Environment-friendly elastic putty and preparation method thereof

An elastic putty, environmentally friendly technology, used in climate sustainability, final product manufacturing, sustainable manufacturing/processing, etc., can solve problems such as inconvenience in construction, and achieve the effect of high construction efficiency, fast grinding, and convenient grinding

Pending Publication Date: 2022-05-27
XIAMEN SUNRUI SHIP COATING
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the pot life is only 15-20 minutes, which means that when using it, only a small amount can be prepared at a time, and it must be used immediately after preparation, which will cause a certain degree of inconvenience to the construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly elastic putty and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042]In order to make the purposes, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention. Obviously, the described embodiments are the present invention. Some examples, but not all examples. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative efforts shall fall within the protection scope of the present invention.

[0043] The present invention provides the group allocation ratio of embodiment and comparative example shown in the following table:

[0044] Table 1 (unit: parts by weight)

[0045]

[0046] Wherein, in the above-mentioned embodiment:

[0047] In component A, the compound resin used is Dekun PU2510 polyol resin and F426 aspartate; the nano-enhancer used is HB-612 hydrop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of chemical materials, in particular to environment-friendly elastic putty and a preparation method thereof.According to the environment-friendly elastic putty, polyether polyol resin and asparaginic acid resin are synergistically compounded, system crosslinking is increased by adding a nanometer reinforcing material, an MDI curing agent and an HDI polyisocyanate curing agent are compounded, and the environment-friendly elastic putty is prepared. The environment-friendly elastic putty is obtained by using an environment-friendly and safe organic bismuth catalyst and adding appropriate pigments and fillers, the putty does not contain toxic organic tin components, the adhesive force of the putty on a blade base material can reach 10 MPa or above, and the impact resistance is gt; the thickness is 100 cm, and the bending resistance is 1t; the putty has the advantages that the thickness is 1 mm, the solid content is 99% or above, the construction time is as long as 8 hours or above, the curing time can be flexibly adjusted by utilizing the catalyst, the polishing is convenient and quick, the construction efficiency is high, and the use requirement of the fan blade putty is met.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to an environment-friendly elastic putty and a preparation method thereof. Background technique [0002] After the fan blade is taken out from the forming mold, there will be defects in the local area of ​​the surface. In addition, there are also gaps in the joint after the two blades are bonded. Therefore, it is usually necessary to use putty to repair the uneven surface of the blade, small holes and large seams. , after grinding, the next coating process can be carried out. Fan blades will not only be impacted by wind, sand, rain and other impacts during operation, but also undergo certain deformation. Therefore, the coating system including putty is required not only to have excellent adhesion, but also to have high flexibility and mechanical strength. Ordinary epoxy putty, unsaturated polyester putty, and solvent-based polyurethane putty are difficult to take into ac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34Y02P70/50
Inventor 李陈郭叶维维康瑞瑞李至秦
Owner XIAMEN SUNRUI SHIP COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap