A kind of thermal insulation and sound insulation glass microfiber wool for low frequency noise and preparation method thereof

A technology of glass microfiber cotton and glass microfiber, which is applied in the field of glass microfiber composite materials, can solve the problems of fiber pore structure construction and uneven bonding system, and achieve the effect of improving sound insulation and heat insulation performance, and improving mechanical properties

Active Publication Date: 2022-07-29
CHONGQING UNIV OF ARTS & SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a thermal insulation and sound-insulating glass microfiber wool for low-frequency noise and its preparation method in order to improve the deficiencies of the prior art, so as to solve the fiber pore structure of the glass fiber wool prepared by the prior art for low-frequency noise. The problem of uneven build and bonding system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermal insulation and sound insulation glass microfiber wool for low frequency noise and preparation method thereof
  • A kind of thermal insulation and sound insulation glass microfiber wool for low frequency noise and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0031] Embodiment 1-3 is implemented according to the following steps:

Embodiment 1

[0033] The inflow temperature of the glass liquid is 1015°C and the hole diameter is 17mm. # The molten glass stream formed by the alloy bushing flows into a temperature of 995 ℃, the number of holes is 17500, and the rotation speed is 3700rpm. # Centrifugal disc, and relying on the centrifugal force of high-speed rotating centrifugal disc and the action of high-pressure extension wind, it is drawn into glass microfibers with a beating degree of SR°21 at high speed. At the same time, the same molten glass flows into 2 with a temperature of 1005°C and a pore size of 16mm. # The molten glass stream formed by the alloy bushing flows into 2 with a temperature of 985°C, a number of holes of 14500, and a rotation speed of 3400rpm. # The centrifugal disc is pulled into glass microfibers with a beating degree of SR°17 at high speed under the action of the centrifugal force of the high-speed rotating centrifugal disc in the centrifuge and the high-pressure extension wind. At the same...

Embodiment 2

[0035] The liquid glass flows into a 1020°C glass with a hole diameter of 18mm. # The molten glass stream formed by the alloy bushing flows into a temperature of 1000 ° C, the number of holes is 18000, and the rotation speed is 3800rpm. # Centrifugal disc, and relying on the centrifugal force of high-speed rotating centrifugal disc and the action of high-pressure extension wind, it is drawn into glass microfibers with a beating degree of SR°21 at high speed. At the same time, the same liquid glass flows into 2 with a temperature of 1010 °C and a hole diameter of 15 mm. # The molten glass stream formed by the alloy bushing flows into 2 with a temperature of 990°C, a number of holes of 15,000, and a rotational speed of 3,500 rpm. # The centrifugal disc is pulled into glass microfibers with a beating degree of SR°17 at high speed under the action of the centrifugal force of the high-speed rotating centrifugal disc in the centrifuge and the high-pressure extension wind. At the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
porosityaaaaaaaaaa
porosityaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-insulating and sound-insulating glass microfiber wool for low-frequency noise and a preparation method thereof. The heat-insulating and sound-insulating glass microfiber wool for low-frequency noise comprises, in mass percentage, 85-95 wt% of ultra-fine glass fiber wool, The modified single-component water-based resin is 5-12wt%, the coupling agent is 1-3wt% and the water-based color paste is 0.5-1wt%. The superfine glass fiber wool is composed of glass microfibers with three degrees of beating. Mixed solution B formed by uniformly mixing one-component water-based resin and coupling agent, mixed solution A formed by uniformly mixing type A modified single-component water-based resin and water-based color paste, and mixed solution B and mixed solution A were divided into two parts The surface is coated with glass microfibers in one step and formed into glass microfiber wool. The thermal insulation and sound insulation glass microfiber cotton prepared by the invention has good softness, strong hydrophobicity, high mechanical strength and excellent thermal insulation and sound insulation performance against low-frequency noise.

Description

technical field [0001] The invention relates to a heat-insulating and sound-insulating glass microfiber wool for low-frequency noise and a preparation method thereof, belonging to the technical field of glass microfiber composite materials. Background technique [0002] The ultra-fine glass fiber cotton produced by centrifugal blowing method has porous, low bulk density, fluffy and soft, interwoven inner fibers and excellent heat insulation and sound absorption properties, and can be used in construction, home appliances, transportation and other industrial fields. When ultra-fine glass fiber wool is used in the field of sound absorption and heat insulation, the degree of fiber thickness has a very significant effect on its heat insulation and sound insulation performance. Generally, when the fiber diameter is thinner, the more semi-connected pores formed in the ultra-fine glass fiber wool, the lower the thermal conductivity and the higher the sound insulation decibel. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B37/04C03C6/04C03C6/02C04B26/32C04B26/16C04B38/00C04B111/52
CPCC03B37/04C03C1/00C03C1/002C04B26/32C04B26/16C04B2111/52C04B2201/32C04B24/302C04B24/282C04B14/42C04B2103/54C04B2103/0068C04B38/0054C04B38/0074
Inventor 翟福强陈威邱鑫胡惠钧王杰杜源李杰陈西浩李璐罗永以
Owner CHONGQING UNIV OF ARTS & SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com