Tool for preparing composite material test sample piece and preparation method of test sample piece

A technology of composite materials and composite material boards, applied in the field of non-metallic material manufacturing, can solve problems such as poor sample consistency, test failure, and debonding of reinforcement sheets

Active Publication Date: 2021-07-30
NO 20 RES INST OF CHINA ELECTRONICS TECH GRP
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies of the prior art, the present invention provides a tooling for preparing composite material test samples and a method for preparing test samples, which can effectively solve the test problems caused by the debonding and abnormal damage of the reinforcin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tool for preparing composite material test sample piece and preparation method of test sample piece
  • Tool for preparing composite material test sample piece and preparation method of test sample piece
  • Tool for preparing composite material test sample piece and preparation method of test sample piece

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.

[0035] The present invention will be further described in conjunction with examples and accompanying drawings. The example is the preparation of a tensile sample of a carbon fiber composite material plate (11), and this example is only a part of the present invention.

[0036] The invention proposes a tooling and processing method for assisting the preparation of composite material test samples. The special tooling is used to fix the sample blank of the three-layer composite structure composed of a reinforcement plate, a limit plate and a composite material plate to be tested, and assist in the preparation of the sample blank. Composite material mechanical performance test sample with reinforcement sheet, which is characterized in that the limit plate, reinforcement plate and composite material board to be tested are fixed on the special tooling first, so ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Outer diameteraaaaaaaaaa
Login to view more

Abstract

According to the tool for preparing the composite material test sample piece and the preparation method of the test sample piece, the special tool is designed to fix a three-interlayer composite structure sample material blank composed of a reinforcing plate, a limiting plate and a to-be-tested composite material plate, and it is ensured that the reinforcing plate and the to-be-tested composite material plate do not have relative displacement in the cementing and curing process; the bonding reliability is improved by adopting a high-temperature-resistant epoxy glue bonding and curing method, and then test samples with corresponding sizes are obtained by machining and cutting according to size requirements. The tool is adopted to assist high-temperature-resistant epoxy glue to perform in-situ cementing of the reinforcing plate/to-be-tested composite plate, then the composite material test sample piece is prepared by a machining method, it is ensured that no relative displacement exists in the resin glue curing process, the batch consistency of the sample piece is improved, the reinforcing plate is reliably cemented, The tool can effectively solve the problem of test failure caused by debonding and abnormal damage of the reinforcing sheet when a sample prepared by a conventional method is tested under harsh environmental conditions such as high temperature and damp heat, and meanwhile, the preparation efficiency of the sample is greatly improved.

Description

technical field [0001] The invention relates to the technical field of non-metallic material manufacturing, in particular to a tooling and method for preparing mechanical performance test samples. Background technique [0002] Composite materials have the characteristics of high specific strength, high specific modulus, and anisotropy, and have been widely used as structural parts in aerospace, electronic equipment manufacturing and other fields. Mechanical properties are the basic characteristics of composite materials, and also the basis for evaluating whether they can be used in actual equipment. In order to evaluate composite materials in engineering applications, it is often necessary to combine the equipment working environment, prepare test samples according to corresponding standards, and conduct sample test comparison and analysis and evaluation of their mechanical properties under specific temperature and humidity conditions. In order to accurately test the mechan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N1/28
CPCG01N1/28
Inventor 孙坤刘明昌张晨晖高琦李建伟章文捷
Owner NO 20 RES INST OF CHINA ELECTRONICS TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka