High-adhesion nano cutter coating and preparation method thereof

A high-adhesion, tool technology, applied in coatings, metal material coating processes, ion implantation plating, etc., can solve problems such as poor bonding strength, improve adhesion performance and anti-shedding performance, and improve film quality. , the effect of promoting particle nucleation

Pending Publication Date: 2021-11-16
科汇纳米技术(常州)有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the defect of poor bonding strength between the existing nano-knife coating and the substrate, the application provides a high-adhesion nano-knife coating and a preparation method thereof, and adopts the following technical scheme:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-adhesion nano cutter coating and preparation method thereof
  • High-adhesion nano cutter coating and preparation method thereof
  • High-adhesion nano cutter coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0039] Weigh 5 kg of water, 1 kg of nano-silica sol, 0.6 kg of alumina particles and 0.3 kg of 1% sodium hydroxide solution by mass fraction respectively, stir and mix to obtain polishing solution 1.

preparation example 2

[0041] 5.5 kg of water, 1.25 kg of nano-silica sol, 0.7 kg of alumina particles and 0.4 kg of 1% sodium hydroxide solution by mass fraction were weighed and stirred to obtain polishing solution 2.

preparation example 3

[0043] Weigh 6 kg of water, 1.5 kg of nano-silica sol, 0.8 kg of alumina particles and 0.5 kg of 1% sodium hydroxide solution by mass fraction, and stir to obtain polishing solution 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of hard coatings, and particularly discloses a high-adhesion nano cutter coating and a preparation method thereof. The high-adhesion nano cutter coating comprises a CrN interface layer, an AlTiN intermediate layer, an AlTiN / TiSiN connecting layer and a TiSiN coating layer which are sequentially coated on the cutter surface subjected to matrix modification from inside to outside, and the CrN interface layer, the AlTiN intermediate layer, the AlTiN / TiSiN connecting layer and the TiSiN coating layer are prepared by adopting a deposition coating scheme. The preparation method comprises the following steps: S1, taking a matrix modified cutter, and activating; and S2, after activation of the cutter is completed, performing deposition in sequence, and preparing the high-adhesion nanom cutter coating. In addition, the surface structure of the cutter material is optimized, and the adhesion performance and anti-falling performance of the hard coating on the cutter surface are improved.

Description

technical field [0001] The application relates to the field of hard coatings, more specifically, it relates to a high-adhesion nano tool coating and a preparation method thereof. Background technique [0002] Generally speaking, in the hard coating system, the coating and the substrate material are different. During the deposition process of the coating, the coating material is generally deposited on the surface of the substrate through chemical bonds, intermolecular forces, mechanical occlusion, etc. The layer-base material interaction is expressed as adhesion, and the force or energy required to peel off the layer-base is called the bonding force or bonding strength. Since the layer-substrate interface between the coating and the substrate is the link between the coating and the substrate, it not only plays the role of transmitting the external load received by the coating, but also bears the stress and strain inside the coating. Therefore, the quality of layer-base inter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/02C23C14/06C09G1/02
CPCC23C14/028C23C14/0641C23C14/0021C09G1/02
Inventor 陈金海梁文勇刘涛严晓倩张杰
Owner 科汇纳米技术(常州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap