Rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete and preparation method thereof

A high-performance concrete, rigid waterproof technology, used in rigid waterproof, anti-freeze-thaw, self-compacting high-performance concrete and its preparation, anti-corrosion field, can solve problems such as short life, corrosion, etc., to improve service life, prevent movement, improve Compatibility effects

Pending Publication Date: 2021-12-17
河南正大金盾环保材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of severe leakage and corrosion and short service life of existing buildings, the present invention provides a rigid waterproof, freeze-thaw resistant, anti-corrosion, self-compacting high-performance concrete and its preparation method, which are waterproof, freeze-thaw resistant, anti-corrosion, self-contained Compact and other advantages, to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete and preparation method thereof
  • Rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete and preparation method thereof
  • Rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: A rigid waterproof, freeze-thaw-resistant, anti-corrosion, self-compacting high-performance concrete is composed of the following raw materials: ordinary Portland cement, water, stones, sand, expansion agent, water-reducing agent, and waterproof nano-powder; The weight of each raw material is: ordinary Portland cement 450Kg, water 132kg, gravel 1250kg, sand 550Kg, expansion agent 15kg, water reducing agent 1.2kg, waterproof nano powder 25Kg, wherein the waterproof nano powder is composed of the following raw materials: mica powder, hydrophobic Water perlite powder, dimethyl silicone oil, silane coupling agent, surfactant, wherein the weight of each raw material is: mica powder 56.95Kg, hydrophobic perlite powder 8.23Kg, dimethyl silicone oil 1.0Kg, silane coupling agent 1.05Kg, surfactant 2.31Kg; the described water reducer is a powder polycarboxylate high-performance water reducer, and the described expansion agent is a calcium sulfoaluminate type expansio...

Embodiment 2

[0029] Embodiment 2: A rigid waterproof, freeze-thaw resistant, anti-corrosion, self-compacting high-performance concrete is composed of the following raw materials: ordinary Portland cement, water, stones, sand, expansion agent, water-reducing agent, and waterproof nano-powder; wherein The weight of each raw material is: ordinary Portland cement 450Kg, water 140kg, gravel 1250kg, sand 550Kg, expansion agent 25kg, water reducing agent 0.7kg, waterproof nano powder 15Kg, wherein the waterproof nano powder is composed of the following raw materials: mica powder, hydrophobic Water perlite powder, simethicone oil, silane coupling agent, surfactant, wherein the weight of each raw material is: mica powder 70Kg, hydrophobic perlite powder 21Kg, simethicone oil 4Kg, silane coupling agent 1.5Kg, Surfactant 2.31Kg; the water reducer is a powder polycarboxylate high-energy water reducer, and the expansion agent is a calcium sulfoaluminate expansion agent.

[0030] A method for preparing ...

Embodiment 3

[0037] Embodiment 3: A rigid waterproof, freeze-thaw-resistant, anti-corrosion, self-compacting high-performance concrete is composed of the following raw materials: ordinary Portland cement, water, stones, sand, expansion agent, water-reducing agent, and waterproof nano-powder; The weight of each raw material is: ordinary Portland cement 450Kg, water 140kg, gravel 1250kg, sand 550Kg, expansion agent 18kg, water reducing agent 0.85kg, waterproof nano powder 19Kg, wherein the waterproof nano powder is composed of the following raw materials: mica powder, hydrophobic Water perlite powder, simethicone oil, silane coupling agent, surfactant, wherein the weight of each raw material is: mica powder 65Kg, hydrophobic perlite powder 18Kg, simethicone oil 3.1Kg, silane coupling agent 1.1Kg , Surfactant 3.9Kg; The described water-reducer is a powder polycarboxylate high-energy water-reducer, and the described expansion agent is a calcium sulfoaluminate expansion agent.

[0038] A method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of building materials, and discloses rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete which is characterized in that the rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete comprises the following components: 400 to 500 parts of cement, 100 to 180 parts of water, 1200 to 1300 parts of stone, 500 to 600 parts of sand, 10 to 30 parts of an expanding agent, 0.5 to 2.5 parts of a water reducing agent, and 10 to 30 parts of waterproof nano powder, and the waterproof nano powder comprises the following components: mica powder, hydrophobic perlite powder, dimethyl silicone oil, a silane coupling agent and a surfactant. According to the rigid waterproof, freeze-thaw-resistant, corrosion-resistant and self-compacting high-performance concrete and the preparation method thereof, the waterproof nano powder is added, and the waterproof nano powder has a strong hydrophobic effect and a unique non-metal sheet structure, so that occlusion and connection among coarse and fine aggregates of the high-performance concrete can be effectively promoted, the contact area of a microstructure is enlarged, the porosity is reduced, and the compactness is improved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a rigid waterproof, freeze-thaw-resistant, anti-corrosion, self-compacting high-performance concrete and its preparation method*. Background technique [0002] With the development of science and technology, the construction industry is becoming more and more developed, high-rise buildings, railways, highway bridges, airports, subways, tunnels, urban underground pipe corridors, large storage warehouses, ports, docks, island construction, etc., are all based on High-performance concrete is the main building material. High-performance concrete looks like a whole. Its interior is full of large and small pores and defects. Water enters into it, and various corrosive ions enter it with the help of water, resulting in high-performance concrete. Various damage forms and defects, such as water seepage, freeze-thaw damage, corrosion damage, etc., greatly reduce the actual life ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B22/14C04B24/42C04B111/26C04B111/20C04B111/27C04B103/65
CPCC04B28/04C04B22/142C04B40/0039C04B2111/27C04B2111/29C04B2111/26C04B2103/65C04B14/02C04B14/06C04B2103/302C04B14/20C04B14/18C04B24/42C04B2103/40
Inventor 杨水红苏峰苏仪方李嘉欣
Owner 河南正大金盾环保材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com