Environment-friendly asphalt high-viscosity additive and preparation method thereof

A high-viscosity, environmentally friendly technology, used in building insulation materials, building components, buildings, etc., can solve problems such as high energy consumption, high-viscosity environmental pollution, and difficulty in melting and dispersing high-viscosity

Active Publication Date: 2021-09-24
湖南省交通科学研究院有限公司
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The main purpose of the present invention is to provide an environment-friendly asphalt high-viscosity additive and its preparation method, aiming at solving the problems that the above-mentioned high-viscosity agent is difficult to melt and disperse in the asphalt mixture, the phenomenon of high energy consumption caused by high-temperature heating construction, and high The technical problem of environmental pollution caused by the components in the adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly asphalt high-viscosity additive and preparation method thereof
  • Environment-friendly asphalt high-viscosity additive and preparation method thereof
  • Environment-friendly asphalt high-viscosity additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The present invention also provides a method for preparing the environment-friendly asphalt high-viscosity additive described in any one of the above, comprising: adding the styrene-butadiene-styrene block copolymer, the viscosity-increasing component , the compatibilizer component, the high-temperature viscosity regulator, the plasticizer, the anti-aging component and the accelerator are mixed and melted at a temperature of 150°C to 190°C and then granulated to obtain The environment-friendly asphalt high-viscosity additive.

[0041] As a detailed description of the preparation method of the environment-friendly asphalt high-viscosity additive, a preparation method of the environment-friendly asphalt high-viscosity additive can be prepared according to the following method: the styrene-butadiene-styrene block copolymerization The thickening component, the compatibilizing component, the high-temperature viscosity regulator, the plasticizer, the anti-aging component, and...

Embodiment 1

[0045] A high-viscosity additive, comprising in parts by mass: 100 parts of styrene-butadiene-styrene block copolymer, 40 parts of viscosity-increasing components, 10 parts of compatibilizing components, 3 parts of high-temperature viscosity regulators, 3 parts of plasticizer, 0.3 part of anti-aging component, 0.2 part of accelerator.

[0046] Among them, the styrene-butadiene-styrene block copolymer is linear SBS-YH791H (Sinopec Baling Petrochemical Branch); the tackifier component is C9 petroleum resin (Zibo Xinle Chemical Co., Ltd., softening point is 120°C); the compatibilizer component is naphthenic rubber oil (China Petroleum Karamay Petrochemical Company); the high temperature viscosity regulator is 50% stearic acid amide (Zibo Xinrong Chemical Technology Co., Ltd.) and 50% polypropylene wax TS-5116 (Nanjing Tianshi New Material Technology Co., Ltd., melting point is 110°C); plasticizer is dioctyl phthalate (Jinan Huijinchuan Chemical Co., Ltd.); anti-aging agent is 2,6...

Embodiment 2

[0049] A high-viscosity additive, comprising in parts by mass: 100 parts of styrene-butadiene-styrene block copolymer, 85 parts of viscosity-increasing components, 30 parts of compatibilizing components, 8 parts of high-temperature viscosity regulators, 10 parts of plasticizer, 3 parts of anti-aging component, 1 part of accelerator.

[0050] Among them, the styrene-butadiene-styrene block copolymer is star-shaped SBS Daokai 2#4303-2 (Sinopec Baling Petrochemical Branch); Thai Petrochemical Co., Ltd., with a softening point of 130°C); the compatibilizer is environmentally friendly aromatic oil (Zibo Guangyi Petrochemical Co., Ltd.); the high-temperature viscosity regulator is 20% stearic acid amide (Zibo Xinrong Chemical Technology Co., Ltd. company) and 80% polyethylene wax H100 (Qingdao Haihao Chemical Co., Ltd., melting point is 100 ℃); plasticizer is dioctyl terephthalate (Shandong Langtai Chemical Co., Ltd.); antiaging agent is four [β -(3,5-di-tert-butyl-4-hydroxyphenyl)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention provides an environment-friendly asphalt high-viscosity additive and a preparation method thereof. The environment-friendly asphalt high-viscosity additive comprises the following components in parts by mass: 100 parts of a styrene-butadiene-styrene block copolymer, 40-85 parts of a tackifying component, 10-30 parts of a compatibilizing component, 3-8 parts of a high-temperature viscosity modifier, 3-10 parts of a plasticizer, 0.3-3.0 parts of an anti-aging component and 0.2-1.0 part of an accelerant. The preparation method of the environment-friendly asphalt high-viscosity additive comprises the following steps: uniformly mixing and melting the styrene-butadiene-styrene block copolymer, the tackifying component, the compatibilizing component, the high-temperature viscosity modifier, the plasticizer, the anti-aging component and the accelerant at the temperature of 150-190 DEG C, and granulating, so as to obtain the environment-friendly asphalt high-viscosity additive. According to the present invention, the high-viscosity adhesive can be rapidly and uniformly molten and dispersed in an asphalt mixture, the mixing construction temperature of the high-viscosity adhesive in the asphalt mixture can be effectively reduced, and the used components belong to the environmental protection non-toxic material.

Description

technical field [0001] The invention relates to the field of road engineering materials, in particular to an environment-friendly asphalt high-viscosity additive and a preparation method thereof. Background technique [0002] Drainage asphalt pavement with large void characteristics has become the best pavement form to achieve a leap in the quality of road surface characteristics because of its outstanding advantages such as high anti-skid performance, low noise, suppression of water mist, prevention of water drift, and reduction of glare. However, due to the large void ratio of the drainage asphalt mixture, it is vulnerable to water damage and aging, which will lead to poor durability of the drainage asphalt pavement. Therefore, the cement must have high viscosity characteristics to make the drainage asphalt pavement have better performance. High-viscosity additives (referred to as high-viscosity agents) are one of the effective ways to improve durability. [0003] In orde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L57/02C08L91/00C08L23/12C08K5/00C08K5/098C08K5/20C08K5/12C08K5/13C08L23/06C08K5/134C08L23/08C08L95/00
CPCC08L53/02C08L95/00C08L2205/035C08L2205/025C08L57/02C08L91/00C08L23/12C08K5/00C08K5/098C08K5/20C08K5/12C08K5/13C08L23/06C08K5/1345C08L23/0853
Inventor 刘至飞陈宇亮吴开孙剑峰李婷玉郑祖恩曾辉彭孝南张迅黄毅任毅
Owner 湖南省交通科学研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap