Self-cleaning super-hydrophilic ceramic material and preparation method thereof

A ceramic material, super hydrophilic technology

Active Publication Date: 2022-01-28
亚细亚新材料科技股份公司
View PDF18 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the above-mentioned scheme has problems such as not being firmly combined with the adobe bricks and falling off easily.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] This embodiment provides a self-cleaning super-hydrophilic ceramic material, the super-hydrophilic ceramic material includes a first coating and a second body layer, the composition of the first coating includes nano-titanium dioxide, nano-alumina and nano-dioxide Silicon oxide; the composition of the second body layer includes 35 parts of quartz, 10 parts of kaolin, 15 parts of alumina, 15 parts of potassium feldspar, 3.2 parts of zinc oxide and 15.2 parts of magnesia mud in parts by mass.

[0052] The size of nano-titanium dioxide in the first coating is 20-30nm; the size of nano-alumina in the first coating is 15-53nm; the size of nano-silicon dioxide in the first coating is 25-30nm 40nm.

[0053] The mass ratio of nano-titanium dioxide, nano-alumina and nano-silicon dioxide in the first coating is 5:2:3; the thickness of the first coating is 0.52mm.

[0054] Present embodiment also provides the preparation method of described self-cleaning superhydrophilic ceramic ...

Embodiment 2

[0058] This embodiment provides a self-cleaning super-hydrophilic ceramic material, the super-hydrophilic ceramic material includes a first coating and a second body layer, the composition of the first coating includes nano-titanium dioxide, nano-alumina and nano-dioxide Silicon oxide; the composition of the second body layer includes 30 parts of quartz, 12 parts of kaolin, 20 parts of alumina, 15 parts of potassium feldspar, 5 parts of zinc oxide and 30 parts of magnesia mud in parts by mass.

[0059] The size of nano-titanium dioxide in the first coating is 30-80nm; the size of nano-alumina in the first coating is 30-100nm; the size of nano-silicon dioxide in the first coating is 30-80nm 200nm.

[0060] The mass ratio of nano-titanium dioxide, nano-alumina and nano-silicon dioxide in the first coating is 4:3:3; the thickness of the first coating is 0.43mm.

[0061] Present embodiment also provides the preparation method of described self-cleaning superhydrophilic ceramic ma...

Embodiment 3

[0065] This embodiment provides a self-cleaning super-hydrophilic ceramic material, the super-hydrophilic ceramic material includes a first coating and a second body layer, the composition of the first coating includes nano-titanium dioxide, nano-alumina and nano-dioxide Silicon oxide; the composition of the second body layer includes 40 parts of quartz, 5 parts of kaolin, 10 parts of alumina, 22 parts of potassium feldspar, 1 part of zinc oxide and 10 parts of magnesia mud in parts by mass.

[0066] The size of nano-titanium dioxide in the first coating is 10-20nm; the size of nano-alumina in the first coating is 15-30nm; the size of nano-silicon dioxide in the first coating is 15-20nm 80nm.

[0067] The mass ratio of nano-titanium dioxide, nano-alumina and nano-silicon dioxide in the first coating is 7:2:1; the thickness of the first coating is 0.78mm.

[0068] Present embodiment also provides the preparation method of described self-cleaning superhydrophilic ceramic materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a self-cleaning super-hydrophilic ceramic material and a preparation method thereof. The self-cleaning super-hydrophilic ceramic material comprises a first coating and a second body layer, wherein the first coating comprises nano titanium dioxide, nano aluminum trioxide and nano silicon dioxide; and the second body layer comprises quartz, kaolin, aluminum oxide, potassium feldspar, zinc oxide and magnesian mud. The first coating on the surface of the self-cleaning super-hydrophilic ceramic material is thin and can be closely associated with the second body layer, and the nano titanium dioxide in the first coating has photocatalytic activity, so that the self-cleaning of the ceramic material can be realized, and the combination of the first coating, the nano titanium dioxide and the second body layer has super-hydrophilic performance and is beneficial to the removal of oil stains.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a self-cleaning super-hydrophilic ceramic material and a preparation method thereof. Background technique [0002] Super-hydrophilic ceramic tiles are mainly through the organic combination of photocatalytic materials and ceramic tiles to achieve anti-fouling and easy-to-clean effects. The existing combination technologies of photocatalytic nanomaterials and ceramic tiles are mainly divided into two types: one is photocatalytic The catalytic material is coated on the ceramic tile to form a thin film, and the other is to add the photocatalytic material to the glaze and raw materials to prepare the easy-to-clean ceramic tile. Among them, easy-to-clean ceramic tiles are prepared by coating photocatalytic nanomaterials on ceramic tiles. This method is to directly cover photocatalytic nanomaterials on ceramic tiles, and a layer of easy-to-clean film is formed on the surface of cerami...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89C04B41/87C09D1/00C09D7/61
CPCC04B41/52C04B41/89C04B41/87C04B41/009C09D1/00C09D7/61C04B35/00C04B41/5041C04B41/5031C04B41/5035C04B41/5049C04B41/5037C04B41/5027Y02P40/60
Inventor 温晓炜马云龙
Owner 亚细亚新材料科技股份公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap