Production process of water-soaking-resistant and corrosion-resistant stone-like coating

A production process, the technology of real stone paint, applied in the direction of anti-corrosion coating, coating, epoxy resin coating, etc., can solve the problems of reducing the water resistance of the coating, losing the texture of real stone paint, real stone paint is not water-resistant, etc., to improve the bonding strength, Improve the performance of colored sand surface interface and strong adhesion

Active Publication Date: 2021-11-23
湖北众雁涂料有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some real stone paints will turn white after being exposed to wind and sun, and the color will gradually fade, losing the original perfect texture of real stone paints, and real stone paints are not water-resistant
The main reason is that the quality of the emulsion used in the coating is not high. Under normal circumstances, the film-forming aid acrylate has strong stability, but some manufacturers use substances such as hydroxyethyl cellulose to prepare real stone paint. Increase the viscosity, these are relatively soluble in water, which greatly reduces the water resistance of the coating. The water absorption rate of the general acrylate coating after spraying is only 0.42%; while adding 0.4% hydroxyl on the basis of the above coating Ethyl cellulose, the water absorption rate soars to 4.3%, it is not resistant to blisters, and its corrosion resistance is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The colored sand used is natural colored sand, which is made of different particle sizes. The mass ratio used is: 10~20 mesh snowflake white sand 20: 20~40 mesh marble 80: 20~40 mesh quartz sand 250: 40~80 mesh Quyanghong 5: 80~120 mesh floor yellow 2.

[0026]Among them, the source of origin: Han flute snowflake white sand Susong Poliang, Hualin quartz sand Fengyang Temple, floor Huanghu Tieshan, Xuanlang marble sand Anqing Poliang, Quyang Hongshan Quyang. Step 1. Surface treatment of colored sand: send the colored sand into the film scraper dryer, add dispersant, the dispersant is composed of neoalkoxy trineodecanoyl zirconate LICA01, neoalkoxy tris (dioctyl) coke Phosphate zirconate LICA38 mixture with a weight ratio of 1:1, step a single drum, drum speed 5r / min steam pressure 0.45MPa, treatment time 10min, dispersant accounts for 10% of the weight of the colored sand, unload after the treatment is completed Material; step 2, the colored sand after the surface treat...

Embodiment 2

[0029] The colored sand used is natural colored sand, which is made of different particle sizes. The mass ratio used is: 10~20 mesh snowflake white sand 20: 20~40 mesh marble 80: 20~40 mesh quartz sand 250: 40~80 mesh Quyanghong 5: 80~120 mesh floor yellow 2. The source of origin: Handi snowflake white sand Susong Poliang, Hongyu Huai Shang clogs mountain quartz sand, floor Huanghu Tieshan, Xuanlang marble sand Anqing Poliang, Quyang red Shandong Quyang.

[0030] Step 1. Surface treatment of colored sand: send the colored sand into the film scraper dryer, add dispersant, neoalkoxy trineodecanoyl zirconate LICA01, neoalkoxy tris (dioctyl) pyrophosphate zirconium A mixture of ester LICA38 with a weight ratio of 1:1, step a single drum, drum speed 3r / min, steam pressure 0.4MPa, treatment time 5min, dispersant accounted for 5% of the weight of the colored sand, unloading after the treatment is completed; step 2. The colored sand after surface treatment is premixed with resin: add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
water absorptionaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process of a water-soaking-resistant and corrosion-resistant stone-like coating, and belongs to the technical field of chemical production. According to the production process, the stone-like coating is prepared from natural colored sand. The process is simple. The raw material source is wide. The stone-like coating has the characteristics of good weather resistance, color retention, corrosion resistance, water resistance, aging resistance, capability of prolonging the service life of a building and the like; the stone-like coating has the advantages of flexibility, capability of effectively covering tiny cracks, cracking resistance, good flexibility, collision resistance and the like; the stone-like coating is rich in expressive force, strong in stereoscopic impression, good in plasticity, and good in alkali-acid resistance and ultraviolet resistance; the stone-like coating is stable in color, free of fading, wide in application range, high in adhesive force, waterproof and breathable; and the stone-like coating has good waterproof, breathable, environment-friendly, safe, aging-resistant, cracking-resistant, corrosion-resistant and water-soaking-resistant performance.

Description

technical field [0001] The invention belongs to the technical field of chemical production, in particular to a production process of blister-resistant and corrosion-resistant genuine stone paint. Background technique [0002] Real stone paint has a three-dimensional hard coating, and the surface of the coating can also be coated with finish varnish to adjust the desired tone and gloss, so as to obtain a coating with rich texture, various colors, and a decorative surface similar to natural stone such as granite. It enhances the decorative effect, so it is deeply loved by people. Real stone paint is composed of synthetic resin emulsion and artificial colored sand and other materials. The source of raw materials is abundant, and the paint production process and equipment are relatively simple. Due to the use of stable materials such as ceramic granules and colored aggregates, it will not change or fade due to the influence of wind and rain, sunlight, sulfur dioxide gas, etc., ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D7/62C09D7/63C09D5/08
CPCC09D163/10C09D7/62C09D7/63C09D5/08C08K2003/265C08K9/08C08K9/04C08K3/00C08K3/26C08K3/36C08K5/053C08K5/17
Inventor 董云龙
Owner 湖北众雁涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap