Memory rubber with high cohesiveness as well as preparation method and application thereof
A cohesive, rubber-based technology, applied in mechanical equipment, pipelines to prevent damage/abrasion, pipeline protection, etc., can solve problems such as poor viscosity of memory rubber, gas leakage, easy to break, etc., to achieve good wear resistance and elasticity , improve adhesion, improve the effect of wear resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0052] Example 1
[0053] Preparation method of memory rubber with high adhesion, comprising the following steps:
[0054] 20 parts of rubber, 10 parts of polycarbonate into the horizontal mixer, stirred at a speed of 40r / min for 1h to obtain the mixture; 1 part of the antioxidant 1010 and 5 parts of terpene resin into the horizontal mixer at a speed of 60r / min stirred for 1h, extruded by extruder to obtain extrusion; 1 part of sulfur and 1 part of stearic acid and extrusion into the rubber injection molding machine for vulcanization, cooling for 2h, to obtain memory rubber.
Example Embodiment
[0055] Example 2
[0056] Preparation method of memory rubber with high adhesion, comprising the following steps:
[0057] Put 20 parts of rubber, 10 parts of polycarbonate into the horizontal mixer, stir at a speed of 40r / min for 1h to obtain the mixture; put 1 part of antioxidant DLTP and 5 parts of rosin glyceride into the horizontal mixer at a speed of 60r / min and stir for 1h, extruded by extruder to obtain extrusion; 1 part of sulfur and 1 part stearic acid and extrudate into the rubber injection molding machine for vulcanization, cooling for 2h, to obtain memory rubber; wherein, rubber is modified natural rubber, Modified natural rubber is prepared by the following steps:
[0058] S1: 30 parts of natural rubber, 5 parts of EPDM rubber and 10 parts of butyl rubber are added to 50 parts of butyl acrylate, and heated and stirred for 2h under the condition of temperature of 50 °C and speed of 30r / min to obtain agitation;
[0059] S2: Mix 10 parts copper alloy with the agitator i...
Example Embodiment
[0061] Example 3
[0062] Preparation method of memory rubber with high adhesion, comprising the following steps:
[0063] Put 20 parts of rubber, 10 parts of polycarbonate into a horizontal mixer, stir at a speed of 40r / min for 1h to obtain a mixture; put 1 part of antioxidant 1010 and 5 parts of polyethylene into a horizontal mixer at a speed of 60r / min and stir for 1h, extruded by extruder to obtain extrusion; 1 part of sulfur and 1 part of stearic acid and extrusion are put into a rubber injection molding machine for vulcanization, cooling for 2h, to obtain memory rubber; among them, rubber is modified natural rubber, Modified natural rubber is prepared by the following steps:
[0064] S1: 30 parts of natural rubber, 5 parts of EPDM rubber and 10 parts of butyl rubber are added to 50 parts of butyl acrylate, and heated and stirred for 2h under the condition of temperature of 50 °C and speed of 30r / min to obtain agitation;
[0065] S2: Mix 10 parts copper alloy with the agitato...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap