PTFE composite fabric

A technology of composite fabrics and fabrics, applied in the field of fabrics, can solve the problems of corrosion resistance, high oxidation resistance, low temperature and wear resistance, shorten the service life of fabrics, and can not be solved, so as to achieve high visibility and strengthen airtightness Sexuality, anti-mold effect

Pending Publication Date: 2021-08-20
四川豪尔泰服饰有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, traditional outdoor fabrics cannot meet the requirements
[0003] At present, there are still some deficiencies in the existing fabrics, for example, the airtightness and watertightness of the existing fabrics are relatively poor during use, and the water vapor inside the structure cannot be discharged quickly, and molds are easy to breed inside the fabric structure, which cannot be solved. Ventilation and windproof, waterproof, heat preservation and other issues, and the corrosion resistance, oxidation resistance, high and low temperature resistance and wear resistance of the existing fabrics during use are relatively poor, which shortens the service life of the fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PTFE composite fabric
  • PTFE composite fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The processing steps of the novel fabric with flame-retardant function are as follows:

[0039] a. First put flame-retardant polyester fiber, flame-retardant acrylic fiber, natural bamboo fiber, cotton fiber, nylon fiber and spandex fiber into the textile machine to weave a combined thread, and then high-grade FDY filament, combed pure cotton sand thread and The combined thread is placed in the textile machine and blended into the outer fabric;

[0040] b. After step a is completed, put the cotton fiber, nylon fiber and spandex fiber into the textile machine to weave into a thread body, then cross the thread body to form a fabric base layer, and then weave the PTFE membrane on the front of the fabric base layer The opposite sides are made into a composite layer;

[0041] c. After step b is completed, put the flame-retardant polyester fiber, flame-retardant acrylic fiber, nylon fiber and spandex fiber into the textile machine to weave into a thread body, and then mix hi...

Embodiment 2

[0047] The processing steps of the novel fabric with flame-retardant function are as follows:

[0048] a. First put flame-retardant polyester fiber, flame-retardant acrylic fiber, natural bamboo fiber, cotton fiber, nylon fiber and spandex fiber into the textile machine to weave a combined thread, and then high-grade FDY filament, combed pure cotton sand thread and The combined thread is placed in the textile machine and blended into the outer fabric;

[0049] b. After step a is completed, put the cotton fiber, nylon fiber and spandex fiber into the textile machine to weave into a thread body, then cross the thread body to form a fabric base layer, and then weave the PTFE membrane on the front of the fabric base layer The opposite sides are made into a composite layer;

[0050] c. After step b is completed, put the flame-retardant polyester fiber, flame-retardant acrylic fiber, nylon fiber and spandex fiber into the textile machine to weave into a thread body, and then mix high...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a PTFE composite fabric. The PTFE composite fabric comprises a fabric body, the fabric body comprises an outer layer, a composite layer and an inner layer, the outer layer is bonded on the outer surface of the composite layer, and the inner layer is bonded on the inner surface of the composite layer. According to the novel fabric, the air tightness and the water tightness of the fabric are enhanced, meanwhile, due to the unique air permeability, water vapor in the structure can be rapidly discharged, mold breeding of the structure is avoided, the human body is kept dry all the time, and the problems of air permeability, wind resistance, water resistance, heat preservation and the like are perfectly solved.

Description

technical field [0001] The invention relates to the technical field of fabrics, in particular to a PTFE composite fabric. Background technique [0002] An integrated textile, printing and dyeing, and garment enterprise specializing in the production of tooling. At present, its products sell well both at home and abroad, especially in the European market. The function of tooling must be to effectively protect the body and safety of workers. Customer groups have very high requirements for outdoor work clothing, and traditional similar fabrics cannot meet actual needs. The main reason is that the wearing of work clothes is different from fashion. Work clothes are basically worn every day, and they are washed and used repeatedly. Moreover, the user wears clothes to work in a high-intensity environment, and the clothes must have many times of bending and wear. Therefore, traditional outdoor fabrics cannot meet the requirements. [0003] At present, there are still some deficie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/32
CPCA41D31/02A41D31/04A41D31/06A41D31/08A41D31/102A41D31/12B32B5/08B32B7/12B32B27/12B32B27/322B32B37/06B32B37/10B32B37/12B32B2262/02B32B2262/0261B32B2262/0284B32B2262/0292B32B2262/062B32B2262/065B32B2262/14B32B2307/304B32B2307/554B32B2307/714B32B2307/7145B32B2307/724B32B2307/7265B32B2437/00
Inventor 林武周何伟李小海
Owner 四川豪尔泰服饰有限公司