A kind of lock body steel with easy drilling and fast chip removal and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of lock body steel and steel billet, which is applied in the field of locks, can solve problems such as reduction, achieve the effects of reducing drilling resistance, inhibiting grain boundary segregation, and improving high-temperature thermoplasticity
Active Publication Date: 2021-12-31
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF0 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The object of the present invention is to overcome the problem that gray cast iron is difficult to forge and roll the lock body steel in the prior art, and provide a lock body steel with easy drilling and fast chip removal and its preparation method; the present invention optimizes each Components, limit the content of hard elements and hard phases in the steel, avoid the wear of the drill bit due to temperature rise and phase change during the drilling process, and prolong the life of the drill bit; The size and shape of Mn(S, Se), ferrite and pearlite of the lock body steel are improved, the hardness of the steel is further reduced, and the chip removal, chip breaking ability and drill life of the drilling process are improved, and the obtained steel can be processed Integrated large-scale industrial production of casting and rolling
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0033] A lock body steel that is easy to drill and fast chip removal in this embodiment, its chemical composition is calculated by mass percentage: C: 0.012%, Si: 0.013%, Mn: 1.64%, P: 0.012%, S: 0.405 %, Bi: 0.214%, Se: 0.0093%, T[O]: 0.0045%, B: 0.0056%, and the rest are Fe and unavoidable impurities.
Embodiment 2
[0035] A lock body steel that is easy to drill and fast chip removal in this embodiment, its chemical composition is calculated by mass percentage: C: 0.018%, Si: 0.031%, Mn: 1.77%, P: 0.025%, S: 0.461 %, Bi: 0.197%, Se: 0.0079%, T[O]: 0.0031%, B: 0.0041%, and the rest are Fe and unavoidable impurities.
Embodiment 3
[0037] A lock body steel that is easy to drill and fast chip removal in this embodiment, its chemical composition is calculated by mass percentage: C: 0.026%, Si: 0.026%, Mn: 1.83%, P: 0.018%, S: 0.504 %, Bi: 0.153%, Se: 0.0061%, T[O]: 0.0054%, B: 0.0052%, and the rest are Fe and unavoidable impurities.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a lock body steel which is easy to drill and has fast chip removal and a preparation method thereof, belonging to the technical field of locks. Its chemical composition is calculated by mass percentage: C: 0.01-0.03%, Si: 0-0.04%, Mn: 1.6%-2.0%, P: 0.010%-0.030%, S: 0.40%-0.55%, Bi: 0.15 %~0.22%, Se: 0.005%~0.01%, T[O]: 0.003%~0.006%, B: 0.004%~0.006%, and the rest are Fe and unavoidable impurities. The invention effectively controls the size and shape of Mn(S, Se), ferrite and pearlite of the lock body steel by compounding a certain amount of Bi and Se and optimizing the content of Mn and S in the steel, further reducing the hardness of the steel, Improve the chip removal, chip breaking ability and drill bit life during the drilling process; and through forging, hot rolling, staged cooling and shot blasting processes in the preparation process, the matrix ferrite structure and a small amount of pearlite structure are finally obtained, and the drilling performance is excellent The lock body steel product is low in hardness, easy to drill, fast in chip removal, fast in heat dissipation, and has little wear on high-speed drill bits. It can be widely used in the manufacture of padlocks and gourd locks.
Description
technical field [0001] The invention relates to the technical field of locks, in particular to a lock body steel which is easy to drill and has fast chip removal and a preparation method thereof. Background technique [0002] Padlocks are the oldest and largest family of locks in the world, and other locks are all derived from padlocks. Pujiang County, Zhejiang Province is currently the largest distribution center for the production and sales of padlocks in my country, with an annual output of more than 300,000 tons of padlocks. Padlocks are mainly divided into stainless steel padlocks, copper padlocks, iron padlocks and zinc alloy padlocks according to their materials. Among them, iron padlocks are the most commonly used due to their low price and good drilling performance, so the output is also the largest. [0003] At present, most of the iron padlocks on the market are made of HT200 gray cast iron. Although gray cast iron contains a large amount of spherical or flake gr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.