Wear-resistant antibacterial microfiber synthetic leather and preparation method thereof

A synthetic leather and wear-resistant layer technology, applied in the textile field, can solve the problems that microfiber synthetic leather is susceptible to antibacterial pollution, easy to tear, and low comfort, achieving good protection effect, improving ductility, and fast moisture absorption dry skin effect

Inactive Publication Date: 2022-03-18
DONGGUAN KEDI IND CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a wear-resistant and antibacterial superfiber synthetic leather and its preparation method, which can solve the problem that the existing superfiber synthetic leather is easily polluted by antibacterial, and the comfort level is not high, and it is easy to tear at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant antibacterial microfiber synthetic leather and preparation method thereof
  • Wear-resistant antibacterial microfiber synthetic leather and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] See attached figure 1 As shown, a kind of wear-resistant and antibacterial superfiber synthetic leather comprises base layer 1, antibacterial layer 2, wear-resistant layer 3, fiber layer 4 and hydrophilic layer 5; One side of the base layer 1; the fiber layer 4 and the wear-resistant layer 3 are sequentially bonded to the other side of the base layer 1, and the thickness of the bonding layer between the fiber layer 4 and the wear-resistant layer 3 is 1mm.

[0033] Preferably, the fiber layer 4 includes a glass fiber layer 41 and a polyester fiber layer 42; the fiber filaments of the glass fiber layer 41 and the fiber filaments of the polyester fiber layer 42 are bonded to each other at an angle of 90°, Wherein, the thickness of the glass fiber layer 41 is 0.75mm, and the thickness of the polyester fiber layer 42 is 0.5mm.

[0034] Preferably, the wear-resistant layer 3 is a polyester layer with a thickness of 2 mm.

[0035] Preferably, the antibacterial layer 2 is bra...

Embodiment 2

[0037] See attached figure 2 As shown, a kind of wear-resistant and antibacterial superfiber synthetic leather comprises base layer 1, antibacterial layer 2, wear-resistant layer 3, fiber layer 4 and hydrophilic layer 5; One side of the base layer 1; the fiber layer 4 and the wear-resistant layer 3 are sequentially bonded to the other side of the base layer 1, and the thickness of the bonding layer between the fiber layer 4 and the wear-resistant layer 3 is 1mm.

[0038] Preferably, the fiber layer 4 includes a glass fiber layer 41 and a polyester fiber layer 42; the fiber filaments of the glass fiber layer 41 and the fiber filaments of the polyester fiber layer 42 are bonded to each other at an angle of 90°, Wherein, the thickness of the glass fiber layer 41 is 0.75mm, and the thickness of the polyester fiber layer 42 is 0.5mm.

[0039] Preferably, the wear-resistant layer 3 is a polyester layer with a thickness of 2mm.

[0040] Preferably, the antibacterial layer 2 is wov...

Embodiment 3

[0043] See attached figure 2 As shown, a kind of wear-resistant and antibacterial superfiber synthetic leather comprises base layer 1, antibacterial layer 2, wear-resistant layer 3, fiber layer 4 and hydrophilic layer 5; One side of the base layer 1; the fiber layer 4 and the wear-resistant layer 3 are sequentially bonded to the other side of the base layer 1, and the thickness of the bonding layer between the fiber layer 4 and the wear-resistant layer 3 is 1mm.

[0044] Preferably, the fiber layer 4 includes a glass fiber layer 41 and a polyester fiber layer 42; the fiber filaments of the glass fiber layer 41 and the fiber filaments of the polyester fiber layer 42 are bonded to each other at an angle of 90°, Wherein, the thickness of the glass fiber layer 41 is 0.5 mm, and the thickness of the polyester fiber layer 42 is 0.5 mm.

[0045] Preferably, the wear-resistant layer 3 is a polyester layer with a thickness of 2.5mm.

[0046] Preferably, the antibacterial layer 2 is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses wear-resistant antibacterial microfiber synthetic leather which comprises a base layer, an antibacterial layer, a wear-resistant layer, a fiber layer and a hydrophilic layer, the antibacterial layer and the hydrophilic layer are sequentially adhered to one side of the base layer; the fiber layer and the wear-resistant layer are sequentially bonded to the other side of the base layer, and the thickness of a bonding layer between the fiber layer and the wear-resistant layer is 1 mm; the invention also discloses a preparation method of the wear-resistant antibacterial microfiber synthetic leather. The microfiber synthetic leather disclosed by the invention has the beneficial effects that the microfiber synthetic leather adopts the arrangement of the hydrophilic layer and the antibacterial layer, so that the whole microfiber synthetic leather is antibacterial, mildew-proof, moisture-absorbing, quick-drying and good in skin-friendly property, and meanwhile, the three external performance layers, namely the fiber layer, the tensile layer and the wear-resistant layer, improve the ductility, the tensile property and the wear resistance of the whole cloth, so that the service life of the cloth is prolonged, and the service life of the cloth is prolonged. And a good protection effect is achieved on the cloth.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a wear-resistant and antibacterial superfiber synthetic leather and a preparation method thereof. Background technique [0002] During the use of existing microfiber synthetic leather, especially during the rainy season, it is extremely vulnerable to pollution by the Israeli army. In addition to the high temperature environment in the rainy season, the surface attachments of the microfiber and the cloth itself are good environments for bacterial growth. Staphylococcus, Escherichia coli, and Candida albicans, which are common in nature, are even more pathogenic. In addition, the existing microfiber synthetic leather mainly uses non-woven fabric as the base layer and polyurethane as the surface layer. The polyurethane surface layer is painted on the non-woven fabric base layer to form a product, but the surface of such microfiber synthetic leather The polymerization degree of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/02B32B17/12B32B23/02B32B23/04B32B27/02B32B27/12B32B27/36B32B33/00