PLA fragrant wire rod for 3D printing as well as preparation method and application thereof

A 3D printing and PLA technology, applied in the field of 3D printing, can solve the problem of unpleasant odor of polymers, and achieve the effect of rich layered sensory experience and uniform color

Pending Publication Date: 2022-02-18
JF POLYMERS (SUZHOU) CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] High molecular polymers often emit unpleasant odors during extrusion processing, and the main way to remove the odor is to add deodorants, but deodorants cannot completely solve the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A PLA scented wire for 3D printing, its raw materials include, by mass percentage: 0.5% white oil, 2.5% microcapsule flavoring agent, 4% masterbatch, 4% toughening agent, and the balance is PLA.

[0023] The above preparation method of PLA scented wire for 3D printing is to mix PLA and white oil evenly, then add microcapsule flavoring agent to mix evenly, and put it into a twin-screw extruder. The screw speed of the twin-screw extruder is 38rpm, 190 Extrude and pelletize at ℃, dry at 100℃ to obtain flavored PLA masterbatches; mix PLA with flavored PLA masterbatches, tougheners, and color masterbatches evenly, and put them into a single-screw extruder, the screw of the single-screw extruder Rotate at 48rpm, extrude at 200°C, cool with warm water at 55°C, and dry at 100°C to obtain PLA scented filaments for 3D printing.

[0024] The resulting PLA scented wire used for 3D printing has a wire diameter of 1.75mm±0.03mm and a roundness of <0.05.

[0025] The method of using ...

Embodiment 2

[0027] A PLA scented wire for 3D printing, its raw materials include: white oil 1.1%, microcapsule flavoring agent 1.5%, color masterbatch 6%, toughening agent 2%, balance PLA.

[0028] The above preparation method of PLA scented wire for 3D printing is to mix PLA and white oil evenly, then add microcapsule flavoring agent to mix evenly, and put it into a twin-screw extruder. The screw speed of the twin-screw extruder is 42rpm, 160 Extrude and pelletize at ℃, dry at 100℃ to obtain flavored PLA masterbatches; mix PLA with flavored PLA masterbatches, tougheners, and color masterbatches evenly, and put them into a single-screw extruder, the screw of the single-screw extruder Rotate at 52rpm, extrude at 160°C, cool with warm water at 65°C, and dry at 100°C to obtain PLA scented filaments for 3D printing.

[0029] The resulting PLA scented wire used for 3D printing has a wire diameter of 1.75mm±0.03mm and a roundness of <0.05.

[0030] The method of using the above-mentioned PLA s...

Embodiment 3

[0032] A PLA scented wire for 3D printing, its raw materials include, by mass percentage: 0.6% white oil, 2.2% chocolate-flavored microcapsules, 4.5% chocolate-colored PLA color masterbatch, 3.5% toughening agent, and the balance is PLA .

[0033] The above preparation method of PLA flavored wire for 3D printing is to mix PLA and white oil evenly, then add chocolate-flavored microcapsules, mix evenly, and put them into a twin-screw extruder. The screw speed of the twin-screw extruder is 39rpm , Extrude and pelletize at 180°C, dry at 100°C to obtain flavored PLA masterbatches; mix PLA with flavored PLA masterbatches, tougheners, and chocolate-colored PLA color masterbatches evenly, and put them into a single-screw extruder, single-screw The screw speed of the extruder is 49rpm, extruded at 190°C, cooled with warm water at 58°C, and dried at 100°C to obtain PLA flavored filaments for 3D printing.

[0034] The resulting PLA scented wire used for 3D printing has a wire diameter o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PLA fragrant wire rod for 3D printing. The PLA fragrant wire rod is prepared from the following raw materials in percentage by mass: 0.5 to 1.1 percent of white oil, 1.5 to 2.5 percent of microcapsule flavoring agent, 4 to 6 percent of color master batch, 2 to 4 percent of flexibilizer and the balance of PLA. The invention discloses a preparation method of the PLA fragrant wire rod, which comprises the following steps: uniformly mixing the PLA and the white oil, adding the microcapsule flavoring agent, uniformly mixing the raw materials, putting the raw materials into a double-screw extruder, extruding and granulating the mixture at 160-190 DEG C, and drying the granules to obtain fragrant PLA master batches; then, uniformly mixing the PLA with the fragrant PLA master batch, the flexibilizer and the color master batch, putting the mixture into a single-screw extruder, extruding the mixture at 160-200 DEG C, and cooling the mixture to obtain the PLA fragrant wire rod. The invention further discloses a use method of the PLA fragrant wire rod, in which the PLA fragrant wire rod is put into an FDM printer for printing, and the printing temperature is 200-230 DEG C.

Description

technical field [0001] The invention relates to the technical field of 3D printing, in particular to a PLA scented wire used for 3D printing and its preparation method and application. Background technique [0002] 3D printing (especially material extrusion 3D printing technology represented by FDM / FFF) has been widely used in industrial design, medical protective gear, aerospace, automobile assembly, education, entertainment and other industries. Material extrusion 3D printing technology has the advantages of low cost, simple operation, and non-toxic and harmful production. [0003] Materials Commonly used materials for extrusion 3D printing include PLA, ABS, PETG, PC, PA, etc. Among them, PLA has been widely used because of its wide range of sources, low printing temperature, good biodegradability, and good printing and molding effects. At the same time, it has stable chemical stability and does not react with commonly used various toners, metal powders, and inorganic add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/04C08L91/06C08K9/10C08K5/00B29B9/06B29C48/05B33Y70/10
CPCC08L67/04B29B9/06B29C48/05B33Y70/10C08L91/06C08K9/10C08K5/00
Inventor 汪一奇
Owner JF POLYMERS (SUZHOU) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap