Alit-leaf liter cement and preparation method thereof

A technology for cement and sandstone, which is applied in the field of Alite-Yelimite cement and its preparation, can solve the problems of complex preparation process of cement clinker cement and reduce the formation temperature of Alite, and achieves the advantages of reducing the formation temperature and simplifying the preparation process. Effect

Pending Publication Date: 2022-04-29
CHUZHOU UNIV
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Barium or strontium is incorporated into the rare earth solid solution in the following ways, and the temperature of yelimite is stabilized at 1380 degrees Celsius; (b) the formation temperature of yelimite is lowered by changing the properties of the liquid phase at high temperature by mineralizers, (c) by wave The secondary heat treatment method of Telan clinker changes the chemical process, although these methods have obtained satisfactory cement clinker in the laboratory, the preparation process of cement clinker is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alit-leaf liter cement and preparation method thereof
  • Alit-leaf liter cement and preparation method thereof
  • Alit-leaf liter cement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] In order to make the above objects, features and advantages of the present invention more comprehensible, specific implementations of the present invention will be described in detail below in conjunction with the accompanying drawings.

[0043] Secondly, the present invention is described in detail in conjunction with schematic diagrams. When describing the implementation of the present invention in detail, for the convenience of explanation, the cross-sectional view showing the device structure will not be partially enlarged according to the general scale, and the schematic diagram is only an example, and it should not be limited here. The protection scope of the present invention. In addition, the three-dimensional space dimensions of length, width and depth should be included in actual production.

[0044] In order to make the purpose, technical solution and advantages of the present invention clearer, the following will further describe the implementation of the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses alite-leaf liter cement and a preparation method thereof, and the alite-leaf liter cement comprises: limestone; according to the formula, the raw materials comprise, by weight, 70%-72% of the raw materials, 6.5%-7.5% of sandstone, 6.8%-7.0% of fly ash, 9.2%-9.4% of gypsum, 1.4%-1.6% of copper slag, 2.2%-2.4% of phosphorus slag, 0.7%-0.9% of aluminum oxide and 1.1%-1.3% of silicon oxide. The preparation method of the alite-leaf liter cement comprises the following steps: mixing the raw materials together for a certain time, pressing the homogenized mixture into a mixture in a parallel epitaxial wafer shape by using water, and sintering the mixture at different temperatures of 1200-1350 DEG C at different time intervals, the samples are taken out at different heat preservation time of 0 h, 0.5 h, 1 h, 1.5 h and 2 h respectively.

Description

technical field [0001] The invention relates to the technical field of cement, in particular to Alite-Yelimit cement and a preparation method thereof. Background technique [0002] Alite-Yelimit cement mainly contains alumina stone, calcium oxide alumina, and minerals, which have been synthesized in recent decades. This type of cement has the properties of Portland cement and CSA cement. In addition, Alite-Yelimit cement is expected to be a promising low-energy cement due to its lower synthesis temperature, easy grinding properties, and potential to recombine more solid waste. [0003] Variations in the formation of alite and yelit, which can coexist at high temperatures. However, the reaction kinetics during clinker firing do not match, as alite is mainly formed in Portland cement clinker at around 1450 °C, while the pure phase of yerlimite decomposes rapidly after 1350 °C , Therefore, in order to improve the quality of clinker, dozens of experimental works have been carr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/345C04B7/147C04B7/36
CPCC04B7/345C04B7/147C04B7/36Y02P40/10
Inventor 郑娇玲
Owner CHUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products