Fireproof door plate with high nail-holding power

A nail-holding force and door panel technology, applied in the field of fire-resistant door panels with high nail-holding force, can solve the problems of unfavorable multi-position drilling nails for nailing, inability to nail nails, poor nail-holding effect, etc., and achieves good market application prospects. The support is easy to operate and the effect of high nail holding force

Inactive Publication Date: 2022-02-08
江山市畅畅木业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usually, although the boards added with reinforcing fibers, especially plastic boards, have high strength and hardness, they cannot be nailed and have poor nail holding effect, which is not conducive to multi-position drilling and nailing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-nail-holding fireproof door panel, the weight ratio of each raw material is: 26% of wood particles, 36% of magnesium oxide, 15% of anhydrous magnesium chloride, 21.7% of water, 1% of vitrified microbeads and 0.3% of fibers.

[0019] The above-mentioned wood particles are wood processing residues, small-diameter wood, and branch wood as raw materials. The water content is 8%-15%, and the size is 5-30mm in length, 3-13mm in width, and 2-10mm in thickness.

[0020] The above-mentioned magnesium oxide refers to magnesium oxide products with a magnesium oxide content greater than 70%, magnesium chloride refers to a moisture content of less than 3%; vitrified microbeads are closed-cell vitrified microbeads with a diameter of less than 4mm; At least one fiber of polypropylene fibers, polyvinyl alcohol fibers, wood fibers, bamboo fibers, and other plant fibers less than 1.2 mm in size.

Embodiment 2

[0022] A high-nail-holding fireproof door panel, the weight ratio of each raw material is: 26% of wood particles, 36% of magnesium oxide, 15% of anhydrous magnesium chloride, 22% of water, 0.9% of vitrified microbeads and 0.1% of fibers.

[0023] The above-mentioned wood particles are wood processing residues, small-diameter wood, and branch wood as raw materials. The water content is 8%-15%, and the size is 5-30mm in length, 3-13mm in width, and 2-10mm in thickness.

[0024] The above-mentioned magnesium oxide refers to magnesium oxide products with a magnesium oxide content greater than 70%, magnesium chloride refers to a moisture content of less than 3%; vitrified microbeads are closed-cell vitrified microbeads with a diameter of less than 4mm; At least one fiber of polypropylene fibers, polyvinyl alcohol fibers, wood fibers, bamboo fibers, and other plant fibers less than 1.2 mm in size.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof door plate with high nail-holding power. The fireproof door plate is composed of magnesium oxide, magnesium chloride, wood particles, water, vitrified micro bubbles, citric acid and fibers, and the weight ratios of the raw materials are as follows: 23 to 47 percent of wood particles, 35 to 40 percent of magnesium oxide, 8 to 20 percent of anhydrous magnesium chloride, 20 to 35 percent of water, 0 to 2 percent of vitrified micro bubbles, and 0 to 0.5 fibers. The fireproof door plate has good fireproof performance and high nail-holding power, the standard combustion time is longer than 30 min when the thickness of the fireproof door plate is 40 mm, and the nail-holding power of standard screws with the diameter of 2.8 mm is 400-2000 N.

Description

technical field [0001] The invention relates to a fireproof door panel, in particular to a fireproof door panel with high nail-holding force. Background technique [0002] There are currently two types of fire-resistant door panels on the market, one is wooden fire-resistant door panels: the wood is treated with flame-retardant treatment, and non-combustible insulation materials are filled between the two facades; the other is metal fire-resistant door panels: non-combustible insulation materials are filled between the metal facades Insulation materials. The fire department has strict regulations on fire door panels used in public places to prevent the spread of fire. Usually, although the boards added with reinforcing fibers, especially plastic boards, have high strength and hardness, they cannot be nailed and have poor nail holding effect, which is not conducive to multi-position drilling and nailing. Contents of the invention [0003] Aiming at the deficiencies of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/32E06B3/70E06B5/16C04B111/28
CPCC04B28/32E06B5/16E06B3/70C04B2111/28C04B18/26C04B14/22C04B24/06C04B16/0633C04B16/0641C04B18/265C04B18/24
Inventor 姜延红郑化高
Owner 江山市畅畅木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com