A coating preparation method for realizing high-efficiency operation of ps-pvd equipment

A PS-PVD, high-efficiency technology, applied in coating, metal material coating process, superimposed layer plating, etc., can solve the problems of low plasma jet usage rate and high cost of coating preparation, achieve liquid phase and non-ferrous metals. The effect of reducing molten particles, sufficient gasification, and improved utilization

Active Publication Date: 2022-04-15
BEIHANG UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the above-mentioned technical problems, the present invention provides a coating preparation method that realizes the low-cost and high-efficiency operation of PS-PVD equipment, and solves the low utilization rate of plasma jets and high coating preparation costs in PS-PVD. The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A coating preparation method for realizing high-efficiency operation of ps-pvd equipment
  • A coating preparation method for realizing high-efficiency operation of ps-pvd equipment
  • A coating preparation method for realizing high-efficiency operation of ps-pvd equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Using the method disclosed in the present invention, on a high-purity graphite substrate of 200 mm × 200 mm × 5 mm, the vacuum degree of the vacuum chamber, the total power of PS-PVD equipment spraying, and the spraying current are adjusted to obtain a plasma of 50-100 mm jet to prepare YSZ coating and analyze jet utilization, the specific process parameters used are as follows:

[0039] (1) Start the PS-PVD equipment, assemble the sprayed workpiece, and close the vacuum chamber;

[0040] (2) Vacuum until the pressure of the vacuum chamber is 50mbar;

[0041] (3) Adjust the spraying power to 70 kW and the spraying current to 1000A;

[0042] (4) Open the working gas valve and strike the arc. After the arc is stable, gradually adjust the gas flow to the specified gas flow Ar: 20L / min, He: 40L / min, H 2 : 10L / min, N 2 : 10L / min;

[0043] (5) Adjust the rotational speed of the workpiece to 10 rpm, use the plasma jet to preheat the blades, and detect the substrate tempera...

Embodiment 2

[0049] Using PS-PVD to spray YSZ ceramic layer on the surface of a duplex guide vane of a certain type of aero-engine, the method designed by the present invention is adopted respectively to regulate the vacuum degree of the vacuum chamber, the spraying power and the spraying current of the PS-PVD equipment To obtain a plasma jet of 50-100 mm to prepare YSZ coating and analyze the utilization rate of the jet, the parameters of the specific process steps are as follows:

[0050] (1) Start the PS-PVD equipment, assemble the spraying blades, and close the vacuum chamber;

[0051] (2) Vacuum until the pressure of the vacuum chamber is 50mbar;

[0052] (3) Adjust the spraying power to 70kW and the spraying current to 1000A;

[0053] (4) Open the working gas valve and strike the arc. After the arc is stable, gradually adjust the gas flow to the specified gas flow Ar: 20L / min, He: 40L / min, H 2 : 10L / min, N 2 : 10L / min;

[0054] (5) The speed of the blade is set to 10rpm, the blad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating preparation method for realizing high-efficiency operation of PS‑PVD equipment, aiming at the low utilization rate of plasma jets and the increase of preparation costs in the process of preparing thermal barrier coatings by plasma physical vapor deposition, and the surface of workpieces is sprayed To solve the technical problem that it is difficult to guarantee the uniformity and uniformity of the microstructure of the coating, in the process of preparing the thermal barrier coating by plasma physical vapor deposition, the plasma The diameter of the jet is 50~100mm, and an optimized design scheme is proposed for the control range of the three parameters and the synergistic control range of the three parameters, so that the heating capacity of the plasma jet will be increased accordingly, and the spray powder will be more fully vaporized. The liquid phase and unmelted particles are correspondingly reduced, the utilization rate of the plasma jet is greatly improved, energy is effectively saved, production costs are reduced, and the prepared coating has better microstructure consistency.

Description

technical field [0001] The invention belongs to the technical field of plasma spraying and physical vapor deposition of coatings, and in particular relates to a coating preparation method for realizing high-efficiency operation of PS-PVD equipment. Background technique [0002] Plasma spraying technology and electron beam physical vapor deposition (B-PVD) technology are currently the most widely used preparation technologies for thermal barrier coatings. The traditional plasma spraying technology has the advantages of higher deposition efficiency and lower equipment cost than the EB-PVD preparation technology, but it can only form a layered structure coating, and the thermal shock resistance of the coating is obviously inferior to that of the EB-PVD columnar crystal structure coating. . In view of this, plasma physical vapor deposition technology has begun to be applied in the field of thermal barrier coating preparation. [0003] Plasma physical vapor deposition (Plasma S...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/32C23C14/54C23C14/08C25D3/56C23C10/06C23C4/073C23C28/00
CPCC23C14/325C23C14/54C23C14/083C25D3/56C23C10/06C23C4/073C23C28/321C23C28/3215C23C28/3455
Inventor 郭洪波高丽华魏亮亮何雯婷彭徽
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com