Silver nanowire containing polyphenol compound and preparation method and application thereof

A polyphenol compound, silver nanowire technology, applied in the field of optoelectronics, can solve the problems of polluted materials, waste, inability to generate high aspect ratio silver nanowires, etc., and achieves the effect of inhibiting lateral growth, solving adverse effects, and accelerating reduction rate.

Active Publication Date: 2021-12-03
中硕实业(上海)有限公司
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the existence of the template, a strong corrosion method is required, which will cause serious pollution and waste of materials. At the same time, under the limitation of the template, silver nanowires with high aspect ratio cannot be produced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silver nanowire containing polyphenol compound and preparation method and application thereof
  • Silver nanowire containing polyphenol compound and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] This embodiment provides a silver nanowire containing a polyphenol compound, and the silver nanowire containing a polyphenol compound is prepared by the following preparation method:

[0055] (1) Take a certain amount of PVP and dissolve it in ethylene glycol, stir until the PVP is completely dissolved to obtain a PVP solution, wherein the PVP molecular weight used is 1300000, and the concentration of the prepared solution is 0.008g / mL; weigh a certain amount of Dissolve ferric bromide in ethylene glycol, stir magnetically until ferric bromide is completely dissolved, and obtain a ferric bromide solution with a concentration of 0.015g / mL; weigh a certain amount of silver nitrate and dissolve it in ethylene glycol, stir magnetically, It was completely dissolved to obtain a silver nitrate solution with a concentration of 0.03g / mL;

[0056] (2) Mix 60mL of PVP solution with 20mL of silver nitrate solution, stir at a speed of 560r / min for 10min, then add 1mL of ferric bromi...

Embodiment 2

[0059] This embodiment provides a silver nanowire containing a polyphenol compound, and the silver nanowire containing a polyphenol compound is prepared by the following preparation method:

[0060] (1) Take a certain amount of PVP and dissolve it in ethylene glycol, and stir until the PVP is completely dissolved to obtain a PVP solution. The PVP molecular weight used is 1300000, and the concentration of the prepared solution is 0.01g / mL; a certain amount of ferric bromide is weighed and dissolved in ethylene glycol, and magnetically stirred until the ferric bromide is completely dissolved to obtain a concentration of 0.03g / mL. mL of ferric bromide solution; weigh a certain amount of silver nitrate and dissolve it in ethylene glycol, stir it magnetically to completely dissolve it, and obtain a silver nitrate solution with a concentration of 0.02g / mL;

[0061] (2) Mix 70mL of PVP solution with 20mL of silver nitrate solution, stir at a speed of 560r / min for 15min, then add 0.5m...

Embodiment 3

[0064] This embodiment provides a silver nanowire containing a polyphenol compound, and the silver nanowire containing a polyphenol compound is prepared by the following preparation method:

[0065] (1) Take a certain amount of PVP and dissolve it in ethylene glycol, and stir until the PVP is completely dissolved to obtain a PVP solution. The PVP molecular weight used is 1300000, and the concentration of the prepared solution is 0.006g / mL; a certain amount of ferric bromide is weighed and dissolved in ethylene glycol, and magnetically stirred until the ferric bromide is completely dissolved, and the obtained concentration is 0.01g / mL. mL of ferric bromide solution; weigh a certain amount of silver nitrate and dissolve it in ethylene glycol, stir it magnetically to completely dissolve it, and obtain a silver nitrate solution with a concentration of 0.04g / mL.

[0066] (2) Mix 45mL of PVP solution with 15mL of silver nitrate solution, stir at a speed of 560r / min for 12min, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a silver nanowire containing a polyphenol compound and a preparation method and application thereof. The silver nanowire containing the polyphenol compound is prepared from the following raw materials: polyvinylpyrrolidone, bromine salt, silver salt and the polyphenol compound. According to the silver nanowire, on the basis of typical polyhydric alcohol synthesized silver nanowires, the polyphenol compound is introduced to serve as a reducing agent, the reduction rate of the reaction is increased, the high-pressure condition is not needed, and operation is easy; and the polyphenol compound is introduced as the reducing agent, so that silver ions can be subjected to a reduction reaction at a lower temperature, the transverse growth of silver is inhibited, and the generation of the silver nanowire with a smaller diameter is facilitated.

Description

technical field [0001] The invention belongs to the field of optoelectronic technology, in particular to a silver nanowire containing a polyphenol compound and its preparation method and application, especially to a silver nanowire containing a polyphenol compound prepared from a polyphenol compound and its preparation method and application . Background technique [0002] With the continuous development of electronic equipment in the direction of flexibility, flexible transparent conductive materials have become a research hotspot. Transparent conductive films are widely used in electronic products such as touch screens, light-emitting diodes, and solar cells, and have great application prospects. Currently, the most commonly used material for preparing transparent conductive films is indium tin oxide (ITO). ITO contains rare metal element indium, which is expensive and toxic, which increases the preparation cost. Therefore, next-generation flexible transparent materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/24B22F1/00B82Y30/00B82Y40/00A01N59/16A01P1/00A01P3/00
CPCB22F9/24B82Y30/00B82Y40/00A01N59/16
Inventor 王立惠吴迎港耿小红吴博竞陈同祥
Owner 中硕实业(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com