Polycarbonate diol and preparation method thereof

A polycarbonate dicarbonate technology, applied in the direction of products, educts, reagents, etc., can solve the problems of few fields, difficult to accurately control the molecular weight of polycarbonate diols, and low sales volume, so as to reduce waste and broaden applications , the effect of increasing the molecular weight

Active Publication Date: 2022-07-05
佛山市中天融新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the current industrial production, due to the harsh and complex conditions of transesterification in the transesterification method, it is extremely difficult to accurately control the molecular weight of polycarbonate diols, and there will be the appearance of polycarbonate diols with low molecular weight. These low molecular weight polycarbonate diols Polycarbonate diols can be used in fewer fields and sales are low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The present invention provides a preparation method of polycarbonate diol.

[0044] The technical solution is:

[0045] A preparation method of polycarbonic glycol, comprising the following steps:

[0046] Using polyol and carbonate as main raw materials, through transesterification polycondensation reaction, the crude product of polycarbonate diol is prepared;

[0047] Collect the polycarbonate diol crude product with a molecular weight of 600-1100;

[0048] The polycarbonate diol crude product with the molecular weight of 600-1100 and the diisocyanate are mixed, and the reaction is stirred to prepare the polycarbonate diol.

[0049]In the process of preparing polycarbonate diol by transesterification, the present invention collects the crude product of polycarbonate diol with low molecular weight (600-1100), and adds diisocyanate to extend the chain and increase the molecular weight. At the same time, it can also ensure that the performance of the polycarbonate dio...

Embodiment 1

[0083] The present embodiment provides a polycarbonate diol and a preparation method thereof, the steps are as follows:

[0084] step 1)

[0085] The initial temperature of the reaction kettle was set at 95°C, the pressure in the reaction kettle was normal pressure, and in terms of the amount of matter, 100 parts of 1,4-butanediol and dimethyl carbonate were successively put into the reaction kettle after the above-mentioned preset temperature. 120 parts and 1.5 parts of catalyst sodium methoxide, then the temperature in the reaction kettle was increased isocratically, the temperature was raised to 160 ° C, and the atmospheric distillation reaction (ie the first stage reaction) was carried out for 6.5 h; after the above reaction was completed, the reaction kettle was The negative pressure of the inner system is reduced to 100Pa~10000Pa, and then the temperature is maintained at 160°C. Under this pressure and temperature, the vacuum distillation reaction (ie the second stage re...

Embodiment 2

[0093] The present embodiment provides a polycarbonate diol and a preparation method thereof, and the specific steps are as follows:

[0094] step 1)

[0095] The initial temperature of the reaction kettle was set to 95°C, the pressure in the reaction kettle was normal pressure, and in terms of the amount of matter, 100 parts of 1,6-hexanediol, dimethyl carbonate were successively put into the reaction kettle after the above-mentioned preset temperature. 120 parts and 1.5 parts of catalyst sodium methoxide, then the temperature in the reaction kettle was increased isocratically, the temperature was raised to 150 ° C, and the atmospheric distillation reaction (ie the first stage reaction) was carried out for 6.5 h; after the above reaction was completed, the reaction kettle was The negative pressure of the system is reduced to 100Pa ~ 10000Pa, and then the temperature is maintained at 160°C. Under this pressure and temperature, the vacuum distillation reaction (ie the second st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of fine chemicals, in particular to a polycarbonate diol and a preparation method thereof. The preparation method of the polycarbonate diol includes the following steps: using polyol and carbonate as main raw materials, through transesterification polycondensation reaction, to prepare a crude product of the polycarbonate diol; collecting polycarbonate with a molecular weight of 600-1100 Diol crude product; mixing the polycarbonate diol crude product with molecular weight of 600-1100 and diisocyanate, stirring and reacting to prepare polycarbonate diol. The preparation method of the invention can increase the molecular weight of the low molecular weight polycarbonate diol crude product within a controllable range, thereby meeting application requirements.

Description

technical field [0001] The invention relates to the technical field of fine chemicals, in particular to polycarbonate diol and a preparation method thereof. Background technique [0002] Polycarbonate diol (PCDL) is a polymer with multiple carbonate groups in the molecule and hydroxyl groups at both ends of the molecule. Compared with polyurethane synthesized by polyol and polyether polyol, polycarbonate polyurethane has excellent mechanical properties, hydrolysis resistance, heat resistance, oxidation resistance and light resistance. Therefore, polycarbonate diol is considered to be a polyol with the best performance at present, and is widely used in the preparation of various polyurethane materials with excellent quality and performance. [0003] In the traditional production process of polycarbonate diol, there are phosgene method, cyclic carbonate ring-opening polymerization method, carbon dioxide and epoxide copolymerization method and transesterification method. Amon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G64/02C08G64/30C08G18/44
CPCC08G64/305C08G64/0208C08G18/44Y02P20/141
Inventor 许阳宾杨武彬黄绍源陈永强
Owner 佛山市中天融新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com