Two-component pad printing silicone rubber and preparation method thereof
A two-component, silicone technology, applied in the field of pad printing silicone rubber, can solve the problems of short service life, increased use cost, short service life of pad printing silicone rubber, etc., achieves long service life, strong resistance to permanent deformation, improved performance effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment approach
[0096] According to a second embodiment of the present invention, there is provided a method for preparing a two-component pad printing silica gel or a method for preparing a two-component pad printing silica gel as described in the first embodiment, the method comprising the following steps:
[0097] 1) Preparation of component A: Mix polyvinyl siloxane, coupling agent, fumed silica, and ultra-short glass fiber in proportion. Then heat up and knead, add platinum catalyst after cooling. Finally, component A is obtained after grinding and filtering.
[0098] 2) Preparation of component B: Mix polyvinyl siloxane, MQ silicone resin, hydrogen-containing siloxane, and inhibitor in proportion, and filter to obtain component B.
[0099] 3) Preparation of two-component pad printing silica gel: Mix components A and B in proportion and react to obtain a two-component pad printing silica gel.
[0100] Wherein, the polyvinyl siloxane is one of the polyvinyl siloxanes having at least 2 t...
Embodiment 1
[0128] The specific surface area of 100g is 300m 2 / g of fumed silica, 13g of hexamethyldisilazane, and 2g of water were added to a reaction kettle filled with nitrogen, and reacted at 180°C for 2h. Then cool to room temperature and vacuumize for 2 hours to remove unreacted substances and small molecular substances, then heat to 120°C and dry for 1 hour to obtain hydrophobically modified fumed silica I.
Embodiment 2
[0130] The specific surface area of 100g is 300m 2 / g of fumed silica, 13g of hexamethyldisilazane, 3g of aluminate coupling agent, and 2g of water were added to a reaction kettle filled with nitrogen, and reacted at 180°C for 2h. Then cool to room temperature and vacuumize for 2 hours to remove unreacted substances and small molecular substances, then heat to 120°C and dry for 1 hour to obtain hydrophobically modified fumed silica II.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com