Sand-in-sand multicolor paint and preparation method thereof

A technology of colorful coatings and sand molds, applied in the field of coatings, can solve the problems of blurred overall effects, differences in imitation stone effects, increased consumption, etc., and achieve the effects of increasing stone imitation effects, easy mixing and even enhancement of thixotropic performance

Active Publication Date: 2021-07-16
福建省三棵树新材料有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-in-sand multi-color paint can better imitate the color spots of various colors. The effect after spraying is uneven, which is closer to the surface effect of stone, but its spraying requires workers with rich experience, and the spraying air pressure must be strictly controlled during spraying. , if the air pressure is too small, the colored dots will not

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sand-in-sand multicolor paint and preparation method thereof
  • Sand-in-sand multicolor paint and preparation method thereof
  • Sand-in-sand multicolor paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] The protective glue is prepared by the following method: add deionized water to container 1, then add protective powder and crosslinking agent at a stirring speed of 1300rpm, and stir for 30 minutes to obtain it;

[0061] Described toning base material is prepared by following method:

[0062] Add deionized water into container two;

[0063] Then, at a stirring rate of 300rpm, add the antifungal agent and dispersant and stir for 1min;

[0064] Then at a stirring rate of 600rpm, add cellulose and stir for 5min;

[0065] Then at a stirring rate of 700rpm, add fillers, toughening agents, polyvinyl alcohol, defoamers and pH regulators, then adjust the rotating speed to 1200rpm and stir for 15min;

[0066] Then at a stirring rate of 1000rpm, add emulsion, film-forming aid, antifreeze, bactericide and colorful wetting agent and stir for 5min;

[0067] Then, at a stirring rate of 1100rpm, add the protective colloid solution and stir for 8min;

[0068] Finally, at a stirrin...

Embodiment 2

[0077] The protective glue is prepared by the following method: add deionized water into container 1, then add protective powder and cross-linking agent at a stirring rate of 1500 rpm, and stir for 40 minutes to obtain it;

[0078] Described toning base material is prepared by following method:

[0079] Add deionized water into container two;

[0080] Then at a stirring rate of 500rpm, add the antifungal agent and dispersant and stir for 2min;

[0081] Then at a stirring rate of 800rpm, add cellulose and stir for 10min;

[0082] Then at a stirring rate of 900rpm, add fillers, toughening agents, polyvinyl alcohol, defoamers and pH regulators, then adjust the rotating speed to 1500rpm and stir for 25min;

[0083] Then at a stirring rate of 1200rpm, add emulsion, film-forming aid, antifreeze, bactericide and colorful wetting agent and stir for 10min;

[0084] Then, at a stirring rate of 1300rpm, add the protective colloid solution and stir for 10min;

[0085] Finally, at a st...

Embodiment 3

[0094] The protective glue is prepared by the following method: add deionized water into container 1, then add protective powder and crosslinking agent at a stirring rate of 1400rpm, and stir for 35 minutes to obtain it;

[0095] Described toning base material is prepared by following method:

[0096] Add deionized water into container two;

[0097] Then at a stirring rate of 400rpm, add the antifungal agent and dispersant and stir for 1.5min;

[0098] Then at a stirring rate of 700rpm, add cellulose and stir for 6min;

[0099] Then at a stirring rate of 800rpm, add fillers, toughening agents, polyvinyl alcohol, defoamers and pH regulators, then adjust the rotating speed to 1400rpm and stir for 20min;

[0100] Then at a stirring rate of 1100rpm, add emulsion, film-forming aid, antifreeze, bactericide and colorful wetting agent and stir for 8min;

[0101] Then, at a stirring rate of 1200rpm, add the protective colloid solution and stir for 9min;

[0102] Finally, at a stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a sand-in-sand type multicolor coating which is mainly prepared from protective glue, a color matching base material, a continuous phase, a pH regulator and a thickening agent, wherein the mass ratio of the protective glue to the color matching base material to the continuous phase is 10:(20-30):(60-70); the pH regulator accounts for 0.1% of the total mass of the protective glue, the toning base material and the continuous phase; and the thickening agent accounts for 0.3-0.5% of the total mass of the protective glue, the toning base material and the continuous phase. The color points prepared by the preparation method are high in toughness and strength, so that the color points are not greatly deformed during spraying due to mutual extrusion of muzzles, the sensitivity to spraying air pressure is reduced, and the color points can be directly sprayed under high air pressure; therefore, the spraying efficiency is improved, and moreover, the colored stone is not easy to break, the whole colored stone is clear, and the stone imitation effect is good.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a sand-in-sand type colorful coating and a preparation method thereof. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. The buildings decorated with real stone paint have natural and real natural color, which gives people elegant, harmonious and solemn aesthetic feeling. It is suitable for indoor and outdoor decoration of all kinds of buildings. Especially when it is decorated on curved buildings, it is vivid and lifelike, and has an effect of returning to nature. However, the color difference of its core raw material natural colored sand is serious, which affects the visual sensory effect of real stone paint, and real stone paint nee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/29C09D7/61C09D7/63C09D7/43C09D7/65
CPCC09D133/04C09D143/04C09D5/29C09D7/61C09D7/63C09D7/43C09D7/65C08L2312/00C08L2205/035C08L2205/025C08L43/04C08L1/284C08L5/00C08K5/3412C08K3/38C08K3/346C08K3/36
Inventor 杨帆
Owner 福建省三棵树新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap