Flame-retardant nylon composite material and preparation method thereof

A flame-retardant composite material, nylon technology, applied in the field of nylon flame-retardant composite materials and its preparation, flame-retardant polyester composite materials, can solve the problems of not meeting the processing requirements of high-temperature nylon, volatile, low decomposition temperature, etc., to achieve Good dimensional stability, good flame retardancy and high mechanical strength

Active Publication Date: 2021-10-12
HONGHU YITAI TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the decomposition temperature of some small molecule organophosphorus flame retardants is low, which cannot meet the processing requirements of high-temperature nylon and is volatile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant nylon composite material and preparation method thereof
  • Flame-retardant nylon composite material and preparation method thereof
  • Flame-retardant nylon composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment discloses the preparation of polyphosphonate flame retardant:

[0035] Add 26.04g phosphate methyl diphenyl ester and 31.8g phenolphthalein in the four-neck flask that electromechanical stirrer and vacuum distillation device are housed, then add 0.32g catalyst sodium metaaluminate (catalyst quality is 1% of phenolphthalein quality ), feed nitrogen under stirring, react at 140°C for 1 hour, and react at 180°C for 3 hours. During the reaction, the small molecule phenol produced is separated, and then the reaction is continued for 4 hours under reduced pressure.

[0036] After the reaction, crush the solid crude product obtained after the reaction, fully stir it in hot water at 60°C for 3 hours, then filter it while it is hot, collect the filter cake, and dry it in a vacuum oven at 50°C for 12 hours to obtain a solid product polyphosphonate.

[0037] Concrete synthetic route is as follows:

[0038]

[0039] Wherein, the structural characterization of t...

Embodiment 2

[0043] This embodiment discloses a method for preparing a high-temperature nylon flame-retardant composite material, which includes the following steps:

[0044] (1) Get the polyphosphonate flame retardant 10g that above-mentioned embodiment 1 makes, 0.5g antioxidant and 89.5g nylon 10T resin resin and carry out thorough mixing, obtain mixed base material, then place co-rotating twin-screw extruder In the machine, pellets are processed and granulated, wherein the temperature range of the twin-screw extruder is 300-350° C., and the rotation speed is 160-220 r / min.

[0045] (2) Take the pellets of step (1) and carry out molding processing in an injection molding machine to obtain a composite material, wherein the temperature of the injection molding machine is 300-350°C.

Embodiment 3

[0047] The difference between this embodiment and the above-mentioned embodiment 2 is that the addition amount of the polyphosphonate flame retardant is 15 g, the nylon 10T resin is 84.5 g, and the others remain the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
carbon residual rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant nylon composite material and a preparation method thereof, and belongs to the technical field of polymer composite materials. The material is prepared from the following raw material components in percentage by mass: 59-94.5% of nylon 10T resin; 5-40% of a polyphosphonate flame retardant; and 0.5%-1% of an antioxidant; wherein the polyphosphonate flame retardant has the following structural formula, and n in the structural formula is a positive integer ranging from 21 to 50. The high-temperature nylon flame-retardant composite material designed by the invention is high in mechanical strength, good in dimensional stability and good in flame-retardant effect.

Description

technical field [0001] The invention relates to a flame-retardant polyester composite material, which belongs to the technical field of polymer composite materials, in particular to a nylon flame-retardant composite material and a preparation method thereof. Background technique [0002] Semi-aromatic high-temperature nylon (PA) has many advantages such as high melting point, low water absorption and good dimensional stability, and is widely used in electronic appliances and many related fields. The main varieties of high temperature nylon are PA4T, PA6T, PA9T, PA10T and so on. When electronic and electrical products work, they will be accompanied by high temperature and high pressure and short circuit, which will easily cause plastic components and cause fire. Therefore, materials that can be widely used in electronic appliances must be subjected to corresponding flame retardant treatment, and the current flame retardants that can meet the processing temperature of high-te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L85/02
CPCC08L77/06C08L2201/02C08L85/02
Inventor 刘学清刘继延邹立勇成贞辉方玮沈道胜
Owner HONGHU YITAI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com