Production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board

A production method and a floor heating technology are applied in the production field of surface compression enhanced ultra-stable solid wood floor heating floor boards, so as to achieve the effect of reducing processing costs and reducing processing procedures.

Active Publication Date: 2022-03-18
JIUSHENG WOOD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For enterprises without deducted floor patents, they also need to bear the cost of using the deducted patents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board
  • Production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board
  • Production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: The production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board, choose density 0.4g / cm 3 The floor board or base material has a moisture content of less than 15%; the thickness is selected to be 30mm, the surface of the floor board or base material is flat, and the total amount of water added to the surface of the floor board or base material by spraying, dipping or immersing in water reaches 0.1g / cm 2 Then put it into the hot pressing plate at 150°C, close the hot pressing plate quickly in no more than 1 minute, the pressure in the closed state is less than 1MPa, then heat it at 150°C for 50 seconds, and then press the Compress wood to a predetermined thickness of 20mm, surface density 0.85g / cm 3 , and then keep it for 5 minutes, reduce the pressure of the hot press plate to 1MPa, and take out the wood after the temperature drops below 60°C to complete a stabilization treatment.

[0022] Palletize the compr...

Embodiment 2

[0025] Embodiment 2: the production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board, choose density 0.4g / cm 3The floor board or base material has a moisture content of 10%; the thickness is selected at 30mm, the surface of the floor board or base material is flat, and the total amount of water added to the surface of the floor board or base material by spraying, dipping or immersing in water reaches 0.03g / cm 2 Then put it into a hot press plate at 160°C, close the hot press plate quickly in no more than 1 minute, the pressure in the closed state is less than 1MPa, and then heat it at 160°C for 40 seconds, and then press it with a pressure of 5MPa Compress wood to a predetermined thickness of 20mm, surface density 0.95g / cm 3 , and then keep it for 5 minutes, reduce the pressure of the hot press plate to 1MPa, and take out the wood after the temperature drops below 60°C to complete a stabilization treatment.

[0026] Palletize the...

Embodiment 3

[0029] Embodiment 3: the production method of surface layer compression enhanced ultra-stable solid wood floor heating floor board, choose density 0.4g / cm 3 The floor board or base material has a moisture content of 10%; the thickness is selected at 30mm, the surface of the floor board or base material is flat, and the floor board or base material is sprayed with water, dipped in water or soaked in water to increase the amount of water on the surface to 0.05g / cm 2 Then put it into a hot press plate at 145°C, close the hot press plate quickly in no more than 1 minute, the pressure in the closed state is less than 1MPa, and then heat it at 145°C for 40 seconds, and then press it with a pressure of 5MPa Compress wood to a predetermined thickness of 20mm, surface density 0.90g / cm 3 , and then keep it for 4 minutes, reduce the pressure of the hot press plate to 1MPa, and take out the wood after the temperature drops below 60°C to complete a stabilization treatment.

[0030] Pall...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of super-stable solid wood floor heating floor panels with surface layer compression enhancement. While the surface layer of the floor panel or base material is compressed and enhanced, the wood is subjected to a stability treatment by controlling the temperature of a hot pressing plate to obtain compressed reinforced wood. , and then put the compressed reinforced wood into a heat treatment tank, and perform secondary stability treatment on the compressed reinforced wood by controlling the steam or air pressure, temperature and treatment time in the heat treated tank to obtain a finished product. The invention can greatly improve the dimensional stability of the surface compressed solid wood floor, and has the characteristics of low water absorption rebound rate and good moisture and heat resistance.

Description

technical field [0001] The invention relates to the technical field of floor production, in particular to a production method of super-stable solid wood floor heating floor plates with surface layer compression enhancement. Background technique [0002] The wood used for solid wood floor processing has relatively high requirements on the hardness of the wood. It is necessary to ensure that the finished solid wood flooring meets the requirements of the first-class solid wood flooring in the national standard. The hardness of the paint film is greater than H, or the hardness of the paint film required by the first-class flooring is greater than 2H. The density of the solid wood flooring substrate must reach 0.60g / cm respectively. 3 and 0.65cm 3 above. Although the average density of various substrates for processing solid wood flooring on the market is 0.60-0.70g / cm 3 However, due to the large variability of wood, the difference in density can reach 0.20g / cm2 due to the dif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27M3/04B27M1/08B27N3/08B27D1/08B27K5/00
CPCB27M3/04B27M1/08B27N3/08B27D1/083B27K5/0085B27K2200/30Y02B30/00B27M1/02B27N3/203E04F15/04B27K5/001B27K5/007B27K1/00
Inventor 黄荣凤王艳伟张恩玖张凯钱新民孔繁旭何啸宇孙龙祥
Owner JIUSHENG WOOD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com