Anti-wrinkling cold rolling method for 443 ultra-pure ferritic stainless steel

A stainless steel and ultra-pure iron technology, applied in metal rolling, metal rolling, rolling mill control devices, etc., can solve the problems of strip wrinkling and stripes, and improve cold rolling reduction rate and grinding efficiency. , The effect of improving the production efficiency of the rolling mill

Pending Publication Date: 2022-02-25
GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a method for cold rolling of 443 ultra-pure ferritic stainless steel with a smooth and flat surface to solve the problem of wrinkling and streaks on the surface of the strip in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-wrinkling cold rolling method for 443 ultra-pure ferritic stainless steel
  • Anti-wrinkling cold rolling method for 443 ultra-pure ferritic stainless steel
  • Anti-wrinkling cold rolling method for 443 ultra-pure ferritic stainless steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Hot metal pretreatment, using conventional ultra-pure ferritic stainless steel smelting methods to decarburize and desulfurize the hot metal to control the internal components of the slab. Specifically, the hot metal is decarburized through the AOD converter and the VOD vacuum smelting furnace in sequence. Two times of decarburization can effectively reduce the carbon content in the molten iron, and finally put the decarburized molten iron into the LF refining furnace for desulfurization to complete the pretreatment.

[0032] (2) Casting slabs, the pretreated molten iron is continuously cast to form ferritic stainless steel slabs (the size of the slabs is 220mm*1270mm*11000mm), and the slabs are placed in the heat preservation pit for heat preservation and slow cooling. The internal composition of the blank is: w (C) ≤ 0.025%, w (Si) ≤ 1.00%, w (Mn) ≤ 1.00%, w (S) ≤ 0.030%, w (P) ≤ 0.030%, 20.50% ≤ w (Cr)≤23.00%, 0.30%≤w (Cu)≤0.80%, w(N)≤0.025%, w(C+N)≤0.1%, w(Ti+Nb...

Embodiment 2

[0048] (1) Pretreatment of molten iron, the molten iron is decarburized through the AOD converter and VOD vacuum smelting furnace in turn, and then the decarburized molten iron is placed in the LF refining furnace for desulfurization to complete the pretreatment.

[0049] (2) Casting slab, the pretreated molten iron is continuously cast to form a ferritic stainless steel slab (the size of the slab is 220mm*1270mm*11000mm), and the slab is placed in the heat preservation pit for heat preservation and slow cooling, and the slab The internal composition of the blank is: w (C) ≤ 0.025%, w (Si) ≤ 1.00%, w (Mn) ≤ 1.00%, w (S) ≤ 0.030%, w (P) ≤ 0.030%, 20.50% ≤ w (Cr)≤23.00%, 0.30%≤w (Cu)≤0.80%, w(N)≤0.025%, w(C+N)≤0.1%, w(Ti+Nb)≤0.8%, the balance is iron and unavoidable impurities. (2) Slab grinding, thermal grinding of the slab surface.

[0050] (3) Heating the slab, and then heating the ground slab to 1150°C to 1200°C and keeping it warm for 20-60min to facilitate subsequent rolli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an anti-wrinkling cold rolling method for 443 ultra-pure ferritic stainless steel. The method comprises the following steps of molding molten iron into a plate blank, rolling the plate blank into an NO1 plate, pickling and annealing the NO1 plate, rolling the NO1 plate into a cold-rolled hard steel coil by adopting a low pressure reduction rate and fewer passes, and finally slitting and packaging the steel coil. Compared with an existing 443 stainless steel rolling method, the anti-wrinkling cold rolling method has the effects that the rolling reduction rate is low, the total deformation amount is small, the surface wrinkling phenomenon of the plate is effectively reduced, and meanwhile the production efficiency is effectively improved due to the fact that the rolling reduction rate is low and the number of passes is small.

Description

technical field [0001] The invention belongs to the technical field of steel rolling, and relates to a 443 ultra-pure ferritic stainless steel and a cold rolling method thereof. Background technique [0002] 443 stainless steel is a new generation of ferritic stainless steel developed in recent years. Because it does not contain nickel, its production cost is significantly lower than that of 300 series stainless steel. Corrosion resistance and processability. 443 ferritic stainless steel has excellent corrosion resistance similar to that of austenitic stainless steel, especially good resistance to chloride ion corrosion. It is considered as a substitute for 304 austenitic stainless steel and has been widely used in the fields of elevators, architectural decoration and kitchen utensils. widely used. [0003] 443 is used as a decorative material. In the post-processing process of the product, oil grinding and wire drawing are required to form a good wire drawing surface. Ho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/28B21B37/00B21B37/74C21C1/02C21C7/064C21C7/068B22D11/00C21D8/02
CPCB21B1/28B21B37/00B21B37/74C21C1/02C21C7/064C21C7/068B22D11/002C21D8/0226C21D8/0236C21D8/0247
Inventor 任娟红白江虎高仁强陈安忠
Owner GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap