe working environment, low degree of automation of additive equipment, and high labor intensity of workers, so as to achieve production environment and batching precision and workers The effect of increasing labor intensity and labor utilization rate, reducing production cost and improving production efficiency

Inactive Publication Date: 2021-05-07
青岛三山伟业机械设备有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art, provide a kind of light gypsum mortar and its preparation method, in order to solve the problem that the current working environment for light gypsum mortar is dirty and unsafe, the degree of pollution is large, and the degree of automation of additive equipment is low. , the labor intensity of workers is high, and the problem of high equipment cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A light gypsum mortar is prepared from the following raw materials in parts by weight: 600 parts of desulfurized gypsum powder, 200 parts of heavy calcium, 50 parts of vitrified microbeads, and 10 parts of additives.

[0027] Preferably, in parts by weight, the additives include 3 parts of hydroxypropyl methylcellulose, 2 parts of thixotropic agent, 3 parts of starch ether, 0.5 parts of redispersible latex powder, and 10 parts of cement.

[0028] Preferably, the bulk density of the vitrified microbeads is 60 kg / m3, and the bulk density of the desulfurized gypsum powder is 700 kg / m3.

[0029] Preferably, the lightweight gypsum mortar also includes 0.2 part of water reducer and 0.01 part of defoamer.

Embodiment 2

[0031] A lightweight gypsum mortar is made of the following raw materials in parts by weight: 700 parts of desulfurized gypsum powder, 300 parts of heavy calcium, 75 parts of vitrified microbeads, and 15 parts of additives.

[0032] Preferably, in parts by weight, the additives include 6 parts of hydroxypropyl methylcellulose, 4 parts of thixotropic agent, 4 parts of starch ether, 1 part of redispersible latex powder, and 16 parts of cement.

[0033] Preferably, the bulk density of the vitrified microbeads is 90 kg / m3, and the bulk density of the desulfurized gypsum powder is 750 kg / m3.

[0034] Preferably, the lightweight gypsum mortar also includes 0.6 part of water reducer and 0.05 part of defoamer.

Embodiment 3

[0036] A lightweight gypsum mortar is made of the following raw materials in parts by weight: 800 parts of desulfurized gypsum powder, 400 parts of heavy calcium, 100 parts of vitrified microbeads, and 20 parts of additives.

[0037] Preferably, in parts by weight, the additives include 8 parts of hydroxypropyl methylcellulose, 6 parts of thixotropic agent, 5 parts of starch ether, 2 parts of redispersible latex powder, and 20 parts of cement.

[0038] Preferably, the bulk density of the vitrified microbeads is 120 kg / m3, and the bulk density of the desulfurized gypsum powder is 800 kg / m3.

[0039] Preferably, the lightweight gypsum mortar also includes 1 part of water reducer and 0.1 part of defoamer.

[0040] Based on the preparation method of above-mentioned lightweight gypsum mortar, may further comprise the steps:

[0041] Step 1: The raw materials desulfurized gypsum powder and heavy calcium are lifted into the raw material bin by the raw material hoist, and the materia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses lightweight gypsum mortar. The light gypsum mortar is prepared from the following raw materials in parts by weight: 600-800 parts of desulfurized gypsum powder, 200-400 parts of heavy calcium carbonate, 50-100 parts of glass beads and 10-20 parts of an additive. The additive comprise the following components in parts by weight: 3-8 parts of hydroxypropyl methyl cellulose, 2-6 parts of a thixotropic agent, 3-5 parts of starch ether, 0.5-2 parts of redispersible latex powder and 10-20 parts of cement. The lightweight gypsum mortar has the advantages of greatly improving a production environment, batching precision, the labor intensity of workers and a labor utilization rate, fully utilizing the working time of the workers and improving production efficiency.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a lightweight gypsum mortar and a preparation method thereof. Background technique [0002] Gypsum is a gel material with a long history. It is listed as the three pillars of meta-mechanical cementitious materials together with lime and cement. The use of gypsum materials is of great significance for saving building material resources and improving the technical level of building materials. It usually has the characteristics of light weight, sound insulation, fire resistance, heat insulation, etc., and gypsum is rich in resources, so gypsum is widely used in the field of building materials. [0003] Mortar is a bonding substance used in building bricks. It is composed of a certain proportion of sand and cementing materials (cement, gypsum, clay, etc.) and water. It is also called mortar and mortar. Mortars generally include cement mortar, mixed mortar (cement-lime mo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/08C04B28/14C04B111/40
CPCC04B28/144C04B2111/40
Inventor 李胜伟
Owner 青岛三山伟业机械设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com