Plate biological glue and manufacturing process of multifunctional plate

A manufacturing process and multi-functional technology, which is applied in the direction of manufacturing tools, wood processing appliances, and the joining of wooden veneers. It can solve the problems of short service life, high energy consumption, and long processing cycle, and achieve simple procedures and high density. , the effect of high production efficiency

Inactive Publication Date: 2022-01-28
张良
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, most of the existing glues on the market for bonding boards have the characteristics of thermal expansion and cold contraction, which have a short service life and will also affect the service life of the boards. Moreover, most of the existing glues on the market contain benzene and benzene. It will pose a serious threat to human health; from the perspective of sheet metal processing technology, the existing sheet metal processing technology is through cold pressing and then hot pressing to shape, which consumes a lot of energy, the process is cumbersome, and the processing cycle is long, thereby reducing the sheet metal. Processing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plate biological glue and manufacturing process of multifunctional plate

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0030] A kind of board biological glue in the present embodiment is made of the following raw materials: mixed and stirred in a reaction kettle by glutinous rice flour, magnesium chloride, water, magnesium sulfate and an emulsifier;

[0031] Wherein, the weight components of the raw materials are 10%-15% of glutinous rice flour, 28%-38% of magnesium chloride, 38%-45% of water, 2%-8% of magnesium sulfate, and 8%-12% of emulsifier.

[0032] A multifunctional board made of board biological glue, the multifunctional board is composed of a composite board 2 and outer boards 1 arranged on both sides of the composite board.

[0033] The composite board 2 is made of multi-layer wood boards pressed vertically and horizontally according to the wood grain texture, and the multi-layer wood boards are bonded and fixed by board bio-glue; the composite board 2 and the outer board 1 are bonded by board bio-glue Fixing, wherein, both sides of the composite board 2 are respectively coated with ...

specific Embodiment 2

[0047] A kind of board biological glue in the present embodiment is made of the following raw materials: mixed and stirred in a reaction kettle by glutinous rice flour, magnesium chloride, water, magnesium sulfate and an emulsifier;

[0048] Wherein, the weight components of the raw materials are 11%-14% of glutinous rice flour, 30%-36% of magnesium chloride, 39%-44% of water, 3%-7% of magnesium sulfate, and 9%-11% of emulsifier.

[0049] A multifunctional board made of board biological glue, the multifunctional board is composed of a composite board 2 and outer boards 1 arranged on both sides of the composite board 2 .

[0050] The composite board 2 is made of multi-layer wood boards pressed vertically and horizontally according to the wood grain texture, and the multi-layer wood boards are bonded and fixed by board bio-glue; the composite board 2 and the outer board 1 are bonded by board bio-glue Fixing, wherein, both sides of the composite board 2 are respectively coated wi...

specific Embodiment 3

[0064] A kind of board biological glue in the present embodiment is made of the following raw materials: mixed and stirred in a reaction kettle by glutinous rice flour, magnesium chloride, water, magnesium sulfate and an emulsifier;

[0065] Wherein, the weight components of the raw materials are 12% of glutinous rice flour, 33% of magnesium chloride, 40% of water, 5% of magnesium sulfate, and 10% of emulsifier.

[0066] A multifunctional board made of board biological glue, the multifunctional board is composed of a composite board 2 and outer boards 2 arranged on both sides of the composite board.

[0067] The composite board 2 is made of multi-layer wood boards pressed vertically and horizontally according to the wood grain texture, and the multi-layer wood boards are bonded and fixed by board bio-glue; the composite board 2 and the outer board 1 are bonded by board bio-glue Fixing, wherein, both sides of the composite board 2 are respectively coated with the board biological...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a plate biological glue. The plate biological glue is prepared by mixing and stirring glutinous rice flour, magnesium chloride, water, magnesium sulfate and an emulsifier in a reaction kettle, the invention further discloses a multifunctional plate made of the plate biological glue and a manufacturing process of the multifunctional plate, the multifunctional plate is composed of a composite board and outer boards arranged on the two sides of the composite board, and the composite board is formed by vertically and horizontally crossing and vertically pressing a plurality of layers of wood boards according to wood grains. The peripheries of the multiple layers of wood boards are coated with the plate biological glue; the multifunctional plate is manufactured through multiple procedures of gluing, cold pressing and shaping, mold removing, drying, delustreing and veneering. The plate biological glue has the advantages of long-term preservation, no formaldehyde and no benzene; in the manufacturing process of the multifunctional plate , after the composite board is subjected to cold pressing shaping and the mold is removed, glue and the wood board are subjected to physical reaction and heating shaping, hot pressing is not needed, the working procedure is simpler, and the production efficiency is higher.

Description

technical field [0001] The invention relates to the technical field of board processing, in particular to a manufacturing process of biological glue for boards and multifunctional boards. Background technique [0002] Existing boards are generally made of boards with different functions bonded together by an adhesive to form a whole. Once bonded, the various boards are not easy to separate from each other. [0003] However, most of the existing glues on the market for bonding boards have the characteristics of thermal expansion and cold contraction, which have a short service life and will also affect the service life of the boards. Moreover, most of the existing glues on the market contain benzene and benzene. It will pose a serious threat to human health; from the perspective of sheet metal processing technology, the existing sheet metal processing technology is through cold pressing and then hot pressing to shape, which consumes a lot of energy, the process is cumbersome,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J199/00C09J11/04B27D1/04B27D1/08
CPCC09J199/00C09J11/04B27D1/04B27D1/08C08K2003/166C08K2003/3063C08K3/16C08K3/30
Inventor 张良
Owner 张良